• Journal of the Korean institute of surface engineering
• /
• v.55 no.6
• /
• pp.441-447
• /
• 2022

Silicon-based materials are one of the most promising anode active materials in lithium-ion battery. A carbon layer decorated on the surface of silicon particles efficiently suppresses the large volume expansion of silicon and improves electrical conductivity. Carbon coating through chemical vapor deposition (CVD) is one of the most effective strategies to synthesize carbon- coated silicon materials suitable for mass production. Herein, we synthesized carbon coated SiOx via pilot scale CVD reactor (P-SiO_x@C) and carbon coated SiO_x via industrial scale CVD reactor (I-SiO_x@C) to identify physical characteristic changes according to the CVD capacity. Reduced size silicon domains and local non-uniform carbon coating layer were detected in I-SiO_x@C due to non-uniform temperature distribution in the industrial scale CVD reactor with large capacity, resulting in increased surface area due to severe electrolyte consumption.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.255-255
• /
• 2016

Resistive random access memory (ReRAM)는 낮은 동작 전압, 빠른 동작 속도, 고집적화 등의 장점으로 인해 차세대 비휘발성 메모리 소자로써 많은 관심을 받고 있다. 최근에 ReRAM 절연막으로 NiOx, TiOx, AlOx TaOx, HfOx와 같은 binary metal oxide 물질들을 적용하는 연구가 활발히 진행되고 있다. 특히, HfOx는 안정적인 동작 특성을 나타낸다는 점에서 ReRAM 절연막 물질로 적합하다고 보고되고 있다. ReRAM 절연막을 형성할 때, 물리 기상 증착 방법 (PVD)이나 화학 기상 증착법 (CVD)과 같은 방법이 많이 이용된다. 이러한 증착 방법들은 고품질의 박막을 형성시킬 수 있는 장점이 있다. 하지만, 높은 온도에서의 공정과 고가의 진공 장비가 이용되기 때문에 경제적인 문제가 있으며, 기판 또는 금속에 플라즈마 손상으로 인한 문제가 발생할 수 있다. 따라서 이러한 문제점들을 개선하기 위해 용액 공정이 많은 관심을 받고 있다. 용액 공정은 공정과정이 간단할 뿐만 아니라 소자의 대면적화가 가능하고 공정온도가 낮으며 고가의 진공장비가 필요하지 않은 장점을 가진다. 따라서 본 연구에서는, 용액공정을 이용하여 HfOx 기반의 ReRAM 제작하였고 $25^{\circ}C$와 $85^{\circ}C$에서 ReRAM의 동작특성에 미치는 compliance current의 영향을 평가하였다. 실험 방법으로는, hafnium chloride (0.1 M)를 2-methoxyethanol에 충분히 용해시켜서 precursor를 제작하였다. 이후, p-type Si 기판 위에 습식산화를 통하여 300 nm 두께의 SiO2 절연층을 성장시킨 후, 하부전극을 형성하기 위해 electron beam evaporation을 이용하여 10/100 nm 두께의 Ti/Pt 전극을 증착하였다. 순차적으로, 제작된 산화물 precursor를 이용하여 Pt 위에 spin coating 방법으로 1000 rpm 10 초, 6000 rpm 30초의 조건으로 두께 35 nm의 HfOx 막을 증착하였다. 최종적으로, solvent 및 불순물을 제거하기 위해 $180^{\circ}C$의 온도에서 10 분 동안 열처리를 진행하였으며, 상부 전극을 형성하기 위해 electron beam evaporation을 이용하여 Ti와 Al을 각각 50 nm, 100 nm의 두께로 증착하였다. ReRAM 동작에서 compliance current가 미치는 영향을 평가하기 위하여 compliance current를 10mA에서 1mA까지 변화시키면서 측정한 결과, $25^{\circ}C$에서는 compliance current의 크기와 상관없이 일정한 메모리 윈도우와 우수한 endurance 특성을 얻는 것을 확인하였다. 한편, $85^{\circ}C$의 고온에서 측정한 경우에는 1mA의 compliance current를 적용하였을 때, $25^{\circ}C$에서 측정된 메모리 윈도우 크기를 비슷하게 유지하면서 더 우수한 endurance 특성을 얻는 것을 확인하였다. 결과적으로, 용액공정 방법으로 제작된 ReRAM을 측정하는데 있어서 compliance current를 줄이면 보다 우수한 endurance 특성을 얻을 수 있으며, ReRAM 소자의 전력소비감소에 효과적이라고 기대된다.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2004.05a
• /
• pp.141-141
• /
• 2004

