• Journal of Korea Foundry Society
• /
• v.41 no.5
• /
• pp.411-418
• /
• 2021

In order to experimentally investigate the effect of Ni or Cu addition on microstructure and mechanical properties of high Si Solution Strengthened Ferritic Ductile cast Iron (SSF DI), a series of lab-scale sand casting experiment were conducted by changing initial concentration of Ni up to 3.0wt% or Cu up to 0.9wt% in the alloy. It was found that increase in Ni or Cu content in the alloy leads to increase in strength properties and hardness as well as decrease in ductility. The higher Ni or Cu content the SSF DI has, the higher fraction of pearlite was observed. At similar levels of Ni or Cu contents in the alloy, higher pearlite area fraction was observed in the Cu-containing SSF DI than that in the Ni-containing SSF DI. When the effect of the microstructure on the mechanical properties of Ni-containing SSF DI was considered, Ni-containing SSF DI was found to have excellent strength and hardness as well as good elongation when the pearlite fraction was controlled less than 10%. As the pearlite fraction in the Ni-containing SSF DI exceeds 10%, however, it shows drastic decrease in elongation. Meanwhile, gradual increase in strength and hardness, and decrease in elongation with respect to increase in pearlite fraction were observed in Cu-containing SSF DI. The different microstructure-mechanical property relationships between Ni-containing and Cu-containing SSF DI were due to the combined effect of the relatively weak pearlite stabilizing effect of Ni compared to that of Cu in high Si SSF DI, and matrix strengthening effect caused by the different amounts of those alloying elements required for similar pearlite fraction.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.7 no.5
• /
• pp.66-71
• /
• 1998

It is required the superior materials for the parts of machines or structures, which could be endurable in severe load and environment. According to advancement of casting technology, nodular graphite cast iron is used as suitable for such condition. But nodular graphite cast iron is scattering of fatigue strength and low reliability. Therefore in this study, the effect of matrix structure and number of nodular graphite on the initiation of fatigue crack and fatigue strength. It was found that the material which has relatively high ferrite volume fraction was more easily cracked than other materials and fatigue limit was low. The material which has not found pinhole on the surface, the crack was initiated in graphite went through ferrite and propagated into through graphite, but separated graphite and ferrite grain boundary and combined with other cracks to fro large one.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.8 no.5
• /
• pp.36-41
• /
• 1999

Although the problems of defects and nonmetallic inclusion in metal fatigue are very complicated it is particularly important to view these problems from the perspective that defects and inclusions are virtually equivalent to small cracks. This concept will help us to understand various fatigue phenomena caused by graphite of Ductile cast iron. Therefore in this study different ferrite-pearlite matrix structure and pheroidal ratio of graphite of 70%, 80% and 90% GCD40 , GCD45-2 series have been carried out rotary bending fatigue test estimated the maxi-mum size of graphite investigated correlation. It was concluded as follows : (1) in ductile cast iron which have various spheroidal ratio of graphite the fatigue limit C series of 90% spheroidal ratio of graphite is the highest. While A series of 70% spheroidal ratio of graphite is the lowest (2) fatigue limit was predicted by vickers hardness(Hv) of matrix {{{{ SQRT {area } }}}} of maximum size graphite inputting Murakami and Endo's formula.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.11 no.1
• /
• pp.82-87
• /
• 2012

For different ferrite-pearlite matrix structure, contain more than 90% spheroidal ratio of graphite, GCD 45-3, GCD 50, GCD 60 series and 70%, 80%, 90% spheroidal ratio of graphite, GCD 40, GCD 45-1, GCD 45-2 series, this paper has carried out rotary bending fatigue test, estimated maximum and mean size of spheroidal graphite, investigated correlation. It was concluded as follows. (1) Fatigue limit in $10^7$cycles and numbers of spheroidal graphite per 1$mm^2$ was linear relation. (2) projection area of graphite can be used to predict fatigue limit of Ductile Cast Iron. The Statistical distribution of extreme values of projection area of defects may be used as a guideline for the control of inclusion size in the steelmaking processes.

