• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.1 no.2
• /
• pp.79-93
• /
• 1991

With the advent of ULSI, many problems in previous metallization techniques and interconnection materials have become more serious. In this work, selective deposition of copper to fill the submicron contact has been tried. After forming electro-deposited copper films on p-type (100) silicon wafer using 0.75M $CuSO_4{\cdot}$5H_2O$ as an electrolyte, the effect of deposition time, current density and concentration of an additive on film properties were investigated. Film thickness, particle size and resistivity were analyzed by Alpha Step, SEM and 4 - point probe measurement respectively. The deposition rate was about $0.5-0.6\mu\textrm{m}$/min at $2A/dm^2$ and the particle size increased with increasing current density. The resistivities of electro-deposited copper films were about $3-6{\mu}{\Omega}{\cdot}$cm for the particle size above $4000{\AA}$. By the addition of 0.2 g/l gelatin, the particle size was reduced to less than $0.1{\mu}m $ and selective plugging of copper on submicron contacts could be successfully achieved.

• Journal of Korean Society of Environmental Engineers
• /
• v.37 no.12
• /
• pp.668-673
• /
• 2015

Alumina-based catalysts with different Ce loadings were studied in the decomposition of $CF_4$ using microwave heating system. Heating material of microwave system used Silicon Carbide. The crystallographic phases of catalysts were investigated by XRD and decomposition rates of $CF_4$ were examined by GC-TCD. The catalysts of 10 wt% Ce modified $Al_2O_3$ showed higher $CF_4$ decomposition rate than un-modified $Al_2O_3$ for $500^{\circ}C$ reaction temperature. The k value of catalysts shows the order of $Ce(20)/Al_2O_3=Ce(0)/Al_2O_3<Ce(5)/Al_2O_3<Ce(10)/Al_2O_3$. XRD patterns of $Ce(0)/Al_2O_3$ were no difference before and after the reaction and showed $Al_2O_3$ phases. With the increase in Ce loadings, $CeO_2$, $AlF_3$ of XRD peaks was observed. The results was indicated that Ce modifed $Al_2O_3$ than un-modifed $Al_2O_3$ was decreased reaction temperature to $200^{\circ}C$ with same decomposition rate. Also the appropriated cerium sulfate loadings on $Al_2O_3$ were 5~10 wt%.

• Korean Journal of Soil Science and Fertilizer
• /
• v.19 no.1
• /
• pp.38-49
• /
• 1986

In order to improve effectiveness of rhizobia-legume symbiotic nitrogen fixation, ecological and physiological characteristics of indigenous rhizobia distributed in Korea soil, that is, the effects of soybean cultivation, physico-chemical properties and climate on the population of indigenous rhizobia and other soil microbes were investigated. The results were summarized as follows: The population of indigenous rhizobia were ranged from $5.1{\times}10^4$ cells to $196.8{\times}10^4$ cells per gram of soil in soybean cultivated soils but from $1.6{\times}10^4$ cells to $78.6{\times}10^4$ cells per gram of soil in soybean un-cultivated soils sampled from 9 different agro-climate zone. The highest population was observed in a soybean cultivated loamy soil from southern part of Korea. The content of available phosphate, exchangeable Ca, Mg, Cu, and B in soil were positively correlated but active Fe, exchangeable Al, Na, and $SO_4$ were inversely correlated to the population of indigenous rhizobia. The inverse relationship was observed between the number of indigenous rhizobia and actinomycetes.

• Membrane Journal
• /
• v.30 no.3
• /
• pp.181-189
• /
• 2020

In the present study, a biomimetic alumina membrane was fabricated by using selenic acid as an electrolyte to overcome the asymmetry limit of the square pulse anodization process. The prepared membrane has conical channels with a minimum diameter of 10 nm, a maximum diameter of 50 nm, and a length of 5 ㎛. The rectification property was higher than membranes fabricated by sulfuric acid. It showed 2.9 times larger current at +1 V than -1 V. Also, the membrane, which sulfonic acid group was introduced by surface modification, showed 4.2 times larger rectification property at -1 V than +1 V. Theoretical verifications were supported by the numerical analyses of 2D models. The results of the present study present a convenient method to fabricate two type membranes with different rectification properties and are expected to be used to control ion transport.

