• Composites Research
• /
• v.30 no.2
• /
• pp.116-125
• /
• 2017

The purpose of this study is to develop silicon carbide fiber showing an excellent mechanical properties under highly oxidative conditions at high temperature. Polycarbosilane(PCS) as a preceramic precursor was used for making the SiC fiber. PCS fiber was taken by melt spinning method followed by melting the PCS at $300{\sim}350^{\circ}C$ in N2 gas. The Curing of PCS fiber was carried out in air oxygen chamber, prior to high temperature pyrolysis. Degree of cure was calculated by characteristic peak's ratio of Si-H to $Si-CH_3$ in FT-IR spectra before and after curing of PCS fiber. The properties of SiC fiber was affected greatly by the degree of cure. The SiC fiber produced by controlling fiber tension during heat treatment showed good properties. The SiC fiber exposed to $1000^{\circ}C$ at air from 1 min. up to maximum 50 hrs showed around 60% reduction in tensile strength. We found that large amount of carbon content on the fiber surface after long-term exposure has resulted in lower tensile strength.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.30 no.6
• /
• pp.258-263
• /
• 2020

Silicon carbide (SiC) fibers mainly fabricated from polycarbosilane, a ceramic precursor, are applied as reinforcing materials for ceramic matrix composites (CMCs) because of their high temperature oxidation resistance, tensile strength, and light weight. In this study, continuous SiC fibers used to fabricate rope-type flexible heating elements capable of generating high-temperature heat (> 650℃). For high-efficiency heating elements, the resistance of SiC fiber rope was measured by 2-point probe method according to the cross-sectional area and length. In addition, the fabrication conditions of rope-type SiC fiber heating elements were optimized by controlling the oxygen impurities and the size of crystal grains present in the amorphous SiC fiber. As a result, the SiC fiber heating element having a resistance range of about 100~200 Ω exhibited an excellent power consumption efficiency of 1.5 times compared to that of the carbon fiber heating element.

• Composites Research
• /
• v.30 no.2
• /
• pp.102-107
• /
• 2017

The preceramic polymer can realize a variety of complex ceramic structures that can not be obtained by conventional ceramic processes. Polycarbosilane, which is a typical preceramic polymer, can control the molecular structure, molecular weight and molecular weight distribution for preparing complex morphology and microstructure of SiC ceramics, including SiC fiber. In this paper, synthesis and molecular structure control technique of polycarbosilane is explained. The silicon carbide fiber prepared by melt spinning, stabilization and heat treatment, and ceramic fiber composites technology made by PIP process are also discussed. In addition, we introduce an example of the development of a complex silicon carbide material such as a silicon carbide hollow fiber having a nanoporous structure.

• Journal of the Korean Ceramic Society
• /
• v.36 no.8
• /
• pp.805-812
• /
• 1999

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.30 no.6
• /
• pp.271-276
• /
• 2020

In this study, an amorphous SiC block was manufactured using polycarbosilane (PCS), an organosilicon polymer. The dense SiC blocks were easily fabricated in various shapes via pyrolysis at 1100℃, 1200℃, 1300℃, 1400℃ after manufacturing a PCS molded body using cured PCS powder. Physical and chemical properties were analyzed using a thermogravimetric analyzer (TGA), scanning electron microscope (SEM), energy dispersive spectroscopy (EDS), and universal testing machine (UTM). The prepared SiC block was decomposed into SiO and CO gas as the temperature increased, and β-SiC crystal grains were grown in an amorphous structure. In addition, the density and flexural strength were the highest at 1.9038 g/㎤ and 6.189 MPa of SiC prepared at 1100℃. The manufactured amorphous silicon carbide block is expected to be applicable to other fields, such as the previously reported microwave assisted heating element.

• Korean Journal of Materials Research
• /
• v.8 no.6
• /
• pp.551-559
• /
• 1998

장경비가 큰 탄화규소를 탄소와 규소간의 고온연소반응으로 제조하기 위하여 공정변수에 따른 연소거동과 미세조직의 변화를 조사하였다. 연소합성된 생성물은 주로 $\beta$-SiC이며 연소반응이 충분히 진행되지 못하였을 경우에는 미량의 잔류 반응물과 $\alpha$-SiC가 관찰되었다. 생성된 탄화규소의 평균입도는 약 5$\mu\textrm{m}$로 작았으며, $1300^{\circ}C$ 이상의 예열 조건에서 장경비가 30이상인 탄화규소를 합성할 수 있었다. 압분 강도가 69MPa인 분말의 성형체에서 평균 연소 온도와 평균 전파 속도는 각각 약 $1425^{\circ}C$와 2.1mm/sec 범위이며, 연소 온도는 흑연 분말을 사용하였을 경우가 탄소 섬유를 사용한 경우보다 약 $10^{\circ}C$ 높았다. 연소 반응을 임의로 중단시킨 시편의 계면을 EDX와 Auger 전자 현미경으로 분석한 결과 상호 확산층이 관찰되지 않았다. 이는 탄화규조의 연소합성이 용해-석출 모델에 의하여 진행됨을 시사한다. 예열 온도에 따른 연소 반응 중의 온도 분포를 유한 요소법으로 해석함으로써 $2500^{\circ}C$의 초기 연소 개시 온도에 대하여 예열 온도 $300^{\circ}C$에서는 연소파가 거의 전파할 수 없으며 예열 온도가 $1300^{\circ}C$에서는 시료 내부에 자체 전파가 가능한 $2000^{\circ}C$이상의 온도 구역이 존재함을 알았다.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1993.05a
• /
• pp.124-124
• /
• 1993

• Composites Research
• /
• v.35 no.1
• /
• pp.23-30
• /
• 2022

Polycarbosilane(PCS) is an important precursor for melt-spinning the silicon carbide(SiC) fibers and manufacturing ceramics. The PCS is a metal-organic polymer precursor capable of producing continuous SiC fibers having excellent performance such as high-temperature resistance and oxidation resistance. The SiC fibers are manufactured through melt-spinning, stabilization, and heat treatment processes using the PCS manufactured by synthesis, purification, and control of the molecular structure. In this paper, we analyzed the effect of purification of unreacted substances and low molecular weight through solvent treatment of PCS and the effect of heat treatment at various temperatures change the polymerization and network rearrangement of PCS. Especially, we investigated the complex viscosity and structural arrangement of PCS precursors according to solvent treatment and heat treatment through the rheological properties.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2002.10a
• /
• pp.54.1-54
• /
• 2002

• Proceedings of the Korean Ceranic Society Conference
• /
• 2000.04a
• /
• pp.113.1-113.1
• /
• 2000