• Journal of the Korean Geotechnical Society
• /
• v.29 no.4
• /
• pp.45-56
• /
• 2013

In this study, a blast furnace slag with latent hydraulic property is used to cement granular soils without using Portland cement. When the blast furnace slag reacts with an alkaline activator, it can cement soils. The effect of amounts of blast furnace slag and types of alkaline activator on soil strength was investigated for resource recycling. Four different amounts of slag and six different activators (two naturals and four chemicals) were used for preparing specimens. The specimens were air-cured for 3 or 7 days and then tested for unconfined compressive strength (UCS). The UCS of cemented sand with slag increased, in the order of specimens mixed with potassium carbonate, calcium hydroxide, sodium hydroxide and potassium hydroxide. Chemical alkaline activator was better than natural alkaline activator. The maximum UCS of 3-days cured specimens was 3 MPa for 16% of slag with potassium hydroxide, which corresponded to 37% of one with 16% of high-early strength portland cement. As the amount of slag increased, the UCS and dry density of a specimen increased for all alkaline activator cases. As the curing time increased from 3 days to 7 days, the UCS increased up to 97%. C-S-H hydrates were found in the cemented specimens from XRD analyses. Cement hydrates were more generated with increasing amount of slag and they surrounded sand particles, which resulted in higher density.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2023.05a
• /
• pp.115-116
• /
• 2023

This study aims to investigate and improve the carbon dioxide sequestration capability and the mechanical properties of non-hydraulic low calcium silicate cement especially designed for CO₂ reaction and ordinary Portland cement subjected to the carbonation curing facilitating pH swing method. Nitric acid (HNO₃) was utilized as an liquid for the mixing of cement paste to enhance the initial dissolution of Ca ions from the cements by promoting low pH environment and prevent the direct precipitation of Ca with the anion, owing to the high solubility of Ca(NO₃)₂ in water. The results presented that the higher the concentration of HNO₃, the higher the compressive strength and CO₂ sequestration (until 0.1 M). Ca dissolution caused by the harsh acid attack onto the anhydrous cement particle lead to the higher carbonation reaction degree, forming abundant CaCO₃ crystals after the reaction. However, cement paste mixed with excessively high concentration of HNO₃ presented deterioration due to the too harsh pH environment and abundant NO₃- ions which are known to retard the reaction of cement.

• Journal of the Korea Concrete Institute
• /
• v.27 no.3
• /
• pp.237-244
• /
• 2015

Entering the 20th century since the industrial revolution, the cement has been widely used in the field of construction and civil engineering due to the remarkable development of construction industry. However, result from that development, each kind of industrial by-products and waste and the carbon dioxide generated in the process of cement production cause air pollution and environmental damage so earth is getting sick now slowly. Therefore, we have to recognize importance about this. It means that the time taking specific and long-term measures have come. In this research paper, as substitution of the cement generating environmental pollution, we investigate the hydration reaction of non-Sintered Cement mortar mixed with GBFS, active stimulant of alkaline and sulphate series by using SEM and XRD, mechanical and chemical properties according to the curing method. As a result of this experiment, NSC realized outstanding strength for water curing and steam curing. It means that it has a good possibility as substitution of cement. From now on, it can be used for structure satisfying specific standard. We expect to find a substitution of outstanding cement by progressing continuous research making the best use of pros and cons according to the curing method.

• Proceedings of the Korea Water Resources Association Conference
• /
• 2023.05a
• /
• pp.464-464
• /
• 2023