• Journal of the Korean Chemical Society
• /
• v.20 no.6
• /
• pp.469-478
• /
• 1976

Clinoptilolite zeolite samples were treated with hydrochloric acid, sulfuric acid and phosphoric acid of different strength and the adsorption characteristics and crystal structures of the original and acid-treated clinoptilolites were studied. By treating with hydrochloric acid, the adsorbed amount increased to 5-fold for nitrogen, to 3-fold for benzene, but for methanol no significant change was observed. As acid strength increased further, there were declines both in adsorption capacity and crystallinity. The results showed that the increase of adsorbed amount was caused by the rearrangement of the pore entrance and cation exchange. A method for determination of clinoptilolite content in natural mineral based on benzene adsorption on acid-treated sample is proposed. By this method, the original sample used in this study was found to contain approximately 40% of clinoptilolite. Using pulse technique in micro-catalytic reactor system, the catalytic activities of hydrochloric acid-treated clinoptilolites in cumene cracking and toluene disproportionation reactions were measured. For cumene cracking reaction, the maximum conversion was observed for the 0.5 N hydrochloric acid-treated sample. It is instructive to note that the maximum benzene adsorption was also observed for the sample treated with 0.5 N HCl. This suggest that the conversion rate was determined mainly by the rate of transport of reactants and the products through the pore structure. In the toluene disproportionation reaction, the same trend was observed. But the rate of deactivation was high for samples with strong acid sites. Since catalyst having higher activity was deactivated more easily, the conversion maximum was shifted to the sample treated with higher concentration of acid, -1N. The catalytic activity of $Ca^{2+} and La^{3+} ion exchanged samples for the toluene disproportion was much lower than that of acid-treated samples. Introduction of Ca^{2+} and La^{3+}$ into the pore structure apparently decreases the effective pore diameter of acid-treated clinoptilolite thus limiting the diffusion of reactants and products.

• Composites Research
• /
• v.13 no.4
• /
• pp.42-53
• /
• 2000

A study has been made to establish an optimum condition in the surface treatment and curing method that is important for the fabrication of Al 7075/CFRP laminates. PAA(Phosphoric Acid Anodizing) provided a good adhesive strength and FPL(Sulfuric / Sodium Dichromate Acid Etching) had a similar adhesive strength with PAA. On the other hand, the poor adhesive strength was shown on vapor degrease and CAA(Chromic Acid Anodizing). By using the atomic force microscope(AFM), it was found that the PAA oxide surface obviously had a greater degree of microroughness as compared to vapor degrease, CAA and FPL treated surfaces. These results support the concept of a mechanical interlocking of the adhesive with-in the oxide pores as the predominant adhesion mechanism. In curing methods, the adhesive strength of co-curing method was higher than that of secondary curing method. With respect to stability of specimen shape, the secondary curing method was better than co-curing method. DMA(Dynamic Mechanical Analysis) test revealed $T_g$ in curing times over 60 min is nearly same, so it is estimated they will have similar degree of curing and joint durability in using FM300M adhesive film.

• Journal of the Mineralogical Society of Korea
• /
• v.4 no.1
• /
• pp.1-10
• /
• 1991

Tosudite from the Sungsan mine, Korea is an alteration product of rhyolitic tuff in the cretaceous Hwangsan Formation. It is associated with illite, dickite, nacrite or quartz and also found in the cavities of black claystone. X-ray diffraction and chemical analyses show that the Sungsan tosudite is a lithium-bearing aluminous 1:1 regularly interstratified mineral of di, dioctahedral chlorite and smectite. Its structural formula is $(K_{0.73}Na_{0.02}Ca_{0.07})(Si1_{13.23}Al_{2.77})(Li_{0.52}Mg_{0.08}Mn_{0.01)Fe^{3+}_{0.07}Al_{12.33})O_{40}(OH)_{20}$ and it suggests that Sungsan tosudite consists of regularly interstratified Li-donbassite and beidellite. DTA and TG curves as well as IR absorption data also support such a result. Temperature of formation of tosudite is inferred to be between $110{\circ}$ and $270{\circ}C$.

• Resources Recycling
• /
• v.28 no.5
• /
• pp.42-50
• /
• 2019

In this study, the precipitation reaction of vanadium and ammonium chloride in aqueous solution was investigated in order to recover vanadium. Ammonium metavanadate having a crystal structure of [$NH_4VO_3$] was precipitated from aqueous solution containing vanadium at pH 9.2 ~ 9.4, and ammonium polyvanadate having a crystal structure of [$(NH_4)_2V_6O_{16}$] was precipitated when the pH of the aqueous solution containing vanadium was adjusted with sulfuric acid. Ammonium polyvanadate [$(NH_4)_2V_6O_{16}$] precipitated at a temperature of $80{\sim}90^{\circ}C$ and pH 2, and at a temperature of $40^{\circ}C$ and pH 6 ~ 8 of aqueous solution. In the acidic region of aqueous solution pH 2, the vanadium content of the aqueous solution should be at least 3,000 mg/L and the precipitation temperature should be maintained at $80^{\circ}C$ or higher in order to obtain a precipitation ratio of 99% or more. When the ammonium vanadate was precipitated in the alkaline region, the vanadium content was more than 10,000 mg/L and the precipitation temperature was maintained at $40^{\circ}C$ to increase the precipitation ratio. Aluminum was not precipitated regardless of the vanadium content and pH of the aqueous solution. However, the iron component reacts with ammonium chloride to precipitate into ammonium jarosite. Therefore, Fe component must be preferentially removed in order to increase the recovery of vanadium.

