The welds tent to be weakened if it is exposed to the air during the welding process. In titanium welding with Gas Tungsten Arc Welding, inappropriate colors of the welds, such as purple/red, blue, yellow, gray, white and pink represents that it is contaminated by oxygen and nitrogen in the air. Shielding gases can be used to protect welds from the contamination. In addition, Weld metal and heat affected zone (HAZ) are also shielded from the air when it is cooled down to the room temperature. In this paper, appropriate shielding gases for the shape and form of Trailing Shielding Jig and torch shielding ($13{\sim}20{\ell}/min$), after shielding ($22{\sim}30{\ell}/min$), and back shielding ($25{\sim}30{\ell}/min$) are studied.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.41 no.4
• /
• pp.321-327
• /
• 2017

In this study, to investigate the shape of the back bead as a weld quality parameter and to select the optimal condition of the root-pass TIG welding of a horizontal butt-joint, an experimental design and the response surface method (RSM) have been employed. Three parameters are used as input variables, which include the base current, peak current, and welding speed. The back bead width is selected as an output variable representing the weld quality, the target value of the width is 5.4 mm. Conducting the experiments according to the Box-Behnken experimental design, a $2^{nd}$ regression model for the back bead width was made, and the validation of the model was confirmed by using the F-test. The desirability function was designed through the nominal-the-best formula for the appropriate back bead width. Finally, the following optimal condition for welding was selected using the RSM: base current of 0.9204, peak current of 0.8676, and welding speed of 0.3776 in coded values. For verification, a test welding process under the optimal condition was executed and the result showed the back bead width of 5.38 mm that matched the target value well.

• Journal of Welding and Joining
• /
• v.15 no.1
• /
• pp.135-148
• /
• 1997

It was attempted to improve wear resistance and durability under the load surface pressure that make a formation of the thick (mm-order) hard-surfacing layer for aluminum alloy of 5083. The thick hard layers were formed on the surface of 5083 by TIG overlay method. Al-(25.4, 33.6, 45.7 mass%) Cu filler metals which were newly developed were overlaid on two base metals forming the one bead, one layer and two layers. The investigation was made on the characteristics of hardening and wear resistance in relation to the microstructure of overlaid layers with selection of optimum overlaying condition.