• 한국수소및신에너지학회논문집
• /
• 제15권1호
• /
• pp.46-53
• /
• 2004

Redox characteristics of cobalt oxide-based oxygen carriers were tested for chemical-looping combustion. Cobalt oxide was chosen as active metal oxide and $CoAl_2O_4$ was compared with YSZ(yttria-stabilized zirconia) as a binder. Cobalt oxide/$CoAl_2O_4$ was prepared by sol-gel method. Hydrogen fuel was reacted with metal oxide and then the reduced metal was successively oxidized by air. The effects of reaction temperature were measured and the regenerabilies during 10 cycles were examined by a TGA. In regenerability of cobalt oxide/YSZ and cobalt oxide/$CoAl_2O_4$, after they showed above 90% conversion in first reduction, they were stabilized in about 70-75% conversion. From reaction rate constant obtained, the activation energies of cobalt oxide/YSZ in oxidation and reduction were 51.47kJ/mol and 7.71kJ/mol respectively.

• 청정기술
• /
• 제21권1호
• /
• pp.68-75
• /
• 2015

본 연구에서는 높은 열전도성을 갖는 금속-세라믹 core-shell 구조의 CoAl₂O₄@Al 복합체를 Al 금속의 수열반응을 통하여 합성하고, 이를 Rh 촉매의 담지체로 적용하여 구조적, 촉매화학적 특성을 분석하였다. Rh/CoAl₂O₄@Al (3 wt% Rh) 촉매는 단순침적법(incipient wetness impregnation)으로 제조하였고, 특성의 비교평가를 위하여 공침법(co-precipitation)으로 합성한 CoAl₂O₄를 담지체로 하여 Rh/CoAl₂O₄ (3 wt% Rh) 촉매를 단순침적법으로 제조하였다. 이들 촉매들은 N₂ 흡착, XRD, 전자 주사현미경, temperature programmed reduction (TPR), CO 화학흡착 분석을 통해서 그 특성을 분석하였고, 글리세롤 수증기 개질 반응(550 ℃)을 통한 수소전환반응에 적용하여 촉매적 특성을 평가하고 분석하였다. 글리세롤 수증기 개질반응에 대하여 Rh/CoAl₂O₄@Al 촉매는 Rh/CoAl₂O₄ 촉매에 비하여 약 2.8배 높은 글리세롤 전환 turnover frequency (TOF)를 보여주었고, 이는 높은 열전도성을 갖는 금속-세라믹 복합체를 통한 원활한 반응열의 전달에 기인한 것으로 분석되었다. CoAl₂O₄@Al 및 CoAl₂O₄ 담지체에서도 환원에 의하여 노출된 일부 Co 금속에 의한 촉매적 활성이 관찰되었는데, Rh/CoAl₂O₄@Al과 Rh/CoAl₂O₄ 촉매에서와 마찬가지로 core-shell 구조체인 CoAl₂O₄@Al이 CoAl₂O₄ 보다 높은 촉매적 활성을 보였다. 그러나, 이들 촉매는 글리세롤 개질반응에서 비교적 높은 비활성화를 보여주었고 이는 촉매표면의 탄소침적(coking)에 기인한 것으로 판명되었다.