• 보존과학연구
• /
• s.32
• /
• pp.89-98
• /
• 2011

It is quite difficult to identify its corrosion compound because they have a wide variety of crystal structures and they are mixed with two component. This study was conducted with the standard iron corrosion compounds through the analysis by Raman Micro-Spectroscopy, which aims to obtain standard Raman Data. To assess the reliability of standard iron corrosion compounds, SEM-EDS analysis and XRD analysis were conducted. Through SEM-EDS analysis, the elements of corrosion compound matched with those of standards iron corrosion compounds except Goethite. XRD analysis showed that the structures of corrosion compounds were identical to those of standard iron corrosion compounds, however, it was identified that Iron sulfate ($FeSO_4{\cdot}6H_2O$) is the Rozenite ($FeSO_4{\cdot}4H_2O$). Through Raman Micro-Spectroscopy analysis, the new peak was detected from the wavenumbers of hydroxide and iron oxide. It is considered that it is due to changes in the wavelength of the laser. As the wavenumbers of iron chloride and iron sulfate have been identified, eight kinds of Raman Data were obtained. It can be considered to contribute to cultral heritage for iron objects that Raman Micro-Spectroscopy analysis which is relatively easy to compare material properties and structures can be highly applicable to the research on cultural heritage with the limited amount of samples.

• Journal of Conservation Science
• /
• v.29 no.3
• /
• pp.287-296
• /
• 2013

Excavated iron objects are preserved in stable condition through processes of conservation treatment because they are found in the form of various corrosion products. However, the conservation treatment leads to re-corrosion over time and accordingly, iron objects can be severely damaged, and therefore fundamental measures need to be prepared to control it. In this study, the types and characteristics of corrosion products were scientifically analyzed according to the re-corrosion of iron artifacts. In addition, the stability of the corrosion products was evaluated by exposing the standard samples under the re-corrosion environment. Re-corrosion proceeded with weeping in reddish brown on the cracks of iron artifacts. Weeping was detected akagan$\acute{e}$ite had a low hydrogen ion concentration and high chloride ion. The selection of standard sample goethite, lepidocrocite, hematite, and magnetite, were evaluated corrosive by weeping. After the samples were immersed in HCl(pH 1), $H_2SO_4$(pH 1), $H_2O$(pH 6) solution, they had been maintained for 180 days in relative humidity of 20%, 50%, 80% to investiage the changes of chemical components. As a result of analysis, the changes of chemical components were not showed in goethite, lepidocrocite, and hematite. But magnetite was changed to lepidocrocite in solution including chloride ion($Cl^-$) and to goethite and lepidocrocite solution including sulfuric acid($SO{_4}^{2-}$). Results of the study, in the case of magnetite known as s stable corrosion compound, it was identified the corrosion of magnetite occurs by corrosive ions, which means weeping generated in the iron artifacts can corrode magnetite as well as base metal.