• Transactions of Materials Processing
• /
• v.17 no.2
• /
• pp.102-106
• /
• 2008

Cryogenic rolling combined with warm rolling has been found more effective than a single cryogenic rolling process in improving the strength of a 5052 Al alloy. In this study, cryo-rolled 5052 Al alloys were warm-rolled at $175^{\circ}C$. A notable increase of tensile strength was achieved by the precipitation during warm rolling process. Mechanical behavior of this alloy was investigated using hardness and tensile tests. It was found that the cryogenic rolling process combined with warm rolling process was very effective in improving tensile strength.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2003.10a
• /
• pp.152-155
• /
• 2003

In order to examine the springback of aluminum alloy sheets, AL1050 and AL5052, in the warm forming which forms the sheet above room temperature, the stretch bending and draw bending tests in various working temperatures were carried out. While the springbacks of AL5052 and AL1050 are tremendously reduced over 150$^{\circ}C$ in the stretch bending test, the springbacks in the draw bending test are rapidly reduced in 150$^{\circ}C$-200$^{\circ}C$ for AL5052 and 200$^{\circ}C$-250$^{\circ}C$ for AL1050. Using the FEM program, the forming and springback processes are analyzed. Though springback amounts of analysis result are slightly bigger than those of experiment, they showed the same trend in the decreasing springback as the forming temperature increases.

• Transactions of Materials Processing
• /
• v.12 no.3
• /
• pp.202-207
• /
• 2003

In order to examine the springback amount and material properties of aluminum alloy sheets (AL1050 and AL5052) in the warm forming which forms the sheet above the room temperature, the stretch bending and draw bending tests and tensile test in various high temperatures are carried out. The warm forming temperature 15$0^{\circ}C$ is a transition in terms of the material properties: over the forming temperature 15$0^{\circ}C$, them $\sigma$$_{YS}$ , $\sigma$$_{TS}$ , E, K, n, etc. are bigger but $\varepsilon$ and plastic strain ratio are smaller. Below the forming temperature 15$0^{\circ}C$, there are no big differences in material properties as the forming temperature changes. AL5052 sheet has more springback effect than AL1050 sheet. While the springbacks of AL5052 and AL1050 sheets show a big reduction over the warm forming temperature 15$0^{\circ}C$ in the stretch bending test, the springback rapidly reduces in the warm forming temperature 15$0^{\circ}C$-20$0^{\circ}C$ for AL5052 sheet and 20$0^{\circ}C$-25$0^{\circ}C$ for AL1050 sheet in the draw bending test.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2009.05a
• /
• pp.401-404
• /
• 2009

The purpose of this study is investigating the joint characteristics of advanced high strength steel DP780 and Al5052 alloy sheet in the clinching process. It is difficult to join the advanced high strength steel with light-weight materials like aluminum alloy, because of low formability of DP780. The defects of clinching joint such as necking of the upper sheet, cracks of the lower sheet and no interlocking were occurred by different ductility between advanced high strength steel and aluminum alloy. The clinching conditions should be optimized to interlock without any defects. In this study, the effect of process parameters of clinching process on joinability of advanced high strength steel with Al5052 alloy was investigated by using FE-analysis. From the result of FE-analysis, the clearance between clinching punch and die, die depth and the shape of die cavity mainly affected the joinability of advanced high strength steel with Al5052 alloy.

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.528-533
• /
• 2002

The mechanical and metallurgical properties of friction welded joints type 5052 Al alloy/A36 steel have been studied in this paper. The joint strength increased with increasing upset pressure and friction time till it reached the critical value. The joint strength was fixed at low strength compare to that of base metal in the case of increasing friction time. Microstructure of 5052 Al alloy was greatly deformed near the weld interface. The very fine and equaxied grain structure was observed at the near interface. The elongated grain was formed outside dynamic recrystallizatoin region at the peripheral part, while the A36 steel' side was not deformed. The hardness of the near interface was slightly softer than that of 5052 Al alloy base metal. The maximum softening width was about 8mm from the interface. In the present work, the friction welding condition, t$_1$=0.5sec, P$_2$=137.5MPa, showed a maximum joint strength (202MPa) when friction pressure, upset time and rotation speed were fixed at 75MPa, 5sec, 2000rev/min and these were the optimum friction welding condition of 5052Al/A36 steel joints.

• Journal of Welding and Joining
• /
• v.22 no.3
• /
• pp.69-76
• /
• 2004

Effects of friction stir welding parameters such as tool rotation speed and welding speed on the joints properties of 5052 Al alloys were studied in this study. A wide range of friction stir welding conditions could be applied to join 5052 AA alloy without defects in the weld zone except for certain welding conditions with a lower heat input. Microstructures near the weld zone showed general weld structures such as stir zone (SZ), thermo-mechanically affected zone (TMAZ) and heat affected zone (HAZ). Each zone showed the dynamically recrystallized grain, transient grain and structure similar to base metal's, respectively. Hardness distribution near the weld zone represented a similar value of the base metal under wide welding conditions. However, in case of 800 rpm of tool rotation speed, hardness of the stir zone had a higher value due to the fine grain with lots of dislocation tangle, a higher angle grain boundary and some of Al3Fe particles. Except joints with weld defects, tensile strength and elongation of the joints had values similar to the base metal values and fracture always occurred in the regions approximately 5mm away from the weld center.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.30 no.2
• /
• pp.146-154
• /
• 2010

The effects of severe plastic deformation, equal channel angular pressing, and annealing of Al 5052 alloy on elastic modulus have been studied. The AI 5052 alloy was plastically deformed by ECAP method after solution treatment, and then finally annealing heat treated. Elastic modulus was measured by conventional tensile and nano-indentation test, and also measured on the surface of the specimen using acoustic material signature of the acoustic microscope. The variation in the elastic modulus influenced by plastic deformation and heat treatment, inaccessible by the conventional techniques, was successfully measured by acoustic material signature and obtained the elastic modulus depending on crystal orientation at each grain.

• Proceedings of the KWS Conference
• /
• 2003.05a
• /
• pp.69-71
• /
• 2003

• Proceedings of the KWS Conference
• /
• 2005.06a
• /
• pp.235-237
• /
• 2005

• Corrosion Science and Technology
• /
• v.19 no.5
• /
• pp.250-258
• /
• 2020

Recently, 5000 series and 6000 series Al alloys have been used as hull materials for small and medium-sized ships because of their excellent weldability, corrosion resistance, and durability in marine environments. Al ships can navigate at high speed due to their light weight. However, cavitation-erosion problems cause reducing durability of Al ship at high speed. In this investigation, 5052-O, 5083-H321, and 6061-T6 Al alloy materials were used to evaluate the damage characteristics with amplitude (cavitation strength). As a result of the electrochemical experiments, the corrosion current density and corrosion potential of 6061-T6 in seawater were 8.52 × 10-7 A/㎠ and -0.771 V, respectively, presenting the best corrosion resistance. The cavitation-erosion experiment showed that 5052-O had the lowest hardness value and cavitation-erosion resistance. 5052-O also had a very short incubation period. As the experiment progressed for 5052-O, pitting formed and grew in a short time, and was observed as severe cavitation-erosion damage that eliminated in large quantities. Among the three specimens, 5083-H321 presented the highest hardness value and the damage rate was the smallest after the initiation of pitting.