• Journal of Powder Materials
• /
• v.30 no.3
• /
• pp.249-254
• /
• 2023

The influence of MgO addition on the densification and microstructure of alumina (Al₂O₃) was studied. Compacted alumina specimens were manufactured using ball-milling and one-directional pressing followed by sintering at temperatures below 1700℃. Relative density, shrinkage, hardness, and microstructure were investigated using analytical tools such as FE-SEM, EDS, and XRD. When the MgO was added up to 5.0 wt% and sintered at 1500℃ and 1600℃, the relative density exhibited an average value of 97% or more at both temperatures. The maximum density of 99.2% was with the addition of 0.5 wt% MgO at 1500℃. Meanwhile, the specimens showed significantly lower density values when sintered at 1400℃ than at 1500℃ and 1600℃ owing to the relatively low sintering temperature. The hardness and shrinkage data also showed a similar trend in the change in density, implying that the addition of approximately 0.5 wt% MgO can promote the densification of Al₂O₃. Studying the microstructure confirmed the uniformity of the sintered alumina. These results can be used as basic compositional data for the development of MgO-containing alumina as high-dielectric insulators.

• Journal of the Microelectronics and Packaging Society
• /
• v.24 no.1
• /
• pp.1-8
• /
• 2017

Fe-9.8Si-6.0Al mother alloy was manufactured using by Fe-3.5Si recycled scrap and Si powder. And then, soft magnetic alloy powder of $D_{50}$ size and sphere type were prepared by gas atomization process. To obtain the soft magnetic powder of a high aspect ratio, in the first, we conducted the ball milling process for 8 hours. And heat treatment was performed under $650^{\circ}C$, 2 hours and $N_2$ atmosphere condition for reducing the residual stress of the powder. Based on these process, we made around $50{\mu}m$ diameter Fe-9.8Si-6.0Al powder, which morphology and shape was a similar to the commercial Fe-Si-Al powder. Finally, the soft magnetic sheets were prepared by tape casting process using by those powders. The permeability of the tape casting sheet was measured, and we confirmed the possibility of reusing to the soft magnetic materials of Fe-Si electric sheet scrap.

• Journal of Biosystems Engineering
• /
• v.25 no.1
• /
• pp.39-46
• /
• 2000

This work was conducted to study the operating characteristics of a grinding system designed to obtain fine rice husk ash powder. To find better utilizing of rice husk, a valuable by-product from rice production, once the rice husk was incinerated and the thermal energy was recovered from the furnace, the ash was fed and pulverized in the grinding system resulting a fine powder to be used as a supplementary adding material to the portland cement manufacturing . The rice husk ash grinding system consisted of a high speed centrifugal fan for the preliminary coarse milling and a dry-type stirred ball mill for the subsequent fine grinding . Total grinding time 9 5, 15, 30, 45 min), impeller speed (250, 500, 750 rpm) , and mixed ratio (4.8, 7.9, 14.9) were three operating factors examined for the performance of a stirred ball mill used for the fine grinding of ash. With the stirred ball mill used in this study, the minimum attianable mean diameter of rice husk ash powder appeared to be 2 ${\mu}{\textrm}{m}$. During the find grinding, the difference in specific surface area of powder showed an increase and the grinding energy efficiency decreased with the increase in total grinding time, impeller speed ,and mixed ratio. For the operating conditions employed , the resulting mean diameter of fine ash powder, specific energy input, and grinding energy efficiency were in the range of 1.79 --16.04${\mu}{\textrm}{m}$, 0.072-5.226kWh/kg, an d1.11-12.15$m^2$/Wh, respectively. Grinding time of 30 min , impeller speed of 750 rpm, and mixed ratio of 4.8 were chosen as the best operating conditions of the stirred ball mill for fine grinding . At these conditions, mean particle diameter of the fine ash, grinding energy efficiency, grinding throughtput, and specific energy input were 2.73${\mu}{\textrm}{m}$, 3.95$m^2$/Wh, 0.25kg/h, and 1.22kWh/kg, respectively.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.40 no.3
• /
• pp.149-158
• /
• 2024

