• Journal of Ocean Engineering and Technology
• /
• v.6 no.2
• /
• pp.85-93
• /
• 1992

The only hardness of 2nd phase of martensite in dual phase steel which was composed of the martensite and ferrite was changed. Fatigue test was conducted by cantilever type of self-made rotated bending fatigue testing machine. The corrosion fatigue fracture behaviors of dual phase steel were investigated in 3% NaCl solution at $N_f$ = $1.5\times$$10^5$ $N_f$=1.0 $\times$ $10^6$ cycles. The fatigue strength was increased with increasing the hardness of 2nd phase. The size and number of corrsion pits were influenced by the 2nd phase hardness and pits remain constant in size just after they were transited into cracks. The life of crack initiation was effected by stress level. The shape of relation of $\Delta$K and da/dn has smaller scattering in it in 3% NaCl solution than that in air. The higher the 2nd phase hardness is, the higher the corrosion fatigue life becomes. Corrosion fatigue fracture behavior was effected by mechanics in case of $N_f$=1.5$\times$10$^5$$N_f$=1.5$\times$10$^6$ cycles.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.23 no.5
• /
• pp.471-477
• /
• 2015

In this study, the property of crack propagation and growth at high tension steel plate existed with center crack is investigated. The behaviors of fracture mechanics due to existence or not of hole near the center crack in specimen and the length of crack length are investigated when the load is applied at the one side end of specimen. Stress, deformation and deformation of this specimen are evaluated through simulation analysis. By the analysis results at this study, stress intensity factors are obtained. The damage happened at machine or structure with crack or defect can be estimated on the basis of study results.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.12 no.3
• /
• pp.473-480
• /
• 1988

In this study, a method that can realize the effect of residual stresses on fatigue crack propagation has been proposed. This method requires that the relaxation quantities of residual stresses are measured by experimental method according to fatigue cycles and are employed to the experimental results of base materials by introducing the concept of superposition. SS41 material has been analyzed as an example. The results show that the relaxation factor of residual stresses for fatigue cycles is .alpha.$_{i}$= 1/0.6903+0.0380 $a_{I}$ the effective stress ratio for fatigue crack propagation length is ( $R_{eff}$)$_{i}$ = 1/1.1274+0.0118$_{I}$ and the fatigue crack propagation rate for relaxation quantities of residual stresses is (da/dN)$_{t}$ = 0.5 $K_{cf}$ - .DELTA.K/{1-1/1.1274+0.0118$_{ai}$ } $K_{cf}$ - .DELTA. K(da/dN), for stress ratio /R=0.5.io /R=0.5.5.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.10 no.2
• /
• pp.186-192
• /
• 2002

The fatigue crack propagation characteristics were investigated on dissimilar friction weld of two kind of heat-resisting steels (STR3 and STR35) commonly used in valve materials for vehicles. A small circular artificial defect was machined to induce fatigue crack at bonded line, heat affected zone and base metal of the weld on the surface of the specimens. From the results of the experiment, the fatigue limits of the materials STR3 and STR35 were obtained to be 429.0MPa and 409.4MPa respectably. The STR35 base metal and 1.0mm HAZ specimens showed 190% and 82% higher fatigue life than STR3 base metal. And the fatigue life of 1.0mm HAZ specimen was shown 99% on STR3 and 29% on STR35 higher than that of their base metal. But the fatigue life of weld interface specimen was shown 18% on STR3 and 72% on STR35 lower than that of their base metal because of the weld interface separation.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.36 no.12
• /
• pp.1619-1625
• /
• 2012

An electrical steel strip is commonly used as a core material in all types of electric transformers and motors. It is produced by a cold rolling process. In this paper, a damage-mechanics-based approach that predicts the edge fracture of an electrical steel strip during cold rolling is presented. We adopted the normal tensile stress criterion and the fracture energy method as a damage initiation criterion and a damage evolution scheme, respectively. We employed finite element analysis (FEA) to simulate crack initiation and propagation at the initial notch located at the edges of the strip. The material constants required in FEA were experimentally obtained by tensile tests using a standard and a notched sheet-type specimen. The results reveal that the edge crack was initiated at the entrance of the roll bite and that it rapidly evolved at the exit. The evolution length of the edge crack increased as the length of the initial notch as well as the front tension reel force of the strip increased.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.12 no.6
• /
• pp.1327-1334
• /
• 1988

