Compressive strength in concrete has many affecting parameters and varies with exposure conditions. Although the concrete has same mix proportions, its properties are different with exposure conditions, and sea-environment can be classified into three groups such as tidal, atmospheric, and sea submerged region particularly. In this study, compressive strength was evaluated on 7-year-cured concrete and the results from previous equations (KDS, ACI, CEB, and JSCE) were compared with them. Furthermore the strength and carbonation progress were evaluated on concrete cured for 7 years exposed to three different sea environment. Three levels of w/c (water to cement) ratio (0.37, 0.42, and 0.47) and three different exposure conditions (tidal, atmospheric, and submerged) were considered. The results from wet-cured condition are all higher than those from the previously proposed equations, and the results from different sea exposure conditions (tidal, atmospheric, and submerged region) were lower than those from wet-cured condition. A reduction of strength was evaluated with increasing w/c ratio and the minimum strength was evaluated in the sea-submerged conditions. Several experimental constants applicable to the previous equations were obtained from regression analysis since the strength change with w/c ratios were not considered in those equations. Regarding carbonation depth with different exposure conditions, higher carbonation depth clearly was observed with increasing w/c ratios, and evaluated in the order of atmospheric, submerged, and tidal region. Considerable carbonation depth was observed in submerged and tidal region due to sulfate ion and dissloved carbon dioxide as well.

• Journal of the Korea Concrete Institute
• /
• v.17 no.2 s.86
• /
• pp.179-189
• /
• 2005

Corrosion of steel due to chloride attack is a major concern in reinforced concrete structures which are located in the marine environments. In this case, Fick's 2nd law has been used for the prediction of chloride diffusion related with service life of concrete structures. However, those studies were confined mostly to the single deterioration due to chloride only, although actual environment is rather of combined type. The purpose of the present study is, therefore, to explore the influences of carbonation to chloride attack in concrete structures and to investigate the validity of Fick's law to chloride attack combined carbonation. The test results indicate that the chloride ion profiles from Fick's law using the diffusion coefficient of immersion tests is not reflected the effect of separation of chloride ions in carbonation region but valid in sound region in case of combined action. On the other hand, the chloride ion profiles from Fick's law using the diffusion coefficient of Tang and Nilsson's method coincide with test results under dry-wet condition but not under combined condition. The results of present study may Imply that the new method for the measurement of diffusion coefficient is required to predict the chloride ion profiles in case of combined action at early.

• Korean Journal of Mineralogy and Petrology
• /
• v.33 no.4
• /
• pp.439-450
• /
• 2020

Global warming caused by the emission of greenhouse gases into the atmosphere is being treated as a major problem for the human life, and mineral carbonation is drawing attention as one of many countermeasures against this situation. In this study, mineral carbonation experiments using autoclaved lightweight concrete (ALC) were performed under various conditions to determine its potential as a carbonation material. ALC can be regarded as a promising material for carbonation because it contains about 27 wt.% of CaO, a major component of mineral carbonation. The CaCO3 content produced as a result of the carbonation of ALC calculated on the assumption that all of the CaO content participates in mineral carbonation is about 40 wt.%. The optimum conditions for the mineral carbonation reaction from ALC are the solid-liquid ratio of 0.01 and the reaction time of 180 minutes when calcite is considered as a single product, or 0.06 and 180 minutes when mixture of calcite and vaterite can be considered. The coexistence of vaterite with calcite at solid-liquid ratio of 0.06 or higher was interpreted to be the case where vaterite formed in the later stage and did not change to calcite until the reaction was completed.

• 레미콘
• /
• no.1 s.74
• /
• pp.25-32
• /
• 2003

• Magazine of the Korea Concrete Institute
• /
• v.18 no.4 s.93
• /
• pp.24-31
• /
• 2006

• Magazine of the Korea Concrete Institute
• /
• v.22 no.4
• /
• pp.36-38
• /
• 2010

• Magazine of the Korea Concrete Institute
• /
• v.27 no.5
• /
• pp.21-24
• /
• 2015

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.24 no.4
• /
• pp.18-25
• /
• 2020

The purpose of this study is to investigate the mechanical and carbon-capture properties of foam concrete containing stainless steel argon oxygen decarbonization(AOD) slag. AOD slag was used as a binder, and foam concrete having a foaming ratio of 69 ± 0.5 % and a slurry density of 573.2 to 578.6 kg / ㎥ was produced. In order to examine the effect of carbonation, blended specimen was cured by two types : normal curing and CO₂ curing. As a result of the experiment, the specimens incorporating AOD slag showed higher compressive strength than Plain after CO₂ curing. According to the analysis of the image of foam concrete, it was confirmed that the ST30 has a lower total pore volume and average pore size than plain, resulting in high compressive strength. The SEM analysis confirmed the formation of calcite by carbonation of AOD slag. Through the thermogravimetric analysis, the increase of CO₂ uptake was confirmed by the incorporation of AOD slag. Foam concrete has a higher porosity than normal concrete, so it is expected that carbon-capture performance can be improved by using a AOD slag.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.7 no.2
• /
• pp.151-157
• /
• 2019

Concrete bridge constructed in metropolitan cities has different superstructure members like slabs and girders, and their carbonation depths vary with different design strengths and local environmental conditions. In this paper, 54 concrete cores were obtained from prestressed concrete girders and the related tests were performed for compressive strength and carbonation depth measurement. Referred to the specified compressive strength of 24MPa for slab and 35MPa for I-type girder, the strengths from cores were evaluated to 82% and 73% of design grade, respectively. For carbonation depth, the slab member showed 30.6mm of average with 32.9% of COV(Coefficient of Variation) and I-type girder showed 16.7~17.0mm with 22.8~33.6 of COV. The I-type girder has much lower carbonation depth and COV compared to slab member, however it has higher COV than column structures.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.33 no.3
• /
• pp.909-916
• /
• 2013

Concrete containing lightly burnt MgO has long term expansibility. It also could compensate for the thermal shrinkage of mass concrete, because the hydration of MgO proceeds at a slow pace to long-term age. Thus, lightly burnt MgO has been applied to the construction of mass concrete such as dams. Recently, the expansion characteristics of MgO concrete with fly ash that could be applied to mass concrete for the reduction of hydration heat have been studied and however, limited studies on its durability. This study investigates the long-term durability characteristics of fly ash concrete with lightly burnt MgO. The durability tests on carbonation, freezing-thawing, diffusion of chloride, and resistance to sulfate attack were carried out for MgO concrete with curing for 360 days in submerged condition with different temperature of 20 and $50^{\circ}C$. The results reveal that MgO concrete shows a greater resistance of carbonation, diffusion of chloride, and resistance to sulfate attack. On the other hand the resistance of freezing-thawing was little influenced by MgO powder.