• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1999.06a
• /
• pp.14-19
• /
• 1999

In order to evaluate the effect of Nb on wear properties of high speed steel by powder metallurgy(PM-HSS), niobium-alloyed PM-HSS have been prepared by adding 0%, 1%, 3% and 5%Nb to PM-HSS of 6%W-5%Mo-4%Cr-5%V-5%Co presented in the previous paper. Sliding wear test have been conducted in various sliding speed conditions under the constant pressure using a pin-on-disc type machine. The results of this study shows that the wear resistance of PM-HSS has been increased by the addition of Nb in the range of experimental sliding speed. However, the amount of Nb shows to be unimportant parameter for the improvement of the wear resistance. It may be due to the thermal stability of carbide and high temperature properties of matrix by adding Nb comparing to the case of no addition.

• Journal of Welding and Joining
• /
• v.15 no.1
• /
• pp.92-100
• /
• 1997

Weld repair of ASTM A-470 class 8 high pressure (HP) steam turbine rotor steel has been performed to extend the service life of older fossil units. Microhardness measurements were conducted across the weldment from unaffected base metal (BM) to weld metal (WM). The hardness of the BM was VHN 253, however it dropped up to VHN 227 at the heat affected zone (HAZ) close to unaffected BM for multipass SAW. This area of hardness drop is called "siftening zone" and has a width of 0.5-0.6mm. During creep rupture test, failure occurred around the softening zone and rupture time was 772.4hr at 19Ksi (132 Mpa) and 593.deg. C. Multipass MIG and TIG welding have been employed to reduce the softening zone width. The softening zone width for MIG was 0.3-0.4mm and for TIG was zero-0.4mm depending on heat inputs. However creep rupture time was decreased as softening zone width reduced. Creep rupture time also showed a close relationship with heat inputs in TIG process. The higher heat input, the longer rupture time. Most failure occurred at intercritical HAZ (ICHAZ), however rupture location was shifted to coarse grained HAZ (CGHAZ) as heat input decreased. The rupture surface showed tearing and dimple which indicated transgranular fracture. fracture.

• Journal of the Korean Society for Heat Treatment
• /
• v.9 no.4
• /
• pp.229-233
• /
• 1996

This work has been carried out to reduce the softening of heat affected zone on laser surface alloying. Iron based rapid solidification material with $Cr_{5-10}$, $V_{1-3}$, $Mo_{3-7}$, $W_{2-5}$, $B_{7-8}$, $C_{2-3}$, $Si_{0.5-1}at%$ was alloyed on the surface of SM45C steel. The excellent softening resistance in alloyed and heat affected zone showed, which could be attributed to the formation of stable high temperature precipitates.

• Journal of the Korean Society of Safety
• /
• v.17 no.4
• /
• pp.11-18
• /
• 2002

We proposed a new experimental method which is required to easily observe the growth behavior of fatigue cracks. In the proposed method, the image data of cracks were stored into the computer while the cyclic loading was interrupted. After testing, crack length was determined using an image processing software which was developed by authors. By comparing the data measured by the image processing system with those by the manual measurement with a microscope, the effectiveness of the image processing system was established. If the proposed method is used to monitor and observe the crack growth behavior automatically, the time and efforts for fatigue test could be dramatically reduced.

• Applied Microscopy
• /
• v.43 no.4
• /
• pp.164-172
• /
• 2013

In this work, microstructural and hardness evolution of the X20 steel upon short-term creep test ($550^{\circ}C$ to $650^{\circ}C$, $180^{\circ}C$ to 60 MPa) was studied by using scanning electron microscope, electron backscattered diffraction, and transmission electron microscope, microhardness tester. After creep rupture, gauge and grip part of the specimens were microstructurally analyzed. Creep at the $650^{\circ}C$/60 MPa resulted in a rupture at 1,460 hours with growth of lath width from 1.31 to $2.87{\mu}m$ and a grain growth with a more equiaxed feature. There is a close relationship between Microhardness and lath width. The formation and coarsening of Laves phase, which was observed up to $600^{\circ}C$ of creep temperature, was accelerated by the applied stress. Slight coarsening of the $M_{23}C_6$ was observed in the $550^{\circ}C$ and $600^{\circ}C$ crept or aged specimens. The coarsening of $M_{23}C_6$ depended on the temperature, where specimens crept at $650^{\circ}C$ showed higher growth rate. The microstructural evolution of X20 after short-term creep test was extensively discussed in relation to the long-term creep/aging test reported in literatures.

• Journal of Korea Foundry Society
• /
• v.20 no.5
• /
• pp.323-329
• /
• 2000

The HSS consists of hard carbide and matrix of martensite, and so its characteristics of wear resistance, fracture resistance, and surface roughness are good. This study was undertaken to investigate the influence of Nb and V and manufacturing conditions on microstructural behaviors and characteristics in the HSS cylindrical specimens(90 $mm^{O.D.}$ ${\times}$ 60 $mm^{I.D.}$ ${\times}$ 50 $mm^H$) manufactured using VCC(Vertical Centrifugal Casting). In the specimen of Fe-2C-6Cr-1.5W-3Mo-4V alloy, the amount of MC carbide was increased and $M_7C_3$ carbide was decreased with the increase of V and Nb contents. The primary VC carbide was formed and followed by the rod-type eutectic MC carbide was formed in the cell boundary in 9%V added specimen. MC carbide was increased, and $M_7C_3$ carbide was decreased with the addition of Nb content. In the specimen containing more than 3%Nb, primary NbC carbide was formed within the cell of matrix. With increase in rpm, cell and carbides became fine, and amount of carbide $M_7C_3$ was decreased due to increase in cooling rate.

• Journal of radiological science and technology
• /
• v.39 no.4
• /
• pp.595-600
• /
• 2016

The diagnostic multileaf collimator(MLC) was designed for patient dose reduction in diagnostic radiography We used monte carlo simulation code (MCNPX, LANL, USA) to evaluate efficiency of shielding material for making diagnostic MLC as preliminary study. The diagnostic radiography unit was designed using SRS-78 program according to tube voltage (80,100,120 kVp) and acquired energy spectrums. The shielding material was SKD11 alloy tool steel that is composed of 1.6% carbon(C), 0.4% silicon(Si), 0.6% manganese (Mn), 5% chromium (Cr), 1% molybdenum(Mo) and vanadium(V). The density of it was $7.89g/cm^3$.Using tally card 6, we calculated the shielding efficiency of MLC according to tube voltage. The results was that 98.3% (80 kVp), 95.7 %(100 kVp), 93.6% (120 kVp). We certified efficiency of diagnostic MLC fabricated from SKD11 alloy steel by monte calro simulation. Based on the results, we designed the diagnostic MLC and will develop the diagnostic MLC for reduction of patient dose in diagnostic radiography.