• 한국기계기술학회지
• /
• 제13권4호
• /
• pp.125-130
• /
• 2011

Technological mode progress demands the use of materials at high temperature and pressure. Constant load creep tests have been carried out over the range of stresses at high temperatures. One of the most critical factors in considering such applications as the most critical one is the creep behavior. In order to investigate the creep behavior in this study, the stress exponents during creep were determined over the temperature range of $275^{\circ}C$ to $325^{\circ}C$ and the stress range of 36MPa to 72MPa. The applicability of modified Monkman-Grant relationship was also discussed.

• 한국정밀공학회지
• /
• 제30권8호
• /
• pp.809-814
• /
• 2013

The relationship between the small-punch creep test and the conventional creep test was investigated experimentally using a method similar to that of the Monkman-Grant relationship. Uniaxial and small-punch creep rupture tests were carried out on 9Cr-2W ferritic steel (Commercial Grade 92 steel: X10CrWMoVNb 9-2) at elevated temperatures. From the relation derived in the same manner as the Monkman-Grant relation, a correlation between the displacement rate in response to the small-punch creep test and the strain rate in the uniaxial creep test was found, and the creep life was calculated using this relation. Furthermore, the failure modes of the small punch creep test specimens were investigated to show that the fracture was caused by creep.

• 한국지반공학회지:지반
• /
• 제9권4호
• /
• pp.55-64
• /
• 1993

이방압밀이 비배수크리프파괴거동에 미치는 영향을 연구하기 위하여 4가지의 압밀응력비(a:In'/clc': 1.0, 0.7, 0.5, 0.4)로서 정규압밀시킨 점토시료에 대해서 비배수크리프시험을 수행하였다. 어떤 최소변형률속도에 이르는 경과시간은 압밀응력비의 감소에 따라 줄어들고 이 최소변형률속도에 대한 파괴시간도 감소된다. Finn and Shead(1.1의 제안식에 의해서 구한 상한항복강도는 압밀응력비의 크기에 관계없이 크리프강도와 잘 일치하며 평균구속응력으로서 정규화한 상한항복 강도는 압밀응력비가 증가할수록 감소한다.

• 비파괴검사학회지
• /
• 제24권1호
• /
• pp.29-37
• /
• 2004

22Cr-5Ni 2상 스테인리스강의 합금원소 중 몰리브덴(Mo) 원소를 텅스텐(W)으로 치환하여 크리프거동에 미치는 영향을 조사하였다. 그리프시험은 $600^{\circ}C$와 $650^{\circ}C$의 온도에서 실시하였다. $650^{\circ}C$ 크리프 시에는 취약한 금속간화합물인 ${\sigma}$상이 석출하였으며 이것은 크리프수명을 급격히 감소시키는 역할을 하였다. Mo에 대한 W원소의 치환은 일반적으로 ${\sigma}$상의 석출을 지연시킨다고 알려져 있으나, 2wt.%까지 W 치환을 실시한 본 연구범위에서는 크리프 수명 및 최소 크리프속도에 뚜렷한 영향을 미치지 못하였다. 크리프손상의 정도를 평가하기 위하여 크리프시편에 대한 초음파검사를 실시하였다 크리프온도 $600^{\circ}C$에서는 크리프시편의 수명이 증가함에 따라 음속이 비례적으로 증가하였으나 $650^{\circ}C$에서는 반대로 감소하였다.

• 터널과지하공간
• /
• 제19권6호
• /
• pp.558-566
• /
• 2009

암석의 시간 의존적 거동은 기본적인 역학적 특성으로서 시간 의존적으로 거동을 분석하여 암반구조물의 파괴시간을 예측하는 것은 매우 중요하다. Voight가 제안한 재료 파괴 예측식($\ddot{\Omega}=A\dot{\Omega}^\alpha$, 여기서 $\Omega$는 변형률이나 변위와 같은 측정 가능한 물리량이고 A & $\alpha$는 상수이다)을 이용하여 터널, 사면 및 실내 크리프 시험으로부터 측정된 변위나 변형률로부터 파괴시간을 예측하고자 하였다. Voight식을 1차 및 2차 적분하여 구한 변위속도 및 변위식에 비선형최소자승법을 적용하여 A & $\alpha$를 구하였으며 이들 상수는 파괴시간을 예측하는데 사용되었다. 예측된 파괴시간은 실제 파괴시간과 잘 일치하는 것으로 나타났다. 크리프 변형률과 변형률속도에 선형역속도법을 적용하여 구한 예측 파괴시간은 변형률과 변형률속도를 이용하여 구한 파괴시간보다 오차가 큰 것으로 나타났다.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2003년도 춘계학술대회
• /
• pp.352-357
• /
• 2003

Creep tests for Titan were carned out using constant-load at $600^{\circ}C$, $650^{\circ}C$ and $700^{\circ}C$. Material constants necessary to predict creep life were acquired from the experimental creep data. And the applicability of Monkman-Grant(M-G) and modified M-G relationships was discussed