다이아몬드상 탄소(diamond-like carbon, DLC) 박막은 명칭에 함축된 의미로 알 수 있듯이 다이아몬드와 유사한 특징을 지니고 있다. DLC 박막은 비정질(amorphous) 고상 탄소 박막으로 구조적으로 Sp$^1$, Sp$^2$, Sp$^3$의 결합들로 구성되어 있다. DLC 박막의 물성으로는 우수한 경도, 내마모성, 낮은 마찰계수, 화학적 안정성 그리고 적외선(IR) 영역에서의 높은 투과율 등이 있다. 현재 DLC 박막은 앞서 열거된 물성들의 장점을 활용하여 다양한 산업분야에서 활발히 응용되고 있다.(중략)

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.3 no.2
• /
• pp.107-116
• /
• 1993

Tungsten thin film was deposited on Si( 100) substrate by either Si substrate reduction of W$F_6$( case 1) or Si$H_4$ reduction of W$F_6$( case 2) in LPCVD system The morphology and properties of deposited films for both cases were examined. The crystal structure for both cases was determined to be bec (body centered cubic). The amount of tungsten and the grain size in thin films were increased as the film grows. From the experimental results and theoretical considerations, it can be understood that the tungsten thin film grows by the volmer-weber growth mode, that is, island growth. The detailed tungsten thin film growth mode is presented. It was also found that the initial polycrystal structure of tungsten thin film developed into single crystal structure as the film grew in thickness.

• Journal of the Korean Vacuum Society
• /
• v.10 no.1
• /
• pp.104-111
• /
• 2001

B-doped hydrogenated amorphous silicon carbide (a-SiC:H) thin films were prepared by plasma-enhanced chemical-vapor deposition in a gas mixture of $SiH_4, CH_4,\;and\; B_2H_6$. Physical and chemical properties of a-SiC:H films grown with varing the ratio of $B_2H_6/(SiH_4+CH_4)$ were characterized with various analysis methods including scanning electron microscopy (SEM), X-ray diffractometry (XRD), Raman spectroscopy, Fourier-transform infrared (FTIR) spectroscopy, secondary ion mass spectroscopy (SIMS), UV absorption CH_4spectroscopy and electrical conductivity measurements. With the B-doping concentration, the doping efficiency and the micro-crystallinity were decreased and the film became amorphous when $B_2H_6/(SiH_4{plus}CH_4)$ was over $5{\times}10^{-3}$. The addition of $B_2H_6$ gas during deposition decreased the H content in the film by lowering the quantity of Si-C-H bonds. Consequently, the optical band gap and the activation energy of a-SiC:H films were decreased with increasing the B-doping level.

• Journal of the Korean Ceramic Society
• /
• v.39 no.5
• /
• pp.479-483
• /
• 2002

Silicon dioxide thick film using silica optical waveguide cladding was fabricated by Plasma Enhanced Chemical Vapor Deposition(PECVD) method, at a low temperature ($320^{\circ}$C) and from $(SiH_4+N_2O)$ gas mixtures. The effects of deposition parameters on properties of $SiO_2$ thick films were investigated by variation of $N_2O/SiH_4$ flow ratio and RF power. After the deposition process, the samples were annealed in a furnace at $1150^{\circ}$C, in N2 atmosphere, for 2h. As the $N_2O/SiH_4$ flow ratio increased, deposition rate decreased from 9.4 to 2.9 ${\mu}m/h$. As the RF power increased, deposition rate increased from 4.7 to 6.9 ${\mu}m/h$. The thickness and the refractive index measurements were measured by prism coupler. X-ray Photoelectron Spectroscopy(XPS) and Fourier Transform-infrared Spectroscopy(FT-IR) were used to determine the chemical states. The cross-section of films was observed by Scanning Electron Microscopy(SEM).

