• Proceedings of the Korean Society For Composite Materials Conference
• /
• 1999.11a
• /
• pp.118-123
• /
• 1999

저밀도 폐놀계 탄소/탄소 복합재의 층간전단강도를 개선하기 위해 흑연분말, 카본블랙, 카본매트, 단섬유 등의 첨가제를 사용하였다. 카본매트와 단섬유를 첨가한 경우, 수지의 부족에 의한 층간접착력의 약화를 가져왔으며, 카본블랙을 첨가한 경우에도 큰 효과를 나타내지 못했다. 흑연을 첨가했을 때 약 30%의 층간강도 개선을 가져왔으며 특히 9 vol.%의 첨가량에 대해서 가장 큰 효과를 보였다.

• Composites Research
• /
• v.30 no.1
• /
• pp.71-76
• /
• 2017

The purpose of this study was to predict the long-term performance using the interlaminar shear strength of carbon fiber/epoxy composites exposed to environmental factors. Interlaminar shear specimens, manufactured by the filament winding method, were exposed to the conditions of drying at $50^{\circ}C$, $70^{\circ}C$, and $100^{\circ}C$ and of immersion at $25^{\circ}C$, $50^{\circ}C$, and $70^{\circ}C$ for up to 3000 hours, respectively. According to the results, the interlaminar shear strength did not vary significantly with the exposure time for the drying at $50^{\circ}C$ and $70^{\circ}C$, but it increased somewhat for the drying at $100^{\circ}C$ due to the post curing as the exposure time increased. The interlaminar shear strength of the specimens exposed to the immersion at $25^{\circ}C$ did not change significantly at the beginning of exposure, but it decreased with the exposure time and the degree of decrease increased as the environmental temperature increased. The linear regression equations for the environmental temperatures were obtained from the interlaminar shear strength of the specimens exposed to the immersion for up to 3000 hours. Using these linear regression equations, the interlaminar shear strength was estimated to be within 5.5% of the measured value at $25^{\circ}C$ and $50^{\circ}C$, and 2.3% of the measured value at $70^{\circ}C$. Therefore, the proposed performance prediction procedures can predict well the long-term interlaminar shear strength of carbon fiber/epoxy composites exposed to environmental factors.

• Composites Research
• /
• v.24 no.5
• /
• pp.34-38
• /
• 2011

Carbon nanotubes (CNTs) have been widely investigated as reinforcements of CNT/polymer nanocomposites to enhance mechanical and electrical properties of polymer matrices since their discovery in the early 90's. Furthermore, the number of studies about incorporating CNTs into carbon fiber reinforced plastics (CFRP) to reinforce their polymer matrices is increasing recently. In this study, single-walled carbon nanotubes (SWNT) were dispersed in epoxy with 0.2 wt.% and 0.5 wt.%. Then, the SWNT/epoxy mixtures were processed to carbon fiber composites by a vacuum assisted resin transfer molding (VARTM) and a wet lay up method. The processed composite samples were tested for the interlaminar shear strength (ILSS). The relationship between the interlaminar shear strengths and processing, and the reinforcement mechanism of carbon nanotubes were investigated. CNT/epoxy nanocomposite specimens showed the increased tensile properties. However, the ILSS of carbon fiber composites was not enhanced by reinforcing the matrix with CNTs because of processing issues caused by increased viscosity of the matrix due to addition of CNTs particularly for a VARTM method.

• Composites Research
• /
• v.28 no.3
• /
• pp.94-98
• /
• 2015

This paper reports the effects of nickel film interleaves on the interlaminar shear strength(ILSS) of carbon fiber reinforced epoxy composites(CFRPs). A nickel thin film was deposited onto the prepreg by radio frequency(RF) sputtering at room temperature. The ILSS of the nickel film interleaved hybrid composites was increased compared to that of the composites without interleaves. To understand the mechanism of enhancement of the ILSS, the fracture surface of the tested specimens was examined by scanning electron microscopy(SEM). The metal interleaves were acted as a reinforcement for the matrix rich interface and the shear property of their composites improved by enhancing the resistance to matrix cracking.

• Composites Research
• /
• v.35 no.1
• /
• pp.13-17
• /
• 2022

RADAR Absorbing Structure (RAS), one of stealth technologies, is a multifunctional composite that is capable of supporting load and absorbing electromagnetic waves. In order to supplement the shortcomings of the existing RAS, a hybrid RAS in which the short carbon fiber layers were inserted has been proposed. However, the inserted short carbon fiber layers may affect the mechanical properties of the structure. Therefore, this study measured the interlaminar shear strength (ILSS) of the hybrid RAS with the inserted short carbon fiber layer. The ILSS of hybrid composite with different areal densities of the short carbon fiber layer was measured to investigate the effect of changes in the areal density of the short carbon fiber layer on the ILSS of the structure. In addition, the ILSS of the 4 kinds of the hybrid RAS were measured and compared with the ILSS of glass/epoxy. As a result of the measurement, it was confirmed that the short carbon fiber layer did not significantly affect the ILSS of the hybrid composite and the hybrid RAS.

