• Journal of the Korean Magnetics Society
• /
• v.9 no.3
• /
• pp.154-158
• /
• 1999

Magnetic properties and microstructure of nanocrystalline $\alpha$-(Fe, Co)-based Nd-(Fe, Co)-B-Nb-Cu alloys have been investigated. $Nd_x(Fe_{0.9}Co_{0.1})_{90-x}B_6Nb_3Cu_1$(x=2, 3, 4, 5, 6) alloys prepared by rapid solidification process show amorphous phase except the one with x=2. By a proper annealing, the amorphous in the alloy is changed to a nanocrystalline phase. It is confirmed that the nanocrystalline alloys are composed of $\alpha$-(Fe, Co) and $Nd_2(Fe, Co)_{14}B_1$ phase. The optimally annealed $Nd_3(Fe_{0.9}Co_{0.1})_87B_6Nb_3Cu_1$ alloy shows the highest remanence of 1.55 T. The coercivity increases with the increase of Nd content The maximum coercivity of 4.6 kOe is obtained from an optimally annealed $Nd_6(Fe_{0.9}Co_{0.1})_84B_6Nb_3Cu_1$ alloy, resulting in the maximum energy product of 10.6 MGOe.

• Journal of the Korean Magnetics Society
• /
• v.3 no.4
• /
• pp.284-288
• /
• 1993

Low temperature magnetic properties and crystal structures of melt-spun $Sm_{2}Co_{7}B_{3}$ compound were characterized. The magnetic measurements in the temperature range 77 K~450 K indicated that a spin-reorientation took place at about 150~160 K. A large anisotropy was observed(Ha=135 kOe at 300 K, 725 kOe at 77 K) for $Sm_{2}Co_{7}B_{3}$ although the magnetic moment is rather low. The crystal structure of the $Sm_{2}Co_{7}B_{3}$ compound was analyzed in detail by Rietveld analysis of powder diffraction pattern, and it was revealed that B(4h) atoms are not placed in the Sm(2e) layer but in between the Sm(2e) and Co($6i_{1}$) layers.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.611-614
• /
• 2004

[ $Ba(Zn_{1/3}Nb_{2/3})O_3$ ] (BZN) 세라믹스의 소결 온도는 약 $1350^{\circ}C$ 이다. 그러나 $B_2O_3$가 첨가된 경우, BZN 세라믹스는 $900^{\circ}C$에서 소결되었다. $BaB_4O_7$, $BaB_2O_4$ 그리고 $BaNb_2O_6$ 이차상이 $B_2O_3$가 첨가된 BZN 세라믹스에서 관찰되었다. $BaB_4O_7$과 $BaB_2O_4$ 이차상은 약 $900^{\circ}C$에서 공정 온도를 가지기 때문에 $B_2O_3$를 첨가한 BZN 세라믹스론 $900^{\circ}C$에서 소결하는 동안 액상으로 존재할 것으로 여겨지며, 그것이 BZN 세라믹스의 소결온도를 낮출 것으로 생각된다. 소결 온도의 증가에 따라 유전 상수 ($\varepsilon_r$)와 품질 계수 ($Q{\times}f$)의 값은 증가하였는데, 이는 밀도의 증가에 기인한다. 그러나 $B_2O_3$의 첨가량이 많은 경우 Q 값은 감소하는데, 이는 이차상의 존재가 품질계수의 저하를 초래한다고 생각된다. 2.0 mol% $B_2O_3$가 첨가된 BZN 세라믹스를 $950^{\circ}C$에서 2시간 동안 소결하는 경우, $Q{\times}f$=13.600 GHz, $\varepsilon_r$=37.6 그리고 공진 주파수 온도계수 ($\tau_f$) = 19 ppm/$^{\circ}C$의 유전특성을 얻을 수 있었다.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.57 no.5
• /
• pp.808-815
• /
• 2008