Purpose: This study aims to investigate the effects of provisional restoration fabrication methods and surface polishing on surface roughness and microbial adhesion through in vitro experiments. Materials and Methods: 120 cylindrical provisional restoration resin blocks (10 × 10 × 2.5 mm) were manufactured according to four fabrication methods, and 30 specimens were assigned to each group. Afterwards, they were divided into non-polishing group, #400 grit SiC polishing group, and #800 grit SiC polishing group and polished to a 10 × 10 × 2 mm specimen size (n = 10). The surface roughness Ra and Ry of the specimen was measured using a Surface Roughness Tester. Three specimens were extracted from each group and were coated with artificial saliva, and then Streptococcus mutans were cultured on the specimens at 37℃ for 4 hours. The cultured specimens were fixed to fixatives and photographed using a scanning electron microscope. For statistical analysis, the two way of ANOVA was performed for surface roughness Ra and Ry, respectively, and the surface roughness was tested post-mortem with a Scheffe test. Results: The fabrication method and the degree of surface polishing of the provisional restorations had a significant effect on both surface roughness Ra and Ry, and had an interaction effect. There was no significant difference in Ra and Ry values in all polishing groups in DLP and LCD groups. Conclusion: The fabrication method and surface polishing of the provisional restoration had a significant effect on surface roughness and showed different adhesion patterns for S. mutans adhesion.

• The Journal of Korean Academy of Prosthodontics
• /
• v.55 no.4
• /
• pp.381-388
• /
• 2017

Purpose: Unpredictable shrinkage of zirconia during sintering process causes discrepancy. Therefore, there have been attempts to reduce discrepancy by milling zirconia after sintering. However, due to the hardness of sintered zirconia, milling takes longer time, causes damage to the machine and causes chip formation. With customized zirconia block using the mean dimension of prepared natural dentition, it is expected to overcome these shortcomings. Materials and methods: The mean dimension of prepared natural dentition was analyzed as STL file after scanning of prepared teeth treated at SNUDH. The transverse, frontal and sagittal planes were set using Mimics and Photoshop. 3D volume was projected on each plane, and the outer line was measured through external tangent line, and the inner line was measured through inflection point of tangent line. Results: The mean height of prepared incisal (N = 57) is $6.60{\pm}1.05mm$, mesiodistal length is $2.98{\pm}0.73mm$, buccolingual length is $2.04{\pm}0.73mm$. The mean height of prepared premolar (N = 15) is $5.37{\pm}1.49mm$, mesiodistal length is $4.10{\pm}1.78mm$, buccolingual length is $5.86{\pm}1.55mm$. And the mean height of prepared molar (N = 13) is $5.11{\pm}1.29mm$, mesiodistal length is $6.80{\pm}1.18mm$, buccolingual length is $7.34{\pm}1.40mm$. Conclusion: Using the mean dimension of prepared natural dentition, it is expected to be able to fabricate customized zirconia block.

• Korean Journal of Food Science and Technology
• /
• v.35 no.4
• /
• pp.610-616
• /
• 2003

Five oats and 17 barley cultivars were ground, sieved (105, 210, 300, 425, 600 ${\mu}m$) and we have analyzed the ${\beta}-glucan$ contents to obtain grain fractions. The milling yields ranged $65.1{\sim}89.7%$ for barley and $53.4{\sim}73.5%$ for oat cultivars. Total ${\beta}-glucan$ contents of barley and oats become higher than those of the flour increasing the particle size. The soluble and insoluble ${\beta}-glucan$ contents of them were especially higher in medium and coarse particle size fractions. The contents of total, soluble and insoluble ${\beta}-glucan$ of barley were 1.5, 1.7 and 2.0 times higher than the whole flour before sieving and these content of oats were 2.1, 1.6 and 2.0 times, respectively. In this study, larger particle size would enrich the ${\beta}-glucan$ and it is desirable to consider the best particle size range to enrich the ${\beta}-glucan$ level, the water-solubility of the ${\beta}-glucan$ as well as cereal varieties.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.346-346
• /
• 2007

