• 한국해양공학회지
• /
• 제6권1호
• /
• pp.140-147
• /
• 1992

Corrsion fatigue test was performed under rotated bending in 3.5% NaCl aqueous solution having a temperature from 278.deg.K in order to investigate the effects of aqueous solution remperature on the corrosion fatigue fracture of raw material steel(SS41) and dual phase steel that was produced from SS41 by a series of heat treatment. Corrosion fatigue life decreases remarkably with increase in solution temperature or with decrease in stress level. The corrosion fatigue life and the crack propagation rate at 303.deg.K show the similar behaviors with those at 318.deg.K, which is assumed to be caused by concentration polarization phenamena. The number and the lengths of microcracks increase with increase in solution temperature, so they lead to the decrease in corrosion fatigue life.

• 콘크리트학회지
• /
• 제6권2호
• /
• pp.129-137
• /
• 1994

해양환경하에 있는 콘크리트 구조물의 열화를 알아보고 철근의 부식 정도를 추정하기 위한 연구내용으로서 콘크리트 중에 철근을 묻은 공시체를 제작하여 간만의 차가 있는 해변에 1년 동안 노출시킨 상태로 시험을 실시 하여 콘크리트 중의 가용성 염분량, 철근의 자연전위값 및 철근의 부식정도에 대하여 고찰하였다. 본 연구 결과 콘크리트 중의 가용성 염분량은 물-시멘트비가 낮을수록, 혼화재를 혼입할 경우 적게 나타났으며 가용성 염분량이 클수록 철근의 부식이 크게 나타났다. 철근 부식의 정도가 심할수록 자연전위값이 감소하였으며 자연전위와 부식면적율과는 상관관계가 있음을 알 수 있었다.

• 한국해양공학회지
• /
• 제19권2호
• /
• pp.53-59
• /
• 2005

The effect of pH on the corrosion characteristics in the dissimilar friction welded zone of IN713LC-SCM440 in the loaded torsional stress was studied. The corrosion experiment was performed for 120 hours on the specimens with five steps of pH. The surface corrosion pattern of the SCM440 area showed global corrosion and narrow pitting, which was caused by galvanic corrosion between friction welded IN713LC and SCM440, but corrosion did not proceeded from the IN713LC area. The average relative electrode potential gradually tends to decrease with the elapse of the immersion time in the acidity area. The average corrosion current also gradually tend to decrease The corrosion rate showed a larger value when the average relative electrode potential was higher and the average relative current was lower. The corrosion rate showed a larger value when the average relative electrode potential was higher in the acidity area, and it showed large when the average relative electrode potential was lower in the alkalinity area.

• 한국해양공학회지
• /
• 제18권5호
• /
• pp.50-56
• /
• 2004

This study is on the constant-current stress corrosion test, related to the load stress, in both the welded and non-welded zones of high tensile strength steel that is used for natural gas transmission. The surface corrosion pattern of the welded zone of API 5L-X65 specimens for natural gas transmission showed general corrosion and narrow pitting, and the pitting was increased with load stress. Initially, the average relative electrode potential and the average relative current of the high tensile strength steel, used for natural gas transmission specimens, were decreased rapidly, and the average relative electrode potential was higher and the average relative current was lower in welded zone, compared to base metal. The average relative electrode potential was decreased with load stress, and the average relative current was somewhat increased by increasing the load stress. The corrosion rate was less in welded zone, compared to base metal, and the corrosion rate was decreased by increasing the load stress.

• 한국어업기술학회:학술대회논문집
• /
• 한국어업기술학회 1997년도 수산관련공동학술대회발표요지집
• /
• pp.108.2-109
• /
• 1997

• 한국어업기술학회:학술대회논문집
• /
• 한국어업기술학회 1997년도 수산관련공동학술대회발표요지집
• /
• pp.106.2-107
• /
• 1997

