• Transactions of Materials Processing
• /
• v.8 no.5
• /
• pp.482-490
• /
• 1999

7000 series Al alloy with good mechanical properties has been focused with tendency to reduce the components weight of aircraft and automobile. However, it is difficult to manufacture a sound extruded product because of segregation, grain growth, casting defect, surface defect, decreasing extrudability and so on. The objective of this study is to manufacture a new 7000 al alloy more than the extrudability of A7N01 and A7003 through controlling the weight (%) Mg, Zn, Si. Hot extrusion experiments on the axisymmetric rod are performed in 500℃ and also performed analysis of the same process using unmerical analysis method, a coupled rigid-thermoviscoplastic finite element method. Extrusion limit diagram was obtained for the developed alloy by FE-simulation in order to define the relationship of extrusion speed and initial billet temperature.

• Journal of Korea Foundry Society
• /
• v.32 no.4
• /
• pp.181-189
• /
• 2012

The microstructures of self-designed 7000 series Aluminium alloys added with Sc are observed. Moreover, the mechanical properties of the Sc-added Aluminium alloys are evaluated as a function of tensile temperature to establish the conditions of a following extrusion process. New casting conditions in the aluminium alloys added with Sc could be established by changing the casting speed and stirring time in the existing casting conditions of Aluminium alloys. The Sc addition results in $Al_3(Sc,Zr)$ precipitates in the cast alloys, and leads to the formation of equal-axed grains and fine grains. After homogenization heat treatment at $450^{\circ}C$, the Sc-added Aluminium alloys showed the highest elongation values in the temperature ranging from $300{\sim}400^{\circ}C$.

• Journal of Korea Foundry Society
• /
• v.41 no.3
• /
• pp.241-251
• /
• 2021

7000-series aluminum alloys are noted for their superior strength compared with other Al alloys, and their billets are generally fabricated by direct-chill (DC) casting. Surface defects in a DC-cast aluminum billet are mainly related to exudation and the meniscus freezing phenomenon, which are influenced by alloy compositions, casting speed, and casting temperature. 7000-series aluminum alloys have a wide freezing range during solidification, which makes it easy for casting defects to occur. In this study, we investigated surface defect evolution in casting billets of Al-8Zn-2Mg-2Cu alloy fabricated by a DC casting process. The billets showed "wavy" or "dotted" surfaces. The wavy surface was formed by meniscus freezing at a lower casting speed (200 mm/min) and temperature (655 ℃). In the wavy surface, refined dendritic cells were observed in a concave region due to the constitutional supercooling caused by meniscus freezing. Meanwhile, at a higher casting temperature (675 ℃), the dotted surface was formed by pore formation. In the dotted surfaces in the billet formed at a high casting speed (230 mm/min), an exudation layer was formed by the high metallostatic head pressure. The dotted region and the smooth region had a refined dendritic morphology and a columnar morphology at the exudation layer, respectively. This is attributed to the formation of gas pores in the dotted region.

• Proceedings of the Korean Institute of Industrial Safety Conference
• /
• 1998.11a
• /
• pp.9-14
• /
• 1998

고강도 알루미늄 합금은 기술의 진보에 따라서 이용도가 높은 매우 중요한 재료로서, 잘 알려진 적용분야로서는 항공우주산업, 고속회전체, 항공기용재 등으로 많이 사용되고 있다. 고강도 알루미늄 합금은 Al-Cu-Mg(2000 series)를 기초로 둔것과 Al-Zn-Mg-Cu(7000 series)를 기초로 둔 것등이 있다. (중략)

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2003.10a
• /
• pp.130-131
• /
• 2003