• 한국신재생에너지학회:학술대회논문집
• /
• 2005.06a
• /
• pp.205-208
• /
• 2005

최근 열선 화학 기상 증착법(HWCVD)은 낮은 온도에서 TFT용 Poly Si 중착을 할 수 있다는 점과 실리콘 박막을 빠른 속도로 증착할 수 있다는 점에서 각광을 받고 있다. 본 연구에서는 HWCVD를 이용하여 태양전지를 제조하고 그 특성을 평가하였다. 조건에 따른 실리콘 박막의 특성 변화를 알기 위해 corning glass 및 실리콘 wafer에 다양한 조건에서 단위 박막(intrinsic layer)을 증착하였고 이 결과를 바탕으로 p/i/n 구조의 태양전지를 제조하였다. Ta 열선 온도는 1700-2000도였고 가스 원료인 $SiH_4$와 수소의 비율을 조절하면서 그 영향을 관찰하였다. 태양전지의 경우 p충과 n충은 PECVD로 증착하였으며 단위박막 및 태양전지 i충 증착시 기판과 열선간의 거리는 7cm, 기판 온도는 $200^{\circ}C$와 $250^{\circ}C$로 고정하였고 작업압력은 30mTorr였다. 단위 박막 특성 평가를 위해 암/광 전도도, SEM, Raman Scattering, FT-IR등을 사용하였으며 태양전지 특성 평가를 위해 I-V 및 Spectral response를 측정하였다. 열선 온도가 증가함에 따라 증착속도 및 결정화 분율은 증가하였다. 특히 비정질에서 결정질로 전이되는 구간은 매우 좁았으며 여러 분석 방법에서 일치되는 결과를 보였다. $SiH_4$ 유량이 늘어날수록 비정질이 결정질로 바뀌는 열선 온도가 증가하였으며 기판 온도가 낮을 경우 또한 결정으로 바뀌는 열선 온도가 증가하였다. 태양전지의 경우 열선 온도가 증가함에 따라 $V_{oc}$ 및 W가 낮아졌으며 $J_{sc}$, 는 증가하는 경향을 보였으며 결정질 비율이 증가하는 것을 관찰할 수 있었다. 이러한 경향은 quantum efficiency 결과에서도 확인할 수 있었다.용을 반복하면서 석재 내부와 외부의 암석 및 결정에 균열과 미세열극 등이 생성되어 석재 자체의 구조적 안정성에 영향을 주고 있다. 따라서 감은사지 석탑은 지리적 환경 차이로 인해 일반적인 환경의 석조물들과는 다른 형태의 풍화양상을 보이고 있어서 풍화양상 및 풍화형태에 대한 정확한 연구와 이해를 바탕으로 보존대책이 마련되어야 한다.되었다. 이런 모든 시편들을 각 탈염방법에 따라 탈염처리한 후 XRD와 SEM-EDS으로 분석한 결과 인철광과 침철광은 어떠한 변화도 보이지 않았고, 다만 적금광으로 동정된 시편만이 잔존하지 않았다. 철기 제작별 $Cl^-$ 이온 추출량과 탈염효과에 대한 비교 실험은 이온 크로마토그래피 분석 결과와 마찬가지로 단조 철제유물이 주조 철제보다 $Cl^-$ 이온을 많이 가지고 있었으며, 탈염 처리 후에는 $Cl^-$ 이온은 전혀 발견되지 않았다. 이상의 결과 $K_2CO_3$와 Sodium 용액은 탈염처리에서 가장 적합한 탈염처리 용액으로 알수가 있었으며 특히 어떠한 탈염 용액으로 유물을 처리한다 해도 철제유물에 생성된 부식물은 제거되지 않는다는 것을 알게 되었다. 따라서 보존처리자는 유물 표면의 부식 상태만을 보고 처리하기 보다는 철기제작물로 고려하여 처리하는 것이 필요하다. 또한 금속에 부식을 야기시키는 $Cl^-$ 이온과 부식물을 완전하게 제거하여 탈염처리를 하는 것이 유물 부식을 최대한 지연시킬 수 있는 것이라 생각된다.TEX>$88\%$)였다.(P=0.063). 결론: 본 연구에서는 MTHFR C/T & T/T 유전자 다형성이 위암의 발생과 그 위치에 대해 관련이 있는 것으로 여겨지고, 흡연력, 음주력과는 관련이 없는 것으로 여겨진다.험이 커지는 경향을 보였으나, 나이 및 병기, 종양의 크기, MD-BED $Gy_{10}$ 등의 예후 인자를 보정한 다변