압전세라믹 재료는 현재 압전 변압기, actuator, transducer, sensor, speaker 등에 광범위하게 이용이 되고 있다. 이 중에서 압전세라믹 소결체를 이용한 스피커의 제조는 가공이 까다롭고, 대형의 크기로 제작 시 소자가 깨지는 등의 많은 제약을 받고 있으며, 저음 특성이 떨어져 응용 범위가 한정되어 있다. 따라서 최근에는 이러한 단점을 극복하기 위하여 세라믹/고분자 복합체를 이용한 필름 스피커를 제작하고자 시도하고 있다. 이러한 세라믹/고분자 0-3형 압전 복합체를 이용할 경우, 제품의 경량화를 실현할 수 있고, 크기나 환경의 영향을 거의 받지 않으므로, 고기능성 스피커로의 응용에 적합할 것으로 보인다. 따라서 본 연구에서는 PZT계의 세라믹와 PVDF, PVDF-TrFE, Polyester, acrylic resin 등의 여러 고분자 물질과의 복합체를 제조하여 압전특성을 평가하였다. 본 실험은 먼저 $(Pb_{1-a-b}Ba_aCd_b)(Zr_xTi_{1-x})_{1-c-d}(Ni_{1/3}Nb_{2/3})_c(Zn_{1/3}Nb_{2/3})_dO_3$ (이하 PZT라 표기)의 최적화 조성을 선택하여, $1050^{\circ}C$에서 소결된 분말을 48시간 ball milling방법 로 약 $1{\mu}m$ 크기로 분쇄하였다. 고분자 물질들은 알맞은 용제들을 선택하여 녹였다. 그 다음 소결된 PZT분말과 고분자를 50:50, 60:40, 65:35, 70:30등의 무게 분율로 혼합하고, 분산제, 소포제 등을 첨가하여 3단 roll mill을 이용하여 충분히 분산시켜 페이스트 (Paste)를 제조하였다. 제조된 페이스트를 ITO가 코팅된 PET필름 위에 스크린 프린팅 법을 사용하여 인쇄하여 $120^{\circ}C$에서 5분간 건조하였다. 코팅된 복합체의 두께는 약 $80{\mu}m$ 정도로 측정되었다. Ag 페이스트를 이용한 상부 전극 형성에도 스크린 프린팅 법을 적용하였다. 이를 $120^{\circ}C$에서 4 kV/mm의 DC 전계로 분극 공정을 수행한 후 전기적 특성을 평가하였다. 유전특성을 조사하기 위해서 LCR meter (EDC-1620)를 사용하였고, 시편의 결정구조는 XRD (Rigaku; D/MAX-2500H)을 통해 분석하였으며, 전자현미경(SEM)을 이용하여 미세구조를 분석하였다. 압전 전하상수$(d_{33})$ 값은 APC 8000 모델을 이용하여 측정하였다. PZT의 혼합비가 증가할수록 비유전율 및 압전 전하 상수 등의 전기적 특성이 증가되었다. 또 여러 고분자 물질 중에서 PVDF-TrFE 수지가 가장 우수한 특성을 보였다. 이는 PVDF-TrFE 수지가 압전성을 나타내기 때문인 것으로 판단되었다.

• Resources Recycling
• /
• v.19 no.6
• /
• pp.51-60
• /
• 2010

A study on the recovery of cobalt and lithium from Lithium Ion Battery(LIB) scraps has been carried out by a physical treatment - leaching - solvent extraction process. The cathode scraps of LIB in production were used as a material of this experiment. The best condition for recovering cobalt from the anode scraps was acquired in each process. The cathode scraps are dissolved in 2M sulfuric acid solution with hydrogen peroxide at $95^{\circ}C$, 700 rpm. The cobalt is concentrated from the leaching solution by means of a solvent extraction circuit with bis(2-ethylhexyl) phosphoric acid(D2EHPA) and PC88A in kerosene, and then cobalt and lithium are recovered as cobalt hydroxide and lithium carbonate by precipitation technology. The purity of cobalt oxide powder was over 99.98% and the average particle size after milling was about 10 lim. The over all recoveries are over 95% for cobalt and lithium. The pilot test of mechanical separation was carried out for the recovery of cobalt from the scraps. The $Co_3O_4$ powder was made by the heat treatment of $Co(OH)_2$ and the average particle size was about 10 ${\mu}m$ after grinding. The recovery was over 99% for cobalt and lithium each other and the purity of cobalt oxide was over 99.98%.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.189-189
• /
• 2008

