• Journal of the Korean Institute of Gas
• /
• v.2 no.1
• /
• pp.99-106
• /
• 1998

In order to investigate the impact properties of structural materials for LNG tank, instrumented Charpy impact tests were carried out at cryogenic temperatures. $9\%$ Ni steel showed a superior fracture resistance because of less degradation in toughness until 77 K. From the load-deflection curve obtained by an instrumented methods it was found that with the decrease of temperature from 173 K to 77 K, the peak load in the curve increased, but the total absorbed energy decreased. In addition, the energy absorbed during the crack growth was larger than one absorbed in the process of crack initiation. In SUS304L material, the energy absorbed in the process of the crack initiation was relatively large, but the energy absorbed in the process of crack growth was small, the behavior of absorbed energy was well agreed with the observations of the fracture surface which showed a relatively smooth fracture surface. The absorbed Charpy impact energy in the case of A5083 alloy was lower as compared with other steels, and some cracks were observed along the crack propagation direction at the fracture surface of 77 K.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.26 no.8
• /
• pp.1645-1652
• /
• 2002

The failure analysis on fractured parts is divided into the qualitative method by naked eyes and metallurgical microscope etc. and the quantitative method by SEM and X-ray diffraction etc. X-ray fractography can be applied to contaminated surface as well as clean surface and gain the plastic deformation and the residual stress near the fractured surface. Turbine blade is subject to cyclic bending force by steam pressure and suffers fatigue damage according to the increasing operating time. Therefore, to clean up the fracture mechanism of torsion-mounted blade in nuclear plant, the fatigue and the X-ray diffraction test was performed on the 12%Cr steel fur turbine blade and the fractured parts. The correlation of X-ray parameter and fracture mechanics parameter was determined, and then the load applied to actual broken turbine blade was predicted. Failure analysis was performed by contact stress analysis and Goodman diagram of torsion-mounted blade.

• Proceedings of the KSME Conference
• /
• 2001.11a
• /
• pp.258-265
• /
• 2001

Turbine blade is subject to force of three type ; torsional force by torsion-mount, centrifugal force by rotation of rotor and cyclic bending force by steam pressure. Cyclic bending force of them is main factor on fatigue fracture. In the X-ray diffraction method, the change in the values related to plastic deformation and residual stress near the fracture surface mat be determined, and information of internal structure of material can be obtained. Therefore, to find a fracture mechanism of torsion-mounted blade in nuclear plant, based on the information from the fracture surface obtained by fatigue test, the correlation of X-ray parameter and fracture mechanics parameter was determined, and then the load applied to actual broken turbine blade parts was predicted. Failure analysis is performed by finite element method and Goodman diagram on torsion-mounted blade.

• Proceedings of the Optical Society of Korea Conference
• /
• 2009.10a
• /
• pp.203-204
• /
• 2009

• Journal of Power System Engineering
• /
• v.9 no.2
• /
• pp.57-64
• /
• 2005

This paper is the study on dry sliding wear behavior of carbon fiber reinforced epoxy matrix composites against lay-up orientation. Tests were investigated on the effect of the lay-up orientation, fiber sliding direction, load and sliding velocity when circumstance keep continuously at $21^{\circ}C$, 60%RH. Pin-on-disk dry sliding wear tests for each experimental condition were carried out with a carbon fiber reinforced plastic pin on stainless steel disk in order to search the friction and wear characteristics. The wear rates and friction coefficients against the stainless steel counterpart were experimentally determined and the wear mechanisms were microscopically observed. The effect on friction and wear behavior are observed differently, according to various conditions. When sliding took place against counterpart, the highest wear resistance and the lowest friction coefficient were observed in the $[0]_{24s}$ lay-up orientation at anti-parallel direction.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.8 no.2
• /
• pp.86-93
• /
• 1999

Ceramic/metal bonded joints have led to increasing use of structural materials such as automobiles and heat engines. A method of strength evaluation focussing on fracture criterion of mixed mode was investigated in {{{{ {Si }_{3 } {N }_{4 } }}}}/metal bonded joint, Also Fracture toughness tests of {{{{ {Si }_{3 } {N }_{4 } }}}}/metal bonded joints with an interface crack were carried out and the stress intensity factors of these joints were analyzed by boundary element method. Form the results the fracture criterion and method of strength evaluation by the fracture toughness were proposed in {{{{ {Si }_{3 } {N }_{4 } }}}}/Metal bonded joints

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2001.10a
• /
• pp.119-126
• /
• 2001

유리와 같이 취성이 큰 재료의 파단면을 주의하여보면 반원형의 곡선이 이따금씩 여러개 나타나 있는 것을 볼 수 있다. 이것은 진행 중에 있는 균열이 어떠한 부분으로부터 나온 음파(횡파)와 만났을 때 일어나는 흔적으로 Wallner선 이라고 한다. 초음파 Fractography는 파괴 시험시 강력한 초음파를 사용하여 파단면에 이와 같은 Wallner 선을 인공적으로 발생시켜, 파면해석을 통하여 파괴속도등 파괴연구에 필요한 정보를 얻는 수법이다. 이 수법은 유리와 같은 비정질 탄성태의 파괴속도 측정을 위해 Kerkhof에 의해 최초로 고안되었으며, 수지와 같은 점탄성재료에 대해서는 Takahashi에 의하여 PMMA(Polymethy1 Methacrylate)재에 강력한 초음파를 사용하여 그 가능성이 제기된 이후 PMMA와 EPOXY재등의 점탄성재료의 파괴속도측정과 파괴강성등의 측정에 본격적으로 연구되기 시작하였다.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.41 no.1
• /
• pp.78-84
• /
• 2005

The main goal of this work is to study the effects of temperature and volume fraction of fiber on the Charpy impact test with GF/PP composites. The critical fracture energy and failure mechanisms of GF/PP composites are investigated in the temperature range of 60^{\circ}C$ to -50^{\circ}C$ by impact test. The critical fracture energy increased as the fiber volume fraction ratio increased. The critical fracture energy shows a maximum at ambient temperature and it tends to decreases as temperature goes up or goes down. Major failure mechanisms can be classified such as fiber matrix debonding, fiber pull-out and/or delamination and matrix deformation.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 1998.03a
• /
• pp.287-292
• /
• 1998

In this study behavior of fatigue crack and fatigue fracture is observed under rotary bending fatigue testing in friction welded dissimilar materials. Fatigue fracture most occurred in SM15C heat affected zone around Interface. In case of fatigue test, stress is reduced the position of fracture gradually moves to the welded Interface. Micro crack of heat affected zone surface on SM15C is observed at any different stress.

• Proceedings of the KSR Conference
• /
• 2000.11a
• /
• pp.461-467
• /
• 2000

This study proposes the integrity evaluation of bogie frame using ultrasonic waves-fractography analysis. Analysis objectives in this study are to investigate fracture planes of damaged zone by the A-scan method. The surface condition of fracture plane shows degree of degradation by stress concentration. The detection of the natural defects in bogie frame is performed using the characteristics of echodynamic pattern in ultrasonic signal. Results of ultrasonic testing agree fairly well with those of actual fracture plane. In quantitative fractography analysis, microstructures of actual fracture plane turned out to be intergranular and transgranular fracture, Proposed ultrasonic-fractography analysis in this study can be used for the integrity evaluation of the bogie frame