The composites were fabricated 61[vol.%] ${\beta}$-SiC and 39[vol.%] $TiB_2$ powders with the liquid forming additives of 8, 12, 16[wt%] $Al_2O_3+Y_2O_3$ as a sintering aid by pressureless annealing at 1650[$^{\circ}C$] for 4 hours. The present study investigated the influence of the content of $Al_2O_3+Y_2O_3$ sintering additives on the microstructure, mechanical and electrical properties of the pressureless annealed SiC-$TiB_2$ electroconductive ceramic composites. Reactions between SiC and transition metal $TiB_2$ were not observed in the microstructure and the phase analysis of the pressureless annealed SiC-$TiB_2$ electroconductive ceramic composites. Phase analysis of SiC-$TiB_2$ composites by XRD revealed mostly of ${\alpha}$-SiC(6H), ${\beta}$-SiC(3C), $TiB_2$, and In Situ YAG($Al_2Y_3O_{12}$). The relative density of SiC-$TiB_2$ composites was lowered due to gaseous products of the result of reaction between SiC and $Al_2O_3+Y_2O_3$. There is another reason which pressureless annealed temperature 1650[$^{\circ}C$] is lower $300{\sim}450[^{\circ}C]$ than applied pressure sintering temperature $1950{\sim}2100[^{\circ}C]$. The relative density, the flexural strength, the Young's modulus and the Vicker's hardness showed the highest value of 82.29[%], 189.5[Mpa], 54.60[Gpa] and 2.84[Gpa] for SiC-$TiB_2$ composites added with 16[wt%] $Al_2O_3+Y_2O_3$ additives at room temperature. Abnormal grain growth takes place during phase transformation from ${\beta}$-SiC into ${\alpha}$-SiC was correlated with In Situ YAG phase by reaction between $Al_2O_3$ and $Y_2O_3$ additive during sintering. The electrical resistivity showed the lowest value of 0.0117[${\Omega}{\cdot}cm$] for 16[wt%] $Al_2O_3+Y_2O_3$ additives at 25[$^{\circ}C$]. The electrical resistivity was all negative temperature coefficient resistance (NTCR) in the temperature ranges from $25^{\circ}C$ to 700[$^{\circ}C$]. The resistance temperature coefficient of composite showed the lowest value of $-2.3{\times}10^{-3}[^{\circ}C]^{-1}$ for 16[wt%] additives in the temperature ranges from 25[$^{\circ}C$] to 100[$^{\circ}C$].

• Proceedings of the Korean Magnestics Society Conference
• /
• 1997.05a
• /
• pp.72-73
• /
• 1997

• Proceedings of the Korean Magnestics Society Conference
• /
• 2000.05a
• /
• pp.62-63
• /
• 2000

• The Journal of Korean Institute of Communications and Information Sciences
• /
• v.22 no.11
• /
• pp.2573-2584
• /
• 1997

In this paper, Ca, Sn substitute YIC(Yttrium Iron Garnet) ceramics were fabricated with Al substitutions in Fe sites. The strip-line circulator was designed and the properties of fabricated ciculator were measured. When the electric, magnetic and microwave properties were measured in Ca, Sn substituted YIG with Al subsititions, the relative permittivity and perfmeability in microwave frequencies were 15.623 and 0.972, repectively. For $Y_{2.4}Ca_{0.3}Sn_{0.3}Fe_{5-x}Al_xO_{12}$ garnet ceramics sintered at $1450^{\circ}C$, the ferrimagnetic resonance line width $\Delta{H}$) of 42 Oe and the saturation magnetization of 487 G were measured at 10 GHz. The strip-line circulator was simulated with 3-D FEM(Finite Element Method) software and designed to have insertion loss of 0.8dB, return loss of 25dB, isolation of 35dB at the center frequency of 1.9GHz. The fabricated strition loss of 0.8B, reture loss of 25dB, isolation of 35dB at the center frequency of 1.9GHz. The fabricated strip-line junction circulator using above YIG ceramics had insertion loss of 0.869dB, return loss of 26.955dB, isolation of 44.409dB at the center frequency of 1.9GHz.

