• Journal of the Korea Institute of Building Construction
• /
• v.18 no.6
• /
• pp.551-558
• /
• 2018

This study evaluate the fluidity and hardening properties of mortar by replacement ratio of ferronickel slag powder to estimate the applicability of ferronickel slag powder for cement replacement materials. Ferronickel slag powder was replaced by 0, 5, 10, 15 and 20% of the cement weight. In addition, blast furnace slag powder and fly ash were also used for comparing with the mixtures using ferronickel slag powder. As the test results, the micro-hydration heat of the mixture containing the ferronickel slag powder was lower than that of the mixtures containing the same amount of blast furnace slag powder and fly ash. The flow of the sample with ferronickel slag powder was relatively higher than the other mixtures. In all ages, the compressive strength of the mixture with ferronickel slag powder and fly ash was similar to that of the mix containing only fly ash. In case of drying shrinkage, the mixture containing ferronickel slag powder exhibited lower drying shrinkage than the mixture using blast furnace slag powder, and similar to the mixture containing fly ash.

• Journal of the Korea Institute of Building Construction
• /
• v.23 no.4
• /
• pp.359-367
• /
• 2023

This experimental study investigates the replacement of conventional Portland cement and sand with non-sintered cement and ferro-nickel slag to formulate eco-friendly cement mortar. The examination aimed to understand the strength properties of non-sintered cement mortar using ferro-nickel slag as fine aggregate by classifying mortar production types, fine aggregates, and curing methodologies. From flexural and compressive strength tests, it was observed that non-sintered cement mortars, incorporating ferro-nickel slag as fine aggregate, exhibited superior strength when compared to both plain mortar and steam-cured non-sintered mortar. This increased strength is attributed to the influence of the particle size, density, and absorption capabilities of the ferro-nickel slag. Furthermore, X-ray Diffraction(XRD) analyses of the mortars verified the presence of MgO, a component of ferro-nickel slag, in the form of a composite oxide. This finding substantiates the consistent strength manifestation of non-sintered cement mortars utilizing ferro-nickel slag as a fine aggregate.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.1
• /
• pp.120-127
• /
• 2011

Recently, there are problems due to the exhaustion of natural aggregate resources, and strict restrictions. In this study, the possibility of using Water Granulated Ferro-Nickel slag as a substitutive material of fine aggregate is determined from the properties of mechanical and durability for the concrete that is made with Water Granulated Ferro-Nickel slag. According to the test results, when the mixing rate of Water Granulated Ferro-Nickel Slag aggregates concrete is adjusted, up to 50% of its aggregates by mixing rate can be mixed with general aggregates. The optimum mix ratio is considered to be 40%. The freezing and thawing resistance of Water Granulated Ferro-Nickel Slag aggregates concrete is identical to that of general aggregates concrete, while the carbonation resistance is found to be same as or lower than that of general aggregates concretes.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.8 no.1
• /
• pp.39-48
• /
• 2020

The present study investigates the chemical reaction and performance of ternary blended binders by mixing ferronickel slag. Cement was replaced using ground granulated blast furnace slag and ferronickel slag, combined up to 50% of the replacement rate. The blended cements were tested by setting times, length change, compressive strength at 1, 3, 7, 28 days. X-ray diffraction and scanning electron microscope were conducted for detecting hydration products while the MIP and microhydation heat were used for examining morphological characteristics. The results showed that by adding ferronickel slag, Pozzolanic reaction occurred, forming a dense pore structure and the effect of reducing hydration heat and dry shrinkage was also found. The compressive strength at 28 days was lower than that of 100% OPC control specimen (OSP0), but ternary blended cements showed no significant difference compared to binary blended (OSP50). If the optimal mix is derived later and used for the purpose, the potential for use as a cement binder is expected.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.4
• /
• pp.319-323
• /
• 2018

Ferronickel slag is a by-product from the ferronickel smelting process and it is divided into air-cooled ferronickel slag and water granulated ferronickel slag according to cooling system. The purpose of this experimental resesrch is to investigate the mechanical properties and resistance to freezing and thawing of concrete using air-cooled ferronickel slag(ACFNS) fine aggregate. For this purpose, the concrete specimens with water-cement ratio of 50% were made with ACFNS's replacement ratios of 0%, 20%, 30%, 40%, 50%, 70%, and 100% by volume of fine aggregate. It was observed from the test results that the compressive strength and static modulus of elasticity of ACFNS fine aggregate concrete were increased with increasing replacement ratio of ACFNS and the resistance to freezing and thawing of this was similar to reference concrete which had the relative dynamic modulus of elasticity of more than 90% during the freezing and thawing of 300 cycles.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.7 no.3
• /
• pp.262-270
• /
• 2019