• 문화기술의 융합
• /
• 제10권1호
• /
• pp.363-368
• /
• 2024

선박, 해양구조물 또는 해상풍력 발전설비 하부구조와 같이 해양환경에서 사용되는 강구조물은 부식이 쉽게 발생한다. 본 연구에서는 실험을 통하여 희생전극으로 많이 사용되는 아연전극의 방식전위와 동등한 -1050mV vs. SCE에서 환경하중에 기인하는 부식피로균열 진전특성에 대하여 고찰하였다. 이를 위하여 본 연구에서는 -1050mV vs. SCE의 음극방식이 해수환경중의 피로균열 진전에 미치는 영향에 대해 합성해수중에서 파랑주기를 고려하여 실험적 고찰을 실시하였다. 음극방식에 의한 방식법은 부식을 차단하지만 과도한 방식은 화학반응에 의하여 수소를 발생시키며, 또한 석회질퇴적물을 발생시킨다. 피로균열진전율은 실험초기에는 해수부식환경하에서의 진전율보다 빠른구간이 나타났다. 그리고 균열길이가 증가하여 응력확대계수 K가 커질수록 균열의 진전율은 해수중의 피로균열진전율보다 느려지는 현상이 나타났다. 그러나 대기중의 균열진전속도보다는 항상 빠른 진전속도를 나타내었다.

• 한국어업기술학회:학술대회논문집
• /
• 한국어업기술학회 2001년도 추계 수산관련학회 공동학술대회발표요지집
• /
• pp.77-78
• /
• 2001

선박건조 기술의 지속적인 발전에도 불구하고 선박운항 중에 반복적으로 발생 하는 문제점중의 하나가 열교환기의 파손에 따른 문제점이다. 이러한 열교환기의 파손문제는 일반적인 기계류의 파손과는 달리 경우에 따라서는 주기관인 main engine을 정지시켜야 되는 등 선박운항에 미치는 영향이 매우 크다. 열교환기에 있어서 선박운항 중에 주로 발생되는 부식사례로는 원통부위의 각종 gauge의 thread부분의 간극부식과 침식-부식에 의한 세관의 파손 등이 있다. 이러한 세관의 파손은 각종 oil의 유출 및 sea water 혼입 등의 문제를 일으킨다. (중략)

• 한국구조물진단유지관리공학회 논문집
• /
• 제26권6호
• /
• pp.1-13
• /
• 2022

이 연구에서는 콘크리트 표면에서 측정된 반전지전위(half-cell potential, HCP)값을 활용하여 철근 부식 상태 및 부식속도의 정량적 평가 가능성을 논의하였다. 이 연구에서는 염수에 침지된 콘크리트 속 철근에 전류를 인가하여 다양한 부식상태의 철근 콘크리트 실험체(한 변의 길이가 200mm 인 정육면체)를 준비하였다. 부식촉진시험을 마치고, 염수 포화상태의 콘크리트 실험체 표면에서 HCP값을 측정하였고, 바로 이어서 동일한 조건의 실험체에서 전기화학적 임피던스 분광법을 활용하여 콘크리트 속 철근의 분극저항값을 측정하였다. 측정된 분극저항값을 Stern-Geary식에 대입하여 부식전류밀도(corrosion current density, i_corr)를 계산하였다. 실험결과를 바탕으로 염해에 따라 다양한 부식상태의 철근이 매입된 철근 콘크리트 실험체의 염수 포화상태에서 HCP와 i_corr의 상관관계를 도출하였다. 대체적으로 HCP와 i_corr은 로그선형관계를 보였으며, R2값이 0.87이상의 높은 적합도를 확인하여 통계적인 유의함을 확인하였다. 이러한 결과는 일정한 환경에 노출된 철근 콘크리트일 경우 자연전위값을 측정함으로서 철근의 부식상태 및 속도를 평가할 수 있음을 실험적으로 확인하였다.

• 수산해양기술연구
• /
• 제37권1호
• /
• pp.65-70
• /
• 2001

바다모래에 의해 뒷채움된 지하연료저장탱크용 연강재의 부식전류밀도, 개로전위, 전식거동 및 연간부식률에 관하여 연구한 결과 다음과 같은 결론을 얻었다. 1) 습바다모래 중에서 비저항이 감소할수록 개로전위는 비전위화되고, 부식전류밀도는 높게 배류된다. 2) 습바다모래의 비저항이 감소할수록 인가전위 부가에 의한 부식전류밀도는 자연전위에서의 부식전류밀도보다 급격히 증가한다. 3) 습바다모래 중에서 비저항이 감소할수록 연간부식률은 선형적으로 증가함으로 지하연료저장탱크에 바다모래로 뒷채움하는 경우 습기가 유입하면 지하연료저장탱크의 부식성은 민감할 것으로 판단된다.