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.142-142
• /
• 2010

본 논문은 단결정 및 다결정 실리콘 기판 상에 아산화질소 플라즈마 처리를 통하여 형성한 초박형 실리콘 옥시나이트라이드 박막의 특성과 이의 어플리케이션에 관한 것이다. 초박형 절연막은 현재 다양한 전자소자의 제작과 특성 향상을 위하여 활용되고 있으나 일반적인 화학 기상 증착 방법으로는 균일도를 확보하기 어려운 문제점을 가지고 있다. 디스플레이의 구동소자로 활용되는 박막 트랜지스터의 특성 향상과 비휘발성 메모리 소자의 터널링 박막에 응용하기 위하여 초박형 실리콘 옥시나이트라이드 박막의 증착과 이의 특성을 분석하였고, 실제 어플리케이션에 적용하였다. 실리콘 산화막과 실리콘 계면상에 존재하는 질소는 터널링 전류와 결함 형성을 감소시키며, 벌크 내에 존재하는 질소는 단일 실리콘 산화막에 비해 더 두꺼운 박막을 커패시턴스의 감소없이 이용할 수 있는 장점이 있다. 아산화질소 플라즈마를 이용하여 활성화된 질소 및 산소 라디칼들이 실리콘 계면을 개질하여 초박형 실리콘 옥시나이트라이드 박막을 형성할 수 있다. 플라즈마 처리 시간과 RF power의 변화에 따라 형성된 실리콘 옥시나이트라이드 박막의 두께 및 광학적, 전기적 특성을 분석하였다. 아산화질소 플라즈마 처리 방법을 사용한 실리콘 옥시나이트라이드 박막을 시간과 박막 두께의 함수로 전환해보면 초기적으로 증착률이 높고 시간이 지남에 따라 두께 증가가 포화상태에 도달함을 확인할 수 있다. 아산화질소 플라즈마 처리 시간의 변화에 따라 형성된 박막의 전기적인 특성의 경우, 플라즈마 처리 시간이 짧은 실리콘 옥시나이트라이드 박막의 경우 전압의 변화에 따라 공핍영역에서의 기울기가 현저히 감소하며 이는 플라즈마에 의한 계면 손상으로 계면결합 전하량이 증가에 기인한 것으로 판단된다. 또한, 전류-전압 곡선을 활용하여 측정한 터널링 메카니즘은 2.3 nm 이하의 두께를 가진 실리콘 옥시나이트라이드 박막은 직접 터널링이 주도하며, 2.7 nm 이상의 두께를 가진 실리콘 옥시나이트라이드 박막은 F-N 터널링이 주도하고 있음을 확인할 수 있다. 결론적으로 실리콘 옥시나이트라이드 박막을 활용하여 전기적으로 안정한 박막트랜지스터를 제작할 수 있었으며, 2.5 nm 두께를 경계로 터널링 메커니즘이 변화하는 특성을 이용하여 전하 주입 및 기억 유지 특성이 효과적인 터널링 박막을 증착하였고, 이를 바탕으로 다결정 실리콘 비휘발성 메모리 소자를 제작하였다.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.9 no.1
• /
• pp.39-42
• /
• 1999

Nitrogen-doped SiC(3C) (N-SiC(3C)) epliayers were grown on Si(111) substrate at $1250^{\circ}C$ using chemical vapor deposition (CVD) technique by pyrolyzing tetramethylsilane(TMS) in $H_{2}$ carrier gas. SiC(3C) layer was doped using $NH_{3}$ during the CVD growth to be n-type conduction. Physical properties of N-SiC(3C) were investigated by Fourier transform infrared (FTIR) spectroscopy, X-ray diffraction (XRD) patterns, Raman spectroscopy, cross-sectional transmission electron microscopy (XTEM), Hall measurement, and current-voltage(I-V) characteristcs of the N-SiC(3C)/Si(p) diode. N-SiC(3C) layers exhibited n-type conductivity. The n-type doping of SiC(3C) could be controlled by nitrogen dopant using $NH_{3}$ at low temperature.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.11 no.2
• /
• pp.56-59
• /
• 2001

Thin films of hydrogenated amorphous silicon (a-Si : H) of different compositions were deposited on Si(100) wafer and glass by RF plasma-enhanced chemical vapor deposition (PECVD). In the present work, we have investigated the effect of the If. power on the properties, such as optical band gap, transmittance and crystallinity, of crystalline silicon thin films. Raman data show that the material consists of an amorphous and crystalline phase for the co-presence of two peaks centered at 480 and 520cm$^{-1}$. X-ray spectra confirmed of crystallites with (111) orientation at 300w The transmittance of thin films was measured by UV-VIS spectrophotometer. In addition, Si-H chemical bondings were studied by Fourier Transform Infrared (FT-IR) spectroscopy.