• Journal of Adhesion and Interface
• /
• v.5 no.1
• /
• pp.21-28
• /
• 2004

In this work, glass fiber/nylon 6 and woven glass fiber/nylon 6 composites have been fabricated using glass fiber reinforcements sized with 3-chloropropyltrimethoxysilane(CTMS) having a chloropropyl organo-functional group in the molecular chain end. The interfacial shear strength of glass fiber/nylon 6 composite was measured using a single fiber microbonding test and the interlaminar shear strength and the storage modulus of woven glass fabric/nylon 6 composites were measured using a short-warn shear test and a dynamic mechanical analysis, respectively, informing the effect of the concentration of CTMS on the properties. With increasing CTMS concentration, the interfacial properties of the composites were improved. The results on the interfacial shear strength, interlaminar shear strength, interlaminar failure pattern, and storage modulus with varying the CTMS concentration agree with each other.

• Applied Chemistry for Engineering
• /
• v.10 no.3
• /
• pp.336-342
• /
• 1999

Various surface treatment techniques can be applied onto the surface of carbon fibers to increase interlaminar shear strength (ILSS). In a commerciaI treatment, first, surface of carbon fiber was oxidized, after that, a sizing agent was coated to improve handleability and adhesion to the matrix. Carbon fiber reinforced composites (CFRC) which is made of these fibers show excellent ILSS but show low vaIues of impact strength In this study, reactive and ductile interphase was introduced between fiber and matrix to increase both the ILSS and impact strength. By using electric conductivity of carbon fibers, flexible polymers which have ionizable group, i.e., MVEMA and EMA, were coated onto the surface (oxidized) of carbon fiber by the technique of electrodeposition. ILSS and impact strength of composites were evaluated according to the surface treatments, i.e., commercial sizing treatment, interphase introduction, and without sizing treatment. Izod impact strength and ILSS of CFRC were simultaneously improved in thc thickness range of $0.08{\sim}0.12{\mu}m$ of MVEMA interphase. Water resistance of the composites was decreased by introducing MVEMA interphase.

• Polymer(Korea)
• /
• v.24 no.6
• /
• pp.845-853
• /
• 2000

The optimum cure cycle and carbonization condition were selected by the DSC and TGA analysis and green bodies were prepared by the method of hot press molding and then carbonized up to 140$0^{\circ}C$. Additives such as graphite powder, carbon black, milled carbon fiber and carbon fiber mat, which were considered to be effective in improving the interlaminar shear strength, were also added to check their effects on the density and porosity of products. Then, their relations with mechanical properties such as ILSS and flexural strength were investigated. The composites added 9 vol% of graphite powder showed the greatest values of ILSS and flexural strength. Otherwise, in case of adding carbon black, the composites showed the slight improvement of ILSS at its contents of 3 vol% but the flexural strength was decreased. When milled carbon fiber and carbon fiber mat were added, the lack of resin and the heat shrinkage during the carbonization caused the delamination, resulting in decreasing the density, ILSS and flexural strength.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2000.11a
• /
• pp.88-91
• /
• 2000

흑연분말, 카본블랙, 탄소섬유분말을 첨가제로 한 저밀도 2-D 탄소/탄소 복합재의 밀도 및 기 기공도에 피치는 영향과 ILSS, 굽힘강도 및 충격에너지와 같은 기계적 물성과의 상관관계에 대하여 연구하였다. 흑연분말을 약 9 vol.% 첨가한 경우 가장 큰 ILSS값과 굽힘강도 및 충격에너지 흡수 거동을 나타내었는데, 특히 흑연의 함량이 증가함에 따라 puncture mode로의 충격 거동을 나타내 띠 많은 충격에너지를 흡수하였고, 인성이 상당히 증가하였다 카본블랙이 첨가된 경우에는, 약 3 vol.%에서 ILSS 값이 증가하였으나 큰 개선을 보이지 못하였으며, 굽힘강도는 감소하였다. 탄소섬유분말의 첨가량이 증가함에 따라 층간분리에 의해 밀도가 현저히 감소하여 ILSS 및 굽힘강도의 감소를 보였다.

• Composites Research
• /
• v.17 no.1
• /
• pp.29-37
• /
• 2004

Honeycomb sandwich composite(HSC) structures have been widely used in aircraft and military industry owing to their light weight and high stiffness. Mechanical properties of honeycomb core materials are needed for accurate analysis of the sandwich composites. In this study. theoretical formula for effective elastic modulus and Poisson's ratio of honeycomb core materials was established using an energy method considering the bending, axial and shear deformations of honeycomb core walls. Finite-element analysis results obtained by using commercial FEA code, ABAQUS 6.3 were comparable to the theoretical ones. In addition, we performed tensile test of HSC plates and analyzed deformation behaviors and interlaminar stresses through its FEA simulation. An increased shear stress along the interface between surface and honeycomb core layers was shown to be the main reason for interfacial delamination in HSC plate under tensile loading.