Ferronickel slag, which is an industrial byproduct, is activated by mechanochemical reaction as a nonferrous metal and can be used as an admixture. Therefore, ferronickel slag is used as a substitute resource of admixture. In this study, to evaluate the effect of mixed of ferronickel slag powder and admixture, a mortar using a mixture of ferronickel slag powder, quicklime, gypsum and calcium chloride was fabricated by vibrated and rolled manufacturing method. Strength were evaluated by flexural and compressive strength tests, and durability was evaluated by performing chlorine ion penetration resistance and chemical resistance test. When the substitution ratio of ferronickel slag powder is constant, it is considered that the mixed use of quicklime, gypsum and calcium chloride as admixtures increases the performance.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.10 no.1
• /
• pp.9-14
• /
• 2022

Most of the existing research on ferronickel slag has focused on its potential as aggregate and fine aggregate, this study was conducted focusing on the potential of ferronickel slag powder as a concrete admixture. For concrete, which fly ash, blast furnace slag, and FSP were mixed with each 10 % type the reactivity was evaluated by applying ASTM C 1260 of the United States. As a result, compared with the control group, the expansion rate of fly ash decreased by 8.43 % and that of fine blast furnace slag powder decreased by 14.46 %, while the expansion rate of ferronickel slag decreased by 49.40 %. it was confirmed that ferronickel slag can sufficiently be replaced existing supplementary cementitious admixtures such as fly ash and blast furnace slag in terms of suppressing the reactivity of aggregates. However as a result of SEM analysis, ettringites were generated, and additional research about how it affects concrete is needed.

• Resources Recycling
• /
• v.22 no.1
• /
• pp.42-47
• /
• 2013

Ferro-Nickel slag is a byproduct of Ferro-Nickel manufacturing process. Ferro-Nickel slag mostly discarded or used as aggregates despite having useful ingredients such as magnesium oxide and silicon oxide. This study tried to extract process for Mg ion using $H_2SO_4$ solution. And remove impurities and get high purity $Mg(OH)_2$ using NaOH. Mg ion was extracted with the Fe ion and other Ferro-Nickel slag composition by $H_2SO_4$ solution. It is important to control the pH because remove impurities and obtain high-purity $Mg(OH)_2$. The impurities were removed by precipitation of the hydroxides. After this process, we added NaOH and high-purity $Mg(OH)_2$ was obtained.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.8 no.2
• /
• pp.190-197
• /
• 2020

This paper evaluates the mechanical properties and durability of cement matrix blended with mineral admixtures and ferronickel slag(FNS) powder which is an industrial b y-product during ferronickel smelting process. The hydration heat, pore structure, compressive strength, length change, rapid chloride penetration test(RCPT), and freezing and thawing resistance of ternary blended cement matrix were investigated and compared with ordinary portland cement matrix. The result showed that the compressive strength of ternary blended cement matrix using ferronickel slag powder and mineral mixture was low in strength compared to the reference concrete, but recovered to a certain extent by using alkali activator. Length change of cement mortar using FNS powder have shown less shrinkage occurs than the reference specimen. In addition, irrespective of using the alkali-activators, all ternary mix are indicative of the 'very low' range for chloride ion penetrability according to the ASTM C 1202, and the freeze-thaw resistance also showed excellent results.

• Journal of the Korea Institute of Building Construction
• /
• v.22 no.6
• /
• pp.641-649
• /
• 2022

This study aims to completely develop a non sintered cement mortar using industrial by-products. To replace Portland cement, blast furnace slag, circulating fluidized bed fly ash, and pulverized coal fly ash were used, and natural aggregates were substituted with ferronickel slag. To understand the characteristics of the non sintered cement mortar to which ferronickel slag is applied, an experiment was conducted by classifying the particle size. Fluidity and workability were confirmed through the flow test, and bending and compressive strength tests were conducted at 3, 7, and 28 days of age. In addition, durability was identified through a chloride ion penetration test. Through the study, it is judged that the binder, which completely replaced cement and aggregate, has high potential of being used as a construction material. Notably, it was confirmed to be advantageous for strength and durability.