• Journal of the Korean Ceramic Society
• /
• v.43 no.10 s.293
• /
• pp.640-645
• /
• 2006

Monoclinic zirconia and yttria were mixed with a stoichiometric composition of 3Y-TZP (3 mol% Yttria-stabilized Tetragonal Zirconia Polycrystal). The specimen was sintered at 1350$\sim$1450$^{\circ}C$ and mechanical characterization and microstructure analysis were conducted. Microhardness and fracture toughness were shown as 1357.4 Hv and 8.56 MPa $m^{1/2}$. respectively. Without alumina, they were 1311 Hv and 10.02 MPa $m^{1/2}$ respectively. By mixing two different oxides, it was possible to obtain high values of microhardness and fracture toughness. It was possible that was turned out nano-scale particle using the co-milling of high mechanical energy.

• Korean Journal of Materials Research
• /
• v.10 no.10
• /
• pp.677-683
• /
• 2000

Three- and five-layer 3Y-YZP/12Ce- TZP composites prepared by a slip casting method have been char­acterized in terms of mechanical properties. The fracture strength of mutilayer c$\alpha$nposites determined in a diametral compression test was 327~534 MPa. Although the indentation strength of the materials was generally reduced with i increasing Vickers indentation load up to 300 N, the damage resistance of multilayer composites was superior com­pared to monolithic layer TZP material. The four-point bend strength of the layered material remained at the values of 620~674 MPa after indentation with a load of 49 N, while that of the monolithic TZP material was 129~339 MPa. The microindentation toughness of the multilayer material was $7.7~13.1\;MPa{\cdot}m^{1/2}$.