Due to the environmental issue vast research is going on to replace the widely used lead contented piezoelectric materials. Bismuth sodium titanate (abbreviated as BNT) based bismuth sodium titanate-barium titanate (abbreviated as BNBT) ceramic was prepared by using modified method rather than conventional mixed oxide method. This modification was made to improve the properties of BNT based ceramic. In this procedure $BaTiO_3$ (abbreviated as BT) was prepared using conventional mixed oxide method. Analytical grade raw materials of $BaCO_3$ and $TiO_2$ were weighted and ball milled using ethanol medium. The mixed slurry was dried and sieved under 80 mesh. Then the powder was calcined at $1100^{\circ}C$ for 2 hours. This calcined BT powder was used in the preparation of BNBT. Stoichiometric amount of $Bi_2O_3$, $Na_2CO_3$, $TiO_2$ and BT were weighted and mixed by using ball mill. The used calcination temperature was $850^{\circ}C$ for 2 hours. Calcined powder was taken for another milling step. BNBT disks were pressed to 15 mm of diameter and then cold isostatical press (CIP) was used. Pressed samples were sintered at $1150^{\circ}C$ for 2 hours. The SEM microstructure analysis revealed that the grain shape of the sintered ceramic was polyhedral and grain boundary was well matched where as the sample prepared by conventional method showed irregular arrangement and grain boundary not well matched. And sintered density was better (5.78 g/cc) for the modified method. It was strongly observed that the properties of BNBT ceramic near MPB composition was found to be improved by the modified method compare to the conventional mixed oxide method. The piezoelectric constant dB of 177.33 pC/N, electromechanical coupling factor $k_p$ of 33.4%, dielectric constant $K_{33}^T$ of 688.237 and mechanical quality factor $Q_m$ of 109.37 was found.

• The Korean Journal of Food And Nutrition
• /
• v.25 no.3
• /
• pp.637-643
• /
• 2012

This study was performed to increase the utilization of rice and improve the productivity of jochung, traditional food in Korea. Two kinds of jochung products were prepared from steamed rice(SR) and wet-milled rice flour(WRF) by rice cultivated from 2006 to 2010. It is common to add a liquefying enzyme for rice liquefaction(4 $m{\ell}$/1,000 g rice, at $90{\sim}95^{\circ}C$, 3 h) and saccharogenic enzyme with malt(45 g/1,000 g rice, at $55{\sim}57^{\circ}C$, 6 h). In order to evaluate the quality characteristics of jochung, producing rate, pH, solidity, reducing sugar, dextrose equivalence(D.E.), viscosity, total phenolic compound, color value and sensory evaluation were carried out. In terms of the producing rate of jochung, WRF jochung was produced about 7.4% much more than SR jochung. There was no difference in producing rate between the jochung cultivated from 2006 to 2010 rice. The pH varied from 4.86~5.66, solidity was 79.48~82.28%. Color L value was 25.82~27.92, a value of 1.28~2.81, b value were 2.98~4.33. The results of sensory evaluation for jochung, as a whole, received higher score than for the commercial product(Daesang Co., Ltd, Seoul, Korea), overall acceptability score was the highest in the 2008SR. Reducing sugar, dextrose equivalence(D.E.) and total phenolic compounds were determined to be higher WRF jochung than SR jochung, while viscosity was lower WRF jochung than SR jochung. These results are thought to be due to increased surface area of rice by milling. SR jochung manufacturd by wet-milled rice flour will increase the producing rate for jochung, thereby saving manufacturing time and costs.