최근 이산화탄소(Carbon Dioxode, CO₂) 배출량 증가로 인하여 지구온난화와 같은 기후변화 문제가 심각한 사회 문제로 대두되고 있다. 이에 따라 2015년 12월 12일 프랑스 파리에서 열린 제21차 유엔기후변화협약에서 교토의정서를 대체하는 파리협정(Paris Agreement)을 채택하였으며, 국내에서는 이러한 국제사회의 기후변화 대응에 동참하고 온실가스 감축을 이행하기 위한 2050 탄소중립 정책을 추진하였다. 이산화탄소를 다량으로 발생시키는 철강·산업·건설·에너지 분야 중건설 분야에서 배출되는 이산화탄소는 전체 배출량의 19.9%로 특히 시멘트를 제조하는 과정에서 많은 양의 이산화탄소가 배출되고 있다. 기존의 건설 분야 에서는 이산화탄소를 저감하기 위해 콘크리트 배합 또는 양생과정에서 챔버 내 이산화탄소를 가스 형태로 주입하여 탄산화 반응을 통해 콘크리트 내부에 이산화탄소를 영구히 저장시키고자 하였다. 그러나 이는 챔버 사용, 양생조건 등 적용 조건이 제한적이며, 콘크리트 내 이산화탄소 흡수 효율이 높지 않아 이를 개선할 수 있는 기술이 필요하다. 이를 개선하기 위해 최근에는 콘크리트 배합수 내 이산화탄소를 용해시켜 배합과정에서 콘크리트 내부로 이산화탄소를 강제로 인입시키는 연구들이 진행되고 있다. 그러나 콘크리트 배합수로 사용되고 있는 일반물이나 지하수의 경우 가압을 하여도 약 1,400mg/L의 이산화탄소를 용해시키며, 가압을 통해 용해된 이산화탄소는 쉽게 대기 중으로 방출되는 한계점을 지니고 있어 현장에서 사용하기 어려운 문제가 있다. 이러한 한계점을 극복하기 위해서 본 연구에서는 200nm 이하의 크기를 가지는 나노버블기술을 이용해 압력을 가하지 않은 상태에서 수중에 이산화탄소를 용해시킬 수 있는 시스템을 개발하고자 한다. 나노버블기술을 이용한 수중 이산화탄소용해 시스템을 통해 수중에 이산화탄소를 용해시켜 콘크리트 배합수로 활용하기 위한 기초 연구가 될 것으로 판단된다.

• Journal of the Korea Institute of Building Construction
• /
• v.24 no.2
• /
• pp.181-191
• /
• 2024

In the realm of cement manufacturing, concerted efforts are underway to mitigate the emission of greenhouse gases. A significant portion, approximately 60%, of these emissions during the cement clinker sintering process is attributed to the decarbonation of limestone, which serves as a fundamental ingredient in cement production. Prompted by these environmental concerns, there is an active pursuit of alternative technologies and admixtures for cement that can substitute for limestone. Concurrently, initiatives are being explored to harness technology within the cement industry for the capture of carbon dioxide from industrial emissions, facilitating its conversion into carbonate minerals via chemical processes. Parallel to these technological advances, economic growth has precipitated a surge in construction activities, culminating in a steady escalation of construction waste, notably waste concrete. This study is anchored in the innovative production of calcium silicate cement clinkers, utilizing finely powdered waste concrete, followed by a thorough analysis of their mineral phases. Through X-ray diffraction(XRD) analysis, it was observed that increasing the substitution level of waste concrete powder and the molar ratio of SiO₂ to (CaO+SiO₂) leads to a decrease in Belite and γ-Belite, whereas minerals associated with carbonation, such as wollastonite and rankinite, exhibited an upsurge. Furthermore, the formation of gehlenite in cement clinkers, especially at higher substitution levels of waste concrete powder and the aforementioned molar ratio, is attributed to a synthetic reaction with Al₂O₃ present in the waste concrete powder. Analysis of free-CaO content revealed a decrement with increasing substitution rate of waste concrete powder and the molar ratio of SiO₂/(CaO+SiO₂). The outcomes of this study substantiate the viability of fabricating calcium silicate cement clinkers employing waste concrete powder.

• Journal of the Korean GEO-environmental Society
• /
• v.18 no.10
• /
• pp.15-22
• /
• 2017

The soil improvement method so far has been developed with an emphasis on enhancing the strength of the ground. A soil improvement method using a excellent cementitious stabilizer in economical efficiency and handling property is mainly used. The soil improvement method using cementitious stabilizer is effective but environmental and human harmful substances are detected and environmental problems such as carbon dioxide emission and groundwater pollution are pointed out. Therefore, as part of an alternative method capable of solving such problems, researches on the soil improvement method incorporating biological technology are being actively carried out. This study was conducted to investigate the characteristics of strength change when mixed with environmentally friendly soil binder and microorganism in clay, and it was analyzed by uniaxial compression test, direct shear test, SEM, XRD. As a results of the test, we confirmed the cementation caused by microbially induced calcite precipitation and the strength increase enhancement by it.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2014.05a
• /
• pp.264-265
• /
• 2014

