In order to investigate the possibility of impact punching in brittle materials, an experimental setup was developed. In the setup, a long bar as a punch was used to apply the impact load to the specimen plate and measure the applied impact force during the impact punching process. Impact punching tests with various shape of punches were performed in soda-lime glass and silicon wafer under a different level of contact pressure. The damage appearance after the impact punching was examined according to the applied contact pressure. The minimum contact pressure required for a complete punching in glass specimens without development of radial cracks around the punched hole was sought at each condition. The minimum contact pressure increased with increasing the thickness of specimens and decreasing the end radius of punches. The profile of impact forces was measured during the impact punching experiment, and it could explain well the behavior of the punching process in brittle material plates. The measured impact force increased with increasing the contact pressure applied to the plates.

• 대한기계학회논문집A
• /
• 제25권5호
• /
• pp.899-905
• /
• 2001

The damage behavior of soda-lime glass was studied due to a steel ball of 1mm and 2mm at oblique impact test. The thickness of glass specimen were 3mm and 5mm and oblique degrees of impact were 90$^{\circ}$,70$^{\circ}$ and 50$^{\circ}$. After the steel ball impact test, the crack patterns were investigated using a stereo-microscope. In addition, the finite element method was performed to analyze the stresses distribution and variation in the oblique impacted glass by steel ball. As a result of the impact test, the crack length of 90$^{\circ}$impacted glass was the largest and that of 50$^{\circ}$impacted glass was the smallest. In particular, as the impact velocity and diameter of the steel ball increased, the difference of crack length was prominent. The finite element analysis showed the maximum principle stresses distribution in contact area of glass specimen. The result of analysis was accorded with the crack growth behavior by the oblique impact test.