• Journal of the Korea Concrete Institute
• /
• v.18 no.6 s.96
• /
• pp.793-800
• /
• 2006

This paper reports test results to assess the influence of superplasticizers and different admixture on the flow and compressive strength development of cementless mortar using developed hwangtoh binder. Test specimens were classified into four groups: series for I the mixing ratio of superplasticizers, series II for a kind and replacement level of admixtures according to the variation of water/hwangtoh binder ratio, series III for the specific surface area and replacement level of ground granulated blast-furnace slag and series IV for the replacement level of powered superplasticizer agent developed to improve slump loss of concrete. The proper replacement level of each admixture is proposed for enhancement the flow and compressive strength of the hwangtoh binder mortar.

• Journal of the Korea Concrete Institute
• /
• v.16 no.3 s.81
• /
• pp.319-326
• /
• 2004

This paper investigates the effect of the concrete containing mineral admixtures(pozzolanic materials such as fly-ash, ground granulated blast-furnace slag, silica fume and meta kaolin) on the resistance properties to chloride ion invasion. The purposed testing procedure was applied to the concrete replaced mineral admixtures for 3${\~}$4 replacement ratios under water-binder ratios ranged from 0.40 to 0.55. For the electro-migration test, Tang and Nilsson's method was used to estimate the diffusion coefficient of chloride ion. As a results, the water-binder ratios, kinds of mineral admixtures and replacement ratios, water curing periods had a great effect on the diffusion coefficient of chloride ion, and the optimal replacement ratios had a limitation for each mineral admixtures. Also, the use of mineral admixtures by mass(replacement of OPC) enhance the resistance ability against chloride penetration compared with the plain concrete. The compressive strength was shown related to the diffusion coefficient of chloride ion, the compressive strength increases with the diffusion coefficient of chloride ion decreasing. Below the 50 MPa, the variation of diffusion coefficient of concrete replaced mineral admixtures was bigger than that of plain concrete.

• Journal of the Korea Institute of Building Construction
• /
• v.13 no.3
• /
• pp.282-290
• /
• 2013

In this study, the adjustment range of mixture factor with replacement mineral admixture was reviewed to secure the mixture change data of high volume concrete compared to general concrete. When changing the concrete mix to high volume concrete within the universal concrete mixing, the adjustment range of mixture to ensure optimum quality is as follows. Unit-water content is $20{\sim}30kg/m^3$ downward. Fine aggregate ratio dropped by approximately 1% when W/B was reduced by 5%, and it is reduced by approximately 0.12% when there is a 5% increase in the total replacement rate. When the FA replacement rate was increased by 5%, the AE agent was approximately 20% to 30% higher compared with the conventional one. When the FA and BS replacement rate rose by 5%, W/B was reduced by about 1 to 4%.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.4 no.2
• /
• pp.143-148
• /
• 2016

The aim of research is inducing the optimum proportion of fly ash(FA) and blast furnace slag(BS) for ternary cement. In this research, hence, the fundamental properties of mortar mixtures were evaluated depending on various proportion of FA and BS. The results of the experiment, within the scope of the study, obtained the following conclusions. Flow of the mixtures was increased with addition of binary supplementary cementitious material(SCM), and especially, portion of FA. The air content of the mixtures was increased with addition of binary SCMs, while it was decreased with increased FA content. In the case of unit mass, increased value was obtained due to the increased air content within 25 to 45% of binary SCM content, while it was increased within 65 to 100% of binary SCM up to only 20% of FA content and decreased more than 20% of FA because of the low density of FA. The setting time of the mixtures was delayed with addition of binary SCM and FA. In the case of compressive strength, at 91-day age, the highest value was obtained with 25 and 45% of binary SCM with the proportion of FA to BS of 40 to 60. Therefore, based on the compressive strength, it is considered that the binary SCM content of 25 and 45% with the proportion of FA to BS of 2 : 3 is the most favorable conditions in this research scope.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.1 no.2
• /
• pp.93-100
• /
• 2013

A variety of researches on the concrete with high volume mineral admixture have increased in recent years. In fact, it is very important to find appropriate replacement ratio of concrete with high volume mineral admixture in order to apply in the field. In this study, compressive strength according to fly ash and blast furnace slag replacement ratio as well as curing temperature was measured in the conditions of obtaining the same workability in order to examine the characteristics of concrete with high volume mineral admixture. In conclusion, it was found that the compressive strength at the age of 3 days decreased by 1.4MPa and the compressive strength at the age of 28 days decreased by 3.8MPa when the fly ash replacement ratio increased by 10%. Also, it was found that the compressive strength at the age of 3 days decreased by 1.0MPa and the compressive strength at the age of 28 days decreased by 0.9MPa when the blast furnace slag replacement ratio increased by 10%. Through the tests, we obtained the basic data for developing the future research on the concrete with high volume mineral admixture for housing structure.