Currently, CO₂ existed in the air usually reacts concrete, and then CaCO₃ can be appeared. As time goes by, pH of concrete is decreased and corrosion of steel can be happened. This phenomenon is called carbonation. For preventing carbonation of concrete, various methods like using corrosion inhibitor, high compressive strength concrete, and enough covering depth are adopted. But these method are usually passive methods focused on corrosion of steel and have limitation on economic. Thus, as basic study for active method of carbonation, cement pastes with CO₂ reactive material (γ-C₂S, MgO) and GBFS were in accelerated carbonation, and the compressive strengths were measured. On the result, the compressive strength was improved better than non-carbonation. Through measuring the weight change using TG-DTA, as specimens were carbonated, according to decreasing of Ca(OH)₂ and Mg(OH)₂, CaCO₃ and MgCO₃ were increased. Therefore it can be shown that carbonation curing can be realized.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2017.05a
• /
• pp.165-166
• /
• 2017

Corrosion of reinforcement is the main factors affecting the durability of reinforced concrete in the world which lead to the failure of structures of reinforced concrete buildings. In this research, mixed brucite(Mg(OH)₂) into ordinary portland cement paste in ratio of 5, 10 and 15% as a kind of CO₂ fixation material. Samples were exposed to an accelerated carbonation enslavement of 20% CO₂ concentration, 60% relative humidity, and a temperature of 20℃ until tested at 3d, 7d, 14d and 28d. After 28d CO₂ accelerated curing, in the paste containing MH megnesian calcite was found by XRD and SEM-EDX. Meanwhile, paste containing Mg(OH)₂ exhibit the better pore distribution than ordinary portland cement paste and relatively good compressive strength.

• Journal of the Korea Concrete Institute
• /
• v.23 no.5
• /
• pp.609-615
• /
• 2011

MgO concrete containing lightly burnt MgO powder at $850{\sim}1,000^{\circ}C$ may have a long-term expansibility characteristic. Such expansibility of MgO concrete can compensate the shrinkage at later ages since the hydration of the MgO is very slow. However, the addition of MgO delays the initial hydration of cement and increases the setting time of cement. Also, the porosity and pore-size distribution of the MgO concrete are different from OPC concrete. Therefore, in order to use MgO in practice, both mechanical and durability properties of MgO concrete should be carefully examined. In this study, durability tests on carbonation, freezing-thawing, and diffusion of chloride were carried out after 56 days of underwater curing at $20^{\circ}C$ to compare durability characteristics of 5% MgO-mixed concrete with those of OPC concrete. The results showed that MgO concrete shows a greater durability than the concrete with no MgO, because the micro structure in the MgO concrete is much denser due to its expansibility characteristic.

• Journal of the Mineralogical Society of Korea
• /
• v.31 no.4
• /
• pp.267-275
• /
• 2018

The purposes of this study were to analyze the mineralogical characteristics of slaked lime used for wall repair of traditional buildings in Bagan, Myanmar and to evaluate the physical properties of lime plaster produced by the same method as Bagan region. In the X-ray diffraction and thermal analysis of the Myanmar slaked lime, portlandite ($Ca(OH)_2$) and brucite ($Mg(OH)_2$) were detected as main constituent minerals, and a carbonate rock mainly composed of dolomite ($CaMg(CO_3)_2$) minerals may be used as a raw material to make slaked lime. The field-emission scanning electron microscope analysis showed that the Myanmar slaked lime was composed of irregularly shaped crystals of $0.5{\mu}m$ or larger and a small amount of $0.1{\mu}m$ of plate - like crystals. The size and uniformity of crystals in Myanmar lime is different from that of Korea slaked lime. This may be attributed to the effect of the mineral composition and the lime hydration method of Myanmar, which produces slurry by immersing the burnt lime in excess water for a long period of time. The compressive strength of the lime plaster in Myanmar resulted in a mean value of $1.13N/mm^2$ for the specimens cured for 28 days. The strength of the specimens with Bale juice was $1.03N/mm^2$, respectively. The lime is an air setting material that exhibits strength through long carbonation process. Therefore, it is necessary to evaluate physical properties according to curing period through long-term curing over 28 days in the future.