• Journal of the korean academy of Pediatric Dentistry
• /
• v.28 no.2
• /
• pp.199-206
• /
• 2001

The purpose of study was to compare the plasma arc light with the halogen light in compostie resin curing. Three composite resin materials(Z-100, 3M, USA; Tetric Ceram, Vivadent, Liechtenstein; SureFil, Dentsply, USA) were filled in the teflon molds (4mm in diameter and 2, 3, 4, 5mm in thickness) and cured with either the conventional low-intensity light curing unit with a halogen lamp (Optilux 360, Demetron, U.S.A.) for duration of 40 seconds or with the high-intensity light curing unit with a plasma arc lamp (Flipo, Lokki, France) for duration of 3, 6, and 9 seconds. The intensity of halogen light was about $370mW/cm^2$ and that of plasma light was about $1,900mW/cm^2$. After one week, the surface hardnesses of both the top and the bottom of the resin samples were measured with a microhardness tester(MXT70, Matsuzawa, Japan). There were significant differences in the hardness between the top and the bottom of the resin samples except the 2mm thickness samples cured by halogen light for 40s or by plasma light for 9s. There was no significant difference between the hardness values of the top surfaces of the thickness groups. The hardness values of the bottom surfaces decreased as the curing time decreased and as the thickness of resin samples increased, and the three kinds of resin composites showed similar patterns. The results suggest that the halogen light for 40 seconds might be able to cure greater depth of resin composites than the plasma light for 3, 6, or 9 seconds.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2011.05a
• /
• pp.79-79
• /
• 2011

water cavitation peening(WCP)은 water jet 과정으로 인한 cavitation이 발생할 때, 금속표면 cavitation 현상에 의해 재료표면의 잔류응력과 경도 등의 물성을 변화시키게 되며, 그로 인해 생긴 잔류 응력으로 재료의 내구성 및 수명을 향상시키는 기술이다. 최근에는 water jet을 이용한 장치들이 건설 분야, 일반기계분야, 컷팅 공정, 분쇄 등 다양한 분야에서도 사용되고있다. 그러나 water jet을 이용한 peening은 소개 된지 20여년이 경과했음에도 불구하고 연구 및 개발 내용은 shot peening에 비해 아직 초기 단계이다. water cavitation peening은 기존의 피닝 방법의 단점을 보완 할 뿐만 아니라 환경적인 측면에서도 그 가치가 크다. 아직은 다른 peening 기법 보다 잔류압축응력 부가 측면에서 그 효과가 떨어지지만, water cavitation peening은 열에 영향을 받는 영역이 생성되지 않으며, 기계의 표면 가공을 하는 동안 어떤 미세한 먼지도 생성하지 않아 친환경적이다. 또한 복잡한 외형을 가지는 부품 및 내면에 적용성이 뛰어나고, 표면 정밀도 저하가 낮다는 장점이 있다. 본 연구에서는 조류발전용 블레이드의 재료로 사용하려는 동합금에 대하여 증류수 내에서 water cavitation peening 시간, 거리, 파형 등의 변수를 적용하여 최적 조건을 찾고, 다양한 전기화학적 실험을 실시하였으며, water cavitation peening 부의 부식특성을 평가 하였다. ASTM-G32 규정에 의거하여 압전효과를 용한 진동발생 장치(RB 111-CE)를 이용하여 동합금 표면에 water cavitation peening을 실시하고, 실험 후 표면의 손상거동을 관찰하기 위하여 3D현미경 및 전자주사현미경(SEM)을 사용하였다. 물성치 변화를 확인하기 위하여 SHIMADZU사의 HVM-2 Model의 비커스 경도기를 이용하여 표면 경도값을 측정하였다. 전기화학실험은 각 3회 이상 실시하였으며, Tafel 분석결과로 부식전류밀도와 부식전위의 평균, 부식전위를 알 수 있었고, 음분극 실험결과, 용존산소 환원반응에 의한 농도분극에서 수소가스발생에 의한 활성화 분극으로 진행되는 변곡점을 확일 할 수 있었다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.38-38
• /
• 2018