In this study rotating bending fatigue tests have been carried out with the deep non-through radial holed notch specimens of low carbon steels(SM 22C). It is investigated that the behaviors of surface and interior fatigue crack propagation and the variations of the shape of the cracked surface on the magnitude of bending stresses. The Obtained results are summarized as follows. (1) The relations between [Crack length] and [Cycle ratio] are expressed by following eq. in the 0.1~0.6 range of N/ $N_{f}$ long[ crack length] = A + B [N/ $N_{f}$ ] In case of surface crack length, values of A and B are uniformed independent upon the magnitude of bending stress, but those are variable according to the magnitude of bending stress for interior crack length. (2) The following eq. is derived on the surface crack propagation rate, bending stress and surface crack length. (dl/dN)=(3.94*10$^{-12}$ ).sigma.$^{4.54}$l (3) Under small stress, interior crack propagation rate increase with the interior crack growth but it decrease for large stress. (4) The shape of cracked surface depends upon the magnitude of bending stress. Under small stress fatigue crack propagates as an semi-ellipse with semi-major axis of surface crack length with semi-major axis of interior crack length for large stress.s.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.19 no.9
• /
• pp.2133-2141
• /
• 1995

The thermo-mechanical fatigue tests were performed on the specimens extracted from 1.5Cr-0. 67Mo-0.33V alloy. The characteristics of thermo-mechanical fatigue crack propagation were examined and reviewed in view of fracture mechanics. The results obtained from the present study are summarized as follows : (1) The propagation characteristics of isothermal low-cycle fatigue crack are dominated by .DELTA.J$_{f}$ in case of PP waveform, and .DELTA.J$_{c}$ in case of CP waveform. (II)The propagation characteristics of thermo-mechanical fatigue crack are dominated by .DELTA.J$_{c}$ for in-phase case, and by .DELTA.J$_{c}$ for out-of-phase. The present results were in good agreement with the equation of propagation law for isothermal low-cycle fatigue crack in case of thermo-mechanical fatigue.tigue.e.

• Journal of Power System Engineering
• /
• v.4 no.4
• /
• pp.41-47
• /
• 2000

Fatigue crack propagation rate and threshold characteristics of the SA516/70 steel which is used for the low temperature pressure vessels, were studied in the room temperature of $25^{\circ}C$ and low temperature ranges of $-10^{\circ}C,\;-30^{\circ}C,\;-60^{\circ}C\;and\;-80^{\circ}C$ with stress ratio of R=0.1. In the logarithmic relationship between the fatigue crack propagation rate($d{\alpha}/dN$) and stress intensity factor range ${\Delta}K$, the linear relationship was obtained up to $d{\alpha}/dN=4.425{\times}10^4mm/cycle$ in the same of room temperature, but in low temperature case, the relationship was extended to the range of low crack propagation rate. The fractured specimens were examined by SEM. Tested results showed that specimen failed at low temperature exhibit the quasi-cleavage fracture formation however considerable ductility proceed final fracture.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2001.05a
• /
• pp.326-331
• /
• 2001

In this study. CT specimens were prepared from ASME SA5l6 which was used for pressure vessel plates for room and low temperature service. And we got the following characteristics from fatigue crack growth test carried out in the environment of room and low temperature at $25^{\circ}C$, -3$0^{\circ}C$, -6$0^{\circ}C$, -8$0^{\circ}C$, -10$0^{\circ}C$ and -12$0^{\circ}C$ in the range of stress ratio of 0.1 by means of opening mode displacement. At the constant stress ratio, the threshold stress intensity factor range ΔKsub/th/ in the early stage of fatigue crack growth ( Region I) and stress intensity factor range ΔK in the stable of fatigue crack growth ( Region II) was increased in proportion to descend temperature. It assumed that the fatigue resistance characteristics and fracture strength at low temperature is considerable higher than that of room temperature in the early stage and stable of fatigue crack growth region. The straight line slope relation of logarithm da.dN -ΔK in RegionII, that is, the fatigue crack growth exponent m increased with descending temperature at the constant stress ratio. It assumed that the fatigue crack growth rate da/dN is rapid in proportion to descend temperature in Region II and the cryogenic-brittleness greatly affect a material with decreasing temperature.

• Journal of Ocean Engineering and Technology
• /
• v.6 no.1
• /
• pp.140-147
• /
• 1992

Corrsion fatigue test was performed under rotated bending in 3.5% NaCl aqueous solution having a temperature from 278.deg.K in order to investigate the effects of aqueous solution remperature on the corrosion fatigue fracture of raw material steel(SS41) and dual phase steel that was produced from SS41 by a series of heat treatment. Corrosion fatigue life decreases remarkably with increase in solution temperature or with decrease in stress level. The corrosion fatigue life and the crack propagation rate at 303.deg.K show the similar behaviors with those at 318.deg.K, which is assumed to be caused by concentration polarization phenamena. The number and the lengths of microcracks increase with increase in solution temperature, so they lead to the decrease in corrosion fatigue life.