• Journal of the Architectural Institute of Korea Structure & Construction
• /
• v.35 no.12
• /
• pp.165-172
• /
• 2019

The aim of the research is to evaluate the influence of various replacing ratios of supplementary cementitious materials(SCMs) such as fly ash(FA), blast furnace slag(BS), and both FA and BS on general properties including segregation resistance as a powder based high fluidity concrete of normal strength grade with water-to-cement ratio 0.40. Specifically, by replacing the SCMs with low density powders, it was assessed that the decreased segregation resistance due to the decreased viscosity by J-ring test. As a result of the experiment, from the general test, the mixtures with SCMs showed increased segregation resistance by increased viscosity as the references, while some segregation was shown from J-ring test due to the decreased density of fresh state mixture related with the capacity of delivering coarse aggregate.

• Journal of the Korea Concrete Institute
• /
• v.24 no.5
• /
• pp.597-604
• /
• 2012

The present study assessed the $CO_2$ emissions of concrete according to the type and replacement ratio of supplementary cementitious materials (SCM) and concrete compressive strength using a comprehensive database including 2464 cement concrete specimens and 776 cement concrete mixes with different SCMs. The system studied in $CO_2$ assessment of concrete based on Korean lifecycle inventory was from cradle to pre-construction, which includes consistent materials, transportation and production phases. As the performance efficiency indicators, binder and $CO_2$ intensities were analyzed, and simple equations to evaluate the amount of $CO_2$ emission of concrete were then formulated as a function of concrete compressive strength and the replacement ratio of each SCM. Hence, the proposed equations are expected to be practical and useful as a guideline to determine the type and replacement ratio of SCM and unit content of binder in concrete mix design that can satisfy the target compressive strength and $CO_2$ reduction percentage relative to cement concrete.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.333-336
• /
• 2008

As the high-rise building increase due to the gravitation of population to big cities recently, it requires high quality and high performance of Concrete. As a result, people are keenly interested in Meta-kaolin as new admixture favorable from an economic perspective, which has strength and endurance with admixture at the same level like Silicafume. Accordingly, as to Meta-kaolin, this study was to set by three levels like domestic one, foreign one, and Silicafume, the waterbinding material ratio 25%, and four level substitute like 0, 10, 20, and 30(%) in order to compare and analyze the quality characteristics of high-strength concrete according to the substitute of Meta-kaolin applicable with replacement of Silicafume. As a result of performing experiment, as to the higher the additive amount of Superplasticizing agents in order to secure target liquidity was, the more the substitute in each admixture increased. This study had a tendency that the Silicafume increased the additive amount of Superplasticizing agents with high fineness compared with Meta-kaolin. In addition, the higher the substitute in each admixture was, the more its strength increased On the strength property, the higher the substitute in each admixture was, the more its strength increased. This study has found out that the Meta-kaolin has shown the better strength than the one of Silicafume. On the other hand, the relationship between the Compressive strength and Elastic coefficient has shown the similar formula suggested from ACI363.

• Journal of the Korea Institute of Building Construction
• /
• v.15 no.6
• /
• pp.597-605
• /
• 2015

The method of concrete mix design used in this study aims to achieve the identical specified design strength, applying different types and replacement ratio of mineral admixtures and afterwards, fire tests were conducted using the standard time-temperature curve specified in the ASTM E119 to identify the influences of the types of mineral admixtures on the fire resistance performance of high strength concrete(HSC). The least spalling was observed in the test specimen containing blast furnace slag as a partial replacement of cement, while the most significant spalling phenomena were observed in the blast furnace slag test specimen that silica-fume was added in. In particular, the reasonable volume of spalling was observed when solely replaced by silica fume. However, the influence of the cement replacement by silica fume and blast furnace slag on the increases of spalling can be explained through blocked pores by the fine particles of silica fume, leading to decreases in permeability.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.2 no.1
• /
• pp.26-33
• /
• 2014

The study investigates the effects of the type, replacement ratio and method of use of mineral admixtures on the fluidity, bleeding ratio, volumetric change and compressive strength of the grout in order to provide basic data for the development of high-quality grout for PSC bridges. In view of the results relative to the type and replacement ratio of the mineral admixtures, it appears that fly ash has practically no effect on the improvement of the fluidity nor on the reduction of bleeding and shrinkage of the grout. On the contrary, blast furnace slag and silica fume appear to have significant effect on the improvement of the fluidity or on the reduction of bleeding and shrinkage of the grout. With regard to the combined use of mineral admixtures, the combination of fly ash and blast furnace slag provides satisfactory fluidity but with significant increase of bleeding and shrinkage, whereas the combination of blast furnace slag and silica fume reduces bleeding and shrinkage but with large loss of the fluidity. On the other hand, the combination of fly ash and silica fume results in satisfactory fluidity accompanied with fair reduction of bleeding and shrinkage of the grout. In view of these results, the type, replacement ratio and method of use of the mineral admixtures are seen to influence the fluidity, bleeding and volumetric change of the grout. Accordingly, it is necessary to select the mineral admixtures considering these effects for their exploitation in the grout of PSC bridges.