• Journal of Bio-Environment Control
• /
• v.13 no.4
• /
• pp.233-239
• /
• 2004

This research was conducted to determine the effect of soil pH change followed by leaching with ground water on crop growth, yield and nutrient uptake of strawberry. Treatments were leaching with ground water (A), hydrated lime application of dissolved portion in $500g{\cdot}L^{-1}$ solution followed by leaching (B), application of $Al_2SO_4$ solution with the concentration of $0.75g{\cdot}L^{-1}$ followed by leaching (C), pH elevation by (B) followed by pH lowering by (C), then leaching (D). Soil samples taken before experiment had 6.0 in soil pH. But the pH of all treatments taken after pH changes and leaching were in the range from 5.8 to 6.2 without statistical differences among treatments. Electrical conductivity of soils taken before experiment was $1.82dS{\cdot}m^{-1}$ and those of (A), (B), (C), and (D) were 1.65, 1.72, 1.71 and $1.83dS{\cdot}m^{-1}$, respectively. The plant height in treatment (C) was 20.4 cm at 80 days after transplanting which was the highest among treatments tested. The other growth characteristics did not show statistical differences among treatments. Tissue contents of Fe, Mn, Zn, Cu and B in treatment (C) were higher than those of other treatments at 80 days after transplanting. The treatment (C) had the highest number of special sizes and fruit weight per 50 plants such as 137 and 3.784 g, respectively. The treatment also had 3.123 kg in total fruit weight and 2,489 kg in marketable fruit weight per 10 are. The treatment (B) also had good results such as 2,820 kg in marketable fruit weight per 10 are.

• Conservation Science in Museum
• /
• v.30
• /
• pp.23-46
• /
• 2023

The Jija Chongtong Gun, owned by Seokdang Museum of Dong-A University, is a tubedstyle heavy weapon of the battlefield in the mid-Joseon Dynasty and is the second largest firearm after Cheonja Chongtong. The original surface color of the Jija Chongtong Gun was obscured by foreign substances and therefore it was judged that its condition requires the conservation treatment. For stable conservation treatment, gamma ray and X-ray non-destructive transmission surveys was conducted to determine the internal structure and conservation condition. And the component analysis on the material components and surface contaminants of Jija Chongtong Gun was conducted by utilizing the p-XRF component analysis, SEM-EDS component analysis, and XRD analysis. As a result of the gamma-ray and X-ray non-destructive transmission investigation, a large amount of air bubbles was observed inside Jija Chongtong Gun, and the part that appeared to be a chaplet by visual observation was not identified. As a result of gamma-ray and p-XRF component analysis, it was confirmed that Jija Chongtong Gun was bronze made of copper (Cu), tin (Sn), and lead (Pb) alloy. As a result of surface analysis of foreign substances using SEM-EDS, it was confirmed that the main components of white foreign substances were calcium (Ca), sulfur (S), and titanium (Ti). Titanium was presumed to be titanium dioxide (TiO₂), the main component of white correction fluid. The red foreign substance was confirmed to contain barium (Ba) as its main ingredient, and was presumed to be barium sulfate (BaSO₄), an extender pigment in paint. White and red contaminants, mainly composed of titanium and barium, are presumed to have been deposited on the surface in recent years. The yellow foreign substances were confirmed to be aluminum (Al) and silicon (Si), and were presumed to have originated from soil components. As a result of SEM-EDS and XRD component analysis, the white foreign substance was confirmed to be gypsum (CaS). Based on the results of component analysis, surface impurities were removed, stabilization treatment, and strengthening treatment were performed. During the conservation process, unknown inscriptions Woo (右), Byeong (兵), Sang (上), and Yi (二) were discovered through a portable microscope and precise 3D scanning. In addition, the carving method, depth, and width of the inscription were measured. Woo Byeong Sang is located above Happo Fortress in Changwon, and Yi can be identified as the second hill.