• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.28 no.1
• /
• pp.55-62
• /
• 2004

Although the previous researches evaluated the fatigue behavior of glass fiber/epoxy laminates using the traditional fracture mechanism, their researches were not sufficient to do it: the damage zone of glass fiber/epoxy laminates was occurred at the delamination zone instead of the crack-metallic damages. Thus, previous researches were not applicable to the fatigue behavior of glass fiber/epoxy laminates. The major purpose of this study was to evaluate delamination behavior using the relationship between crack length and delamination width in hybrid composite material such as Al/GFRP laminate. The details of investigation were as follows : 1) Relationship between crack length and delamination width, 2) Relationship between delamination aspect ratio and delamination area rate, 3) Variation of delamination growth rate is attendant on delamination shape factors. The test results indicated that the delamination growth rate depends on delamination width delamination aspect ratio and delamination shape factors.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2003.04a
• /
• pp.113-116
• /
• 2003

The investigation of delamination growth behavior in hybrid composite material such as FRMLs should be considered delamination growth rate, dA_D/da$ using the delamination shape factor, $f_S$ instead of traditional fracture mechanics parameters. The main objective of this study is to evaluate the relationship between delamination element (i. e. delamination width, b, delamination contour, c, delamination shape factor, $f_S$ and delamination growth rate, dA_D/da$) and delamination growth in FRMLs under cyclic bending moment. The delamination shape formed along the fatigue crack between aluminum layer and glass fiber/epoxy layer are measured by scanning method. The details of study are as follow : ⅰ) Relationship between crack length, a and delamination width, b. ⅱ) Variation of delamination growth rate, dA_D/da$ was attendant on delamination shape factors, $f_{S1}$, $f_{S2}$, $f_{S3}$. The test result indicated the delamination growth behavior depends in delamination element such as delamination width, b, delamination shape factors, $f_{S1}$, $f_{S2}$, $f_{S3}$.

• Composites Research
• /
• v.14 no.1
• /
• pp.1-7
• /
• 2001

In this study, damage evaluation of glass fiber reinforced thermoplastic composites was investigated with acoustic emission method. Specimens of 1.7mm thickness laminate were made from PET and 7 layers o171ass fabrics. Notch and impact loading were added to the specimen and normal tensile test and tensile test with the dead load were carried out. AE signal was measured as the functions of notch ratio to the width0 and impact energy in order to find out the correlation between fracture mode and AE parameters. The result has shown that low amplitude of AE signal was due to the microcrack of matrix and its growth, whereas the amplitude in the mid range was the response to the delamination and interfacial separation. In the range of high amplitude above 90dB. the fracture of glass fabric was found. Tensile strength decreased with increasing notch ratio to the width and impact energy because of tile effect or delamination, the cracking of matrix and stress concentration. In proportion to the size of damaged area. AE signal showed its wider range of frequency and energy as well as increased number of hits.