TiMoN 코팅층은 우수한 내마모 특성과 낮은 마찰계수를 보여 많은 연구가 진행되고 있다. 본 연구에서는 음극아크 증착으로 질소 가스 유량, 아크 전류, 기판 전압 등 공정 변수를 제어하여 TiMoN 코팅층을 스테인리스와 초경 기판 위에 제조하고 색상, 미세구조, 경도 등 물리적 특성을 평가하였다. TiMo 타겟은 Mo가 약 8 at.% 함유되어 있으며 직경은 80 mm이었다. 색차계를 이용하여 TiMoN 코팅층의 색상을 분석한 결과, 질소 유량이 증가할수록 $a^*$와 $b^*$ 값이 증가하는 경향을 확인하였다. 질소 유량 90 sccm으로 제조한 TiMoN 코팅층은 TiN 코팅층과 유사한 색상을 보였다. TiMoN 코팅층의 조성을 에너지분산형 분광기(energy dispersive spectroscopy)로 분석한 결과, 타겟과 유사한 조성을 보였다. TiMoN 코팅층의 단면을 주사전자현미경으로 관찰한 결과, 주상정 형성이 확인되었으며 코팅층 표면에는 음극 아크 공정 시 발생하는 거대입자가 발견되었다. 질소 유량 50 sccm으로 제조한 TiMoN 코팅층은 약 3000 Hv의 경도 값을 보였다. X-선 분광기로 TiMoN 코팅층의 결정성을 분석한 결과, TiN과 유사한 합금상이 형성된 것을 확인할 수 있었다. TiMoN 코팅층은 TiN과 유사한 색상을 보였으며 경도는 TiN보다 높은 값을 보여 절삭공구, 금속 가공용 부품 등 고경도 코팅층으로 활용이 가능할 것으로 판단된다.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.7 no.5
• /
• pp.805-810
• /
• 2006

Defects in the conventional casting process of silver jewelry can result in famished products of mediocre hardness. To overcome the shortcomings of conventional methods, we proposed new press forming process, which involves applying uniaxial pressure on casting 92.5%Ag-6.5%Cu-1%Zn ring elements and shaping with a lath. We investigated Vickers hardness, density, and microstructure evolution by changing the applied uniaxial pressure. We report that our newly proposed process can increase the hardness up to 2.3 times and decrease average grain size by 50%. Our method leads to drastic mechanical property enhancements, and is thus suitable for casting tension-style jewelry.

• Analytical Science and Technology
• /
• v.7 no.4
• /
• pp.527-540
• /
• 1994

The surface microstructure modification by $N^+ion$ implantation into 7050A1 alloy was investigated. Ion implantation method is to implant physically accelerated ions to the surface of a substrate. High doses of nitrogen($5{\times}10^{15}ions/cm^2$, $5{\times}10^{17}ions/cm^2$, $8{\times}10^{17}ions/cm^2$) were implanted into 7050A1 alloy using accelerating voltage of 100KeV and current density of $23.1{\mu}A/cm^2$. The implanted layers were characterized by EPMA, AES, XRD, and TEM. The experimental results were compared with computer simulation data. The results showed that AlN was formed from the surface to $4000{\AA}$ depth with Gaussian distribution and the damage region was also observed. This surface modification by $N^+ion$ implantation increased the microhardness of 7050A1 alloy surface.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2009.05a
• /
• pp.211-211
• /
• 2009

높은 이온화율과 복잡한 형상의 모재에도 표면 도포성 및 균일성을 나타내는 아크이온플래이팅 기술과 비전도성 세라믹 타겟물질에 적용가능한 스퍼터링 기술이 결합된 하이브리드 코팅 시스템(Hybrid coating system)을 이용하였다. 그리고 Cr-Al-N과 Cr-Si-N 코팅막의 강화 기구를 복합시킨 새로운 개념의 Cr-Al-Si-N 코팅막을 초경(WC-Co)시험편에 증착하여 Si 첨가량에 따른 미세구조의 미세경도 특성을 파악하였다. 공구성능 평가는 고속가공조건하에 마이크로 밀링기에서 무코팅(초경공구), Cr-Al-Si-N (Si : 0, 4.5, 8.7, 16 at.%) 코팅 마이크로엔드밀에 대하여 공구마멸에 대한 공구수명을 비교, 평가하였다.