• Korean Journal of Soil Science and Fertilizer
• /
• v.45 no.4
• /
• pp.532-539
• /
• 2012

This study was carried out to investigate the effect of substrate to inoculum ratio on ultimate methane potential ($B_u$) from piggery wastes. BMP(Biochemical methane potential) assays were executed for the three samples that have different organic characteristics (Filtrate of pig slurry, LF; Thermal hydrolysate of piggery sludge cake, TH; Mixture of LF and TH at the ratio of 4 to 1, Mix), and $B_u$ values obtained from BMP assays were compared with the theoretical methane potential ($B_{th}$) of each samples. While $B_u$ values (0.27, 0.44, and $0.46Nm^3\;Kg^{-1}-VS_{added}$) of TH sample that was pretreated with thermal hydrolysis were below the $B_{th}$ at all S/I ratios (0.1, 0.3, and 0.5), and $B_u$ values of LF (0.64 and $0.53Nm^3\;Kg^{-1}-VS_{added}$ for the S/I ratios of 0.1 and 0.3, respectively) at the lower S/I ratios of 0.1 and 0.3 exceeded the $B_{th}$ values ($0.418Nm^3\;Kg^{-1}-VS_{added}$). And also biodegradability ($B_u/B_{th}$) of LF sample were obtained as 152.07%, 122.67%, and 95.71% at the S/I ratios of 0.1, 0.3, and 0.5, respectively, and unreasonable $B_u/B_{th}$ values were presented at lower S/I ratios of 0.1 and 0.3. $B_u$ and $B_u/B_{th}$ of Mix sample showed a similar tendency with those of LF sample. Therefore, TH sample by thermal hydrolysis pretreatment showed lower anaerobic biodegradability than those of other samples (LF and Mix) and ultimate methane potentials of LF and Mix samples were overestimated in the lower S/I ratio of 0.1 and 0.3.

• 전기의세계
• /
• v.21 no.6
• /
• pp.17-20
• /
• 1972

The magnetic properties of Ba-Ferrite ( $M^{+2}$O.nF $e_{2}$ $O_{3}$ is highly improved under the condition of composition ratio n=4.4 when B $i_{2}$ $O_{3}$ is added to Ferrite, the adding amount and sintering temperature which affect the magnetic properties were investigated and the following results; were obtained; 1. Magnetic properties are varied with B $i_{2}$ $O_{3}$ content and singering temperature, and coercive force and residual induction can be improved with B $i_{2}$ $O_{3}$. 2. The optimal content of B $i_{2}$ $O_{3}$ amount is about 4 mol %, 3. Without the addition of B $i_{2}$ $O_{3}$, the optimal sintering temperature is about 1300.deg. C, but when 4 mol % of B $i_{2}$ $O_{3}$ is added, the optimal sintering temperature falls to the range of 900.deg. C to 1100.deg. C and it also improves magnetic properties. 4. Residual induction increases as the singering temperature is raised to 1100.deg. C. Coercive force also increased as the sintering temperature is raised to 1000.deg. C, but it rapidly decreases when sintering temperature goes beyond 1000.deg. C. 5. Only a negligible change may be noticed in the decrease of Curie temperature by the addition of about 4 mol % of B $i_{2}$ $O_{3}$.

• Journal of the Korean Ceramic Society
• /
• v.20 no.3
• /
• pp.236-242
• /
• 1983

The purpose of present study is to find the structures physical properties and their inter-relations in the system of (60-x) PbO.xMO.$40B_2O_3$ glasses where MO represents for ZnO and CdO. The experiments such as differential thermal analysis infrared spectral analysis X-ray diffraction analysis density and thermal expansion measurements have been done. From infrared spectral analysis the structural units of glasses and the corresponding crystallized glasses were com-posed of $BO_3$ triangles and $BO_4$ tetrahedra. These basic units found in $PbO-B_2O_3$ binary glass system did not charge even though the divalent metallic oxides were substituted for PbO. The structures of these ternary glasses were more coalescenced than $PbO-B_2O_3$ binary glass system. This fact was supported bydecrease in thermal expansion coeffici-ent and molar volume with substitution of divalent metallic oxide for PbO. Crystalline phases obtained from the heat treatment of the $PbO-ZnO-B_2O_3$ glasses were 4PbO.2ZnO.$5B_2O_3$ PbO.2ZnO.$B_2O_3$ and unknown phases.