• Journal of Welding and Joining
• /
• v.10 no.1
• /
• pp.12-19
• /
• 1992

용접능률의 향상을 위한 대입열용접법의 적용은 과도한 입열량으로 인하여 용접부의 인성이 저 하한다는 점에서 그 적용에 주의를 요한다. 본 보에서는 대입열용접시 열영향부의 인성 저하의 원인과 그 대책을 강재의 측면에서 검토하였다. 고장력강을 용접하면 입열량이 증가함에 따라 오스테나이트 결정립이 조대화되고 상부 베이나이트와 도상 마르텐사이트가 생성되어 인성이 저하한다. 그 대책으로서는 용접 열싸이클과정중 안정한 질화물, 산화물등을 모재에 미세분산시켜 오스테나이트 결정립 성장을 억제하고, 페라이트, 펄라이트 변태를 촉진시킨다. 이러한 석출물의 형성을 위해서는 주로 Ti, Ca, REM, B등의 합금원소가 이용된다. 소입성이 높은 주질고장력 강에서는 석출물의 분산에 의한 페라이트의 변태 촉진 보다는 Mn, Ni, Cr, Mo, V등의 합금원 소를 첨가하여 소입성을 높여 인성이 우수한 하부 베이나이트 조직을 형성하든가, 탄소량을 저 감시켜 도상 마르텐사이트의 생성을 억제하므로서 인성을 확보한다. 현재 국내에서 제조되고 있는 대입열용접용강중 인장강도 50kgf/mm$^{2}$급강은 기본적으로 용접부 인성이 우수한 TMCP법으로 제조되며, Ti등을 첨가하여 석출물의 효과를 이용하고 N을 억제하여 기지의 인 성을 향상시키는 등의 방법을 병용하고 있다. 인장강도 60kgf/mm$^{2}$ 급강은 조질처리에 의하여 제조되며, 50kgf/mm$^{2}$급강과 같이 Ti, B등의 첨가에 의한 석출물의 효과를 이용 하고 있다.

• Journal of the Korean Society for Precision Engineering
• /
• v.20 no.1
• /
• pp.214-221
• /
• 2003

In this study, based on the effect of the interaction of fracture mechanics by graphite and fatigue limit phenomena of the microscopic observation various matrix structure, spheroidal ratio, size of graphite and distribution etc. parameters containd with Ductile Cast Iron. Therefore, in this study, different ferrite-pearlite matrix structure and spheroidal ratio of graphite of 70%, 80% and 90%, GCD40, GCD45-1 and GCD45-2 series and three different ferrite-pearlite matrix structure, GCD 45-3, GCD 50, GCD 60 series, all of which contain more than 90% spheroidal ratio of graphite, were used to obtain the correlation between mean size of spheroidal graphite and fatigue strength. (1) 73% pearlite structure had the highest fatigue limitation while 36% pearlite structure had the lowest fatigue limitation among ferrite-pearlite matrix. the increase in spheroidal ratio with increasing fatigue limitation, 90% had the highest, 14.3% increasing more then 10%, distribution range of fatigue life was small in same stress level. (2) (equation omitted) of graphite can be used to predict fatigue limit of Ductile Cast Iron. The Statistical distribution of extreme values of (equation omitted) may be used as a guideline for the control of inclusion size in the steelmaking processes.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.9 no.6
• /
• pp.71-77
• /
• 2010

Although the problems of defects and nonmetallic inclusion in metal fatigue are very complicated, it is particularly important to view these problems from the perspective that defects and inclusions are virtually equivalent to small cracks. This concept will help one to understand various fatigue phenomena caused by Ductile Cast Iron. For different ferrite-pearlite matrix structure, containing more than 90% spheroidal ratio of graphite, GCD 45-3, GCD 50, GCD 60 series and 70%, 80%, 90% spheroidal ratio of graphite, GCD 40, GCD 45-1, GCD 45-2 series, this paper has carried out image analyzer, estimated maximum and mean size of graphite, investigated correlation. It was concluded as follows. (1) A good quality of Ductile cast iron using in this experiment, the graphite was separated well. The effect of the interaction by graphite was verified by microscopic observation and by fracture mechanics investigation in surface, interior of the specimen. (2)${\sqrt{area}}_{max}$ of graphite can be used to predict fatigue limit of Ductile Cast Iron. The Statistical distribution of extreme values of ${\sqrt{area}}$ may be used as a guide line for the control of inclusion size in the steel making processes.