• Journal of the Korean institute of surface engineering
• /
• v.29 no.1
• /
• pp.15-25
• /
• 1996

자동차엔진의 피스톤-링에 응용할 목적으로 플라즈마 용사 기술로 피막한 몰리부덴늄 및 코발트 합금 피막 층의 마모성질을 비교 조사하였다. Ball-on-disc 형태의 마모기를 사용하여 상온 및 대기 중에서의 마모 및 마찰거동에 대하여 조사하였다. 용사 층의 미세경도 시험도 행하였으며, 용사층의 결정구조를 알기 위해 용사층을 x-선 회절 방법으로 분석하였다. 주사전자현미경을 사용하여 마모면의 표면 형상을 관찰하였다. 여러 용사조건으로 만든 용사층의 미세경도치와 마모거동과의 상관관계를 이해하려고 시도하였다. 주사전자현미경과 EDX를 사용하여 마모시 화학반응층과 마모기구를 규명하고자 하였다. 모리부덴늄 및 코발트 합금 분말을 각각 플라즈마 용사층의 단면을 관찰하여 마모기구을 비교하였다.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.32 no.1
• /
• pp.7-12
• /
• 2005

The objective of this study was to evaluate the effects of nanofiller content on the microhardness and polymerization of experimental microhybrid composites. The nanofiller contorts in the experimental composites were varied (0%, 1%, 2%, 3%), while the total filler content remained constant as 76%wt. We obtained the following results: 1. The microhardness of the top surface for the 2% 3% nanofilled microhybrid composites were significantly higher than those for the 0%, 1% nanofilled composites (p<0.05), but the difference was not great. 2. The microhardness of the bottom surfaces significantly increased with an increase in the nanofiller level (p<0.05), except between the 2% and 3% nanofilled groups (P>0.05). 3. As the nanofiller level increased, the difference between microhardness of top and bottom surfaces significantly decreased (p<0.05), except between 2% and 3% nanofilled groups (p>0.05).

• Journal of Conservation Science
• /
• v.26 no.3
• /
• pp.269-276
• /
• 2010

This study aims to extract manufacturing techniques by analysing metallurgical characteristics of the cast-iron pot from Bubjusa, examining corrosion status and microstructure with a optical microscope, SEM-EDS, micro vickers hardness tester and XRD. The microstructure analysis has presented that ferrite and partial portion of pearlite exist within the corroded outer layer. The analysis of the inner layer revealed that there is pearlite and graphite of feather shape. The one of the middle layer, which is placed between outer and inner layer, showed that corrosion has been heavily developed. Micro vickers hardness values range from 217Hv to 698Hv in constituent layers and such values lie within the ranges of the ancient iron relics. The result of EDS analysis for each microstructure presented that the outer layer has been more decarbonized than the inner layer. XRD analysis of iron corrosion compound revealed that Goethite and Hematite had been produced from the corrosive process of iron. The study concludes that the large iron pot was made by casting technique, and microstructure of inner layer had a gray cast iron. Outer layer has been decarbonized through repetitive process of heating and cooling. This results can be used as fundamental data for comparative study to reveal manufacturing techniques of large cast-iron pot.

• Proceedings of the KAIS Fall Conference
• /
• 2005.05a
• /
• pp.58-60
• /
• 2005

기존의 금속조형물은 만드는 공정으로 주조-후처리 또는 정밀 기계가공방법은 많은 시간과 노력이 필요한 단점이 있었다. 최근에 귀금속 성형점토 (PMC)라는 마이크로 크기의 분말과 바인더가 혼합되어 마치 점토와 같이 직접 수공 또는 치공구를 이용하여 완성하고 $650-850^{\circ}C$ 정도의 저온에서 소결하여 단시간 안에 최종 조형물을 만들 수 있는 신공정이 개발된 바 있다. 본 연구에서는 선진사와 비슷한 $1{\~}3{\mu}$m급은 분말을 1:1로 혼합하고 고형 바인더를 첨부하여 기존 선진사와 동등하거나 우수한 미세조직과 표면경도를 확보하고 조형비가 있는 시작품을 만드는데 성공하였다.