• Journal of Korea Foundry Society
• /
• v.19 no.1
• /
• pp.47-53
• /
• 1999

Squeeze casting process has been used in the field of a commercial manufacturing method, in which metal is enforcedly solidified under pressure enough to prevent the cast defects such as either gas porosity or shrinkage defect. In this paper, to clarify the relationship between applied pressures and macro ${\cdot}$ microstructural behaviors in gravity and direct squeeze casts, specimens were cast by various squeezing pressures during solidification of 7000 series Al wrought alloy in the metal die designed specially. The applied pressures used in this study were 0, 25, 50, and 75 MPa. The microstructural morphologies of squeeze cast were more fine and dense with increasing the applied pressures, because of the greater solidification rate of billet resulting from the applied pressure. A normal segregation phenomenon of an increasing in amount of eutectics towards the center of the billet was observed for squeeze casts, whereas gravity cast showed an inverse segregation phenomenon of an increasing in amount of eutectics towards the edge in the billet. This change in segregation pattern which is normal or inverse is due to a higher radial temperature gradient and reduced time in the semi solid state for squeeze casting.

• Journal of Korea Foundry Society
• /
• v.34 no.2
• /
• pp.54-59
• /
• 2014

In this study, the extruded Al-6.3Zn-2.4Mg alloys were selected among the 7000 series aluminum alloys sensitive to hydrogen environment in order to examine the effects of both the aging conditions and the length of hydrogen charging period on the mechanical properties of the alloy. The specimens were aged for 24hours at $100^{\circ}C$ (under aging (UA)), $120^{\circ}C$ (peak aging (PA)), and $160^{\circ}C$ (over aging (OA)), respectively. Charging tests were performed at RT for 12, 24, 36 hours under potentiostatic conditions (-2000 mV vs (Ag/AgCl)) for 12, 24 and 36 hours in 1M $H_2SO_4$ and 0.1%$NH_4SCN$ solution. The fracture surface was examined by scanning electron microscopy (SEM). X-ray diffraction (XRD) pattern in peak aged sample was obtained before and after hydrogen charging from extruded Al-6.3Zn-2.4Mg alloys. The decreasing rate of tensile strength and elongation is represented in order of over aging < under aging < peak aging, and it is believed that the hydrogen recharge is more sensitive to elongation than tensile strength. The formation of $AlH_3$ in hydrogen charged Al-6.3Zn-2.4Mg alloys has been confirmed by X-ray diffraction studies.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1992.05a
• /
• pp.14-14
• /
• 1992

During the past five years a very successful effort has been made to improve existing and develop new aluminium alloys. The progress achieved has been possible because of the development of new production methods, such as powder metallurgy and spray/deposition. These methods make use of rapid solidification process which alloys compositions other than those achieved by conventional ingot metallurgy. The ingot metallurgy of the 2000 and 7000 series used thus far, as well as the age hardening Al-Li alloys, show several disadvantages caused by the production process. Such problems are primarily coarse intermetallic constituent phases, coarse grains and macrosegregation, resulting in low fracture toughness. The present contribution reports results of an experimental investigation performed on a modern high strength spay deposited aluminium alloy of the Al-Zn-Mg-Cu (7075 and the modified 7150X) type. Results are given in terms of its microstructural characterization by using X-ray diffractomertry and transmission electron microscopic. The mechanical propierties of those alloys in the as-extruded and extruded+aged condition were evaluated by using microhardness Vickers, tensile test and fracture toughness measurements.

• Journal of Korea Foundry Society
• /
• v.19 no.6
• /
• pp.456-465
• /
• 1999

The overall objective of this study is to investigate the effect of Ag addition on the mechanical properties and microstructure of rapid solidified 7000 Al series alloys. Al-Zn-Mg-Cu alloys with small amounts of Ag was fabricated into the powder by gas atomization. The powder was extruded after the cold compaction and degassing and then followed by T6 heat treatment. Microstructure observation, phase analysis, room and high temperature tensile test and hardness test were pursued. The tensile strength and hardness of Ag-added alloy after heat treatment was increased with increasing Ag contents. However, the elongation of extruded alloys was not increased as much as to be expected. The reason of this result seems to be related to $the{\Omega}$ phase, which contribute to the high temperature strength stability of Al-Cu-Zn alloys through the formation of eutectoid with Ag addition.