• Journal of Welding and Joining
• /
• v.6 no.2
• /
• pp.47-55
• /
• 1988

This paper reports on a study of the influence of welding variables on the weld shape of Al-7020 in pulse-GMA welding. Five variables, i.e., wire feed rate, peak pulse current, welding speed, welding votage, and pulse frequency were investigated for their effects on the weld shape. From the results of the 2$^{n-1}$ fractional factorial design, quantitative effects of each variable and the interaction of two variables were obtained, and consequently wire feed rate, welding voltage, and welding speed were determined as the main welding variables. Supplementary experiment was performed for ivestigating the detailed relationship between the main variables nd the seld shape. In this experiment, the penetation of the seldment increased when the wire feed rate was raised, nad the bead width increased when the welding voltage was raised or the welding speed was reduced.d.

• Journal of Welding and Joining
• /
• v.6 no.4
• /
• pp.54-62
• /
• 1988

Major problems in welding Al-7020 include shrinkage, rpopositgy in welds and loss of strength in the heat affected zone. Thus it is important to examine the mechanical properties and reliability of welds. In this study, a series of experiments was carried out to determine the mechanical properties such as micro-hardness distribution, tensile strength, porosity and residual stress distribution of the Al-7020 weldment made by pulse-GMA welding. The resuts of the experiemnts are as folows. 1) The micro-hardness of weld metal and heat affected zone was lower than that of the base metal. 2) The tensile strength of the deposited metal was much lower than that of the base metal. 3) The porrosity in weld metal zone was negligible under the adopted conditsion of experiemnts. 4) The residual stress in the weld metal was lower than that of the heat affected zone, because the weld metal was softened. And the mciro-hardness distribution, the tensile strength and the residual stess distribution of the weldment in the as-welded condition were compared with those of the weldment after heat treatment.