• 한국해양공학회지
• /
• 제27권3호
• /
• pp.79-84
• /
• 2013

The seawater pipes in the engine rooms of ships are surrounded by severely corrosive environments caused by fast flowing seawater containing chloride ions, high conductivity, etc. Therefore, it has been reported that seawater leakage often occurs at a seawater pipe because of local corrosion. In addition, the leakage area is usually welded using shielded metal arc welding with various electrodes. In this study, when seawater pipes were welded with four types of electrodes(E4311, E4301, E4313, and E4316), the difference between the corrosion resistance values in their welding zones was investigated using an electrochemical method. Although the corrosion potential of a weld metal zone welded with the E4316 electrode showed the lowest value compared to the other electrodes, its corrosion resistance exhibited the best value compared to the other electrodes. In addition, a heat affected zone welded with the E4316 electrode also appeared to have the best corrosion resistance among the electrodes. Furthermore, the corrosion resistance of the weld metal zone and heat affected zone exhibited relatively better properties than that of the base metal zone in all of the cases welded with the four types of electrodes. Furthermore, the hardness values of all the weld metal zones were higher than the base metal zone.

• 수산해양기술연구
• /
• 제23권2호
• /
• pp.61-65
• /
• 1987

선박용 강판(KR Grad A-3)과 라임티타니아계 피복 아아크 용접봉(E4303)을 이용하여 대기중용접 및 습식 수중 용접하여 TRC 임계응력치, 열 사이클, 경도분포, 확산성 수소량, micro조직 등을 실험적으로 조사한 결과를 요약하면 다음과 같다. 1. TRC 시험에 의한 초기 임계응력치 $\sigma$ 하(cr) 은 대기중 용접 및 수중용접의 어느 쪽에서도 Y groove 형상의 경우가 각각 71kg/mm 상(2), 51kg/mm 상(2) 로서 가장 높고, 반대로 45$^{\circ}$r 형 groove의 경우가 각각 52kg/mm 상(2), 41kg/mm 상(2)로서 최저이며, 수중용접부의 냉파괴 감수성이 대기중용접보다 높다. 2. 용접부의 경도는 조립 열영향부에서 가장 높고 대기중용접에서 약 H 하(k) 365, 수중용접에서는 급격한 냉각속도 때문에 약 H 상(k) 670으로 높게 되어 후자의 경우 파괴 감수성의 증가에 의한 낮은 임계응력치를 갖게 된다. 3. 48시간 동안의 확산성 수소량은 대기중용접에서 약 18cc/100g-weld-metal, 수중용접의 경우 약 48cc/100g-weld-metal로서 수중용접의 경우가 약 3배 정도 더 침입하고 있으므로 이의 방지책이 필요하다.

• 수산해양기술연구
• /
• 제23권2호
• /
• pp.15-15
• /
• 1987

선박용 강판(KR Grad A-3)과 라임티타니아계 피복 아아크 용접봉(E4303)을 이용하여 대기중용접 및 습식 수중 용접하여 TRC 임계응력치, 열 사이클, 경도분포, 확산성 수소량, micro조직 등을 실험적으로 조사한 결과를 요약하면 다음과 같다. 1. TRC 시험에 의한 초기 임계응력치 σ 하(cr) 은 대기중 용접 및 수중용접의 어느 쪽에서도 Y groove 형상의 경우가 각각 71kg/mm 상(2), 51kg/mm 상(2) 로서 가장 높고, 반대로 45°r 형 groove의 경우가 각각 52kg/mm 상(2), 41kg/mm 상(2)로서 최저이며, 수중용접부의 냉파괴 감수성이 대기중용접보다 높다. 2. 용접부의 경도는 조립 열영향부에서 가장 높고 대기중용접에서 약 H 하(k) 365, 수중용접에서는 급격한 냉각속도 때문에 약 H 상(k) 670으로 높게 되어 후자의 경우 파괴 감수성의 증가에 의한 낮은 임계응력치를 갖게 된다. 3. 48시간 동안의 확산성 수소량은 대기중용접에서 약 18cc/100g-weld-metal, 수중용접의 경우 약 48cc/100g-weld-metal로서 수중용접의 경우가 약 3배 정도 더 침입하고 있으므로 이의 방지책이 필요하다.

• Journal of Welding and Joining
• /
• 제2권1호
• /
• pp.30-40
• /
• 1984

Moisture content in the coating of an electrode is known to cause defects such as porosities, fish eyes and cracks in the weld metal, however, quantitative relationship between them is not clearly understood. In this study widely consumed and the most common type of arc welding rods such as ilmenite and low hydrogen type were chosen for the investigation, and attempts were made to correlate the relationship between the mechanical properties and gas contents when welding was carried out with electrodes of various moisture contents. As the relative humidity changed from 70% to 92%, it was determined that moisture content to reach saturation was in the range of 0.6~6.8%. As the moisture content in the electrode coating was increased, the amount of gaseous components (H, O, N) in the weld metal was accordingly increased, especially diffusible hydrogen showed prominent effect, i.e. it increased proportionally to the increase of the moisture content. The mechanical properties of the weld metal was observed to become more inferior as the diffusible hydrogen was greater. It was determined for ilmenite type of electrode that the increase of hydrogen content was approximately 1.8ml per unit weight percent increase of moisture and also tensile strength resulted lowering from $45.3kg/\textrm{mm}^2$ to $42.7kg/\textrm{mm}^2$ as moisture content increased from 0.7% to 6.8%. For low hydrogen type the increase of the hyrogen was about 2.4ml per unit percent of moisture and tensile strength decreased from $63.0kg/\textrm{mm}^2$ to $53.8kg/\textrm{mm}^2$ particularly in the region of moisture content 0.1~4.2%.