The effect of weld improvement on the corroded fatigue life of welded structures was investigated. Toe grinding, TIG dressing and weld profiling were used as the geometric improvement methods. Fatigue tests under the corroded condition in artificial seawater were carried out to investigate the corrosion fatigue behavior of API 2W Gr.50T steel plate produced by POSCO. The test results in weld improved conditions were compared with those in as-welded condition. The test results were also compared with the design curves in UK DEn Class F. Corroded fatigue life of weld improved specimens was longer than that of as-welded specimen. Especially, the corroded fatigue life exceeded the mean SN curve in air of UK DEn Class F.

• Journal of Welding and Joining
• /
• v.24 no.2
• /
• pp.42-47
• /
• 2006

While it is known that the weld toe grinding method may give 3.4 times of fatigue strength improvement, this improvement may significantly vary according to weld bead shapes and loading modes. Although tremendous interest have been given in improving fatigue strength improvement for ship structures, quantitative results are yet in need. In this context, a series of fatigue tests is carried out for a type of test specimen that are typically found in ship structures. Weld burr grinding is carried out using a electric grinder in order to remove surface defects and improve the weld bead profile. The test results are compared with the same type of test specimen without applying the fatigue improvement technique in order to obtain a quantitative measure of the fatigue strength improvement. On the other hand, both hot spot stress and structural stress methods are employed to compare the effectiveness of the two methods in evaluating the fatigue strength improvement of welded structures.

• Journal of the Korean Society for Precision Engineering
• /
• v.29 no.3
• /
• pp.307-312
• /
• 2012

This study aims to investigate the effect of the post weld treatments on the fatigue life of T-type welded structure made by a SM50A steel material, generally used for excavators, because changes in the geometry, material and surface properties of welded regions affect the fatigue life of welded structures. T-type test specimens were prepared by the CO2 welding of rolled steel plates (SM50A steel) with a thickness of 10 mm at a welding speed of 30 cm/min and these Ttype welded specimens were further treated by UIT (Ultrasonic Impact Treatment) and/or toegrinding post welding treatment methods. In order to investigate improvements on the fatigue life of the samples. 3-point bending fatigue tests were conducted with a stress ratio of R=0.1 under a cyclic loading environment at a frequency of 5 Hz, via a hydraulic fatigue testing machine (${\pm}100\;kN$, MTS 809). The tests were performed at room temperature. The fatigue life of UIT specimens was approximately 25 times longer than that of as-welded specimens at a stress amplitude of 281 MPa, while toe-grinding specimens exhibited 4.15 times longer fatigue life. The current results could provide important guidelines to determine the proper post weld treatment methodologies of T-type welded parts for excavators with a satisfactory fatigue life although under severe operating conditions.