• Proceedings of the KSME Conference
• /
• 2001.06a
• /
• pp.268-273
• /
• 2001

Fossil power plants operated in high temperature condition are composed of components such as turbine, boiler, and piping system. Among these components, turbine blades made with 12%Cr steel operate at a temperature above $500^{\circ}C$. Due to the long term service, turbine blades experience material degradation manifested by change in mechanical and microstructural properties. The need to make life assessment and to evaluate material degradation of turbine blade is strongly required but in reality, there is a lack of knowledge in defining failure mechanism and fundamental data for this component. Therefore, in making life assessment of turbine blade, evaluation of material degradation must be a priority. For this purpose, evaluation of toughness degradation is very important. The major cause of toughness degradation in 12Cr turbine blade is reported to be critical corrosion pitting induced by segregation of impurity elements(P etc.), coarsening of carbide, and corrosion, but the of materials for in-service application. In this study, the purpose of research is focused on evaluating toughness degradation with respect to operation time for 12%Cr steel turbine blade under high temperature steam environment and quantitatively detecting the degradation properties which is the cause of toughness degradation by means of non-destructive method, electrochemical polarization.

• Journal of the Korean Institute of Gas
• /
• v.16 no.5
• /
• pp.28-34
• /
• 2012

Material degradation of Cr steels in using for boiler tubes was studied in the relation of microstructural changes like carbide behavior and mechanical properties of hardness and creep-rupture life. The carbide dissolution was occurred in 2Cr steel of T22 during high temperature operation. And the grain refinement within martensite lath of 12Cr steel of X20 was derived by the high temperature-long time exposure. But the specific phenomena of material degradation which might be represented by hardness or creep-rupture time of the used tubes were not shown in all the tubes of T22 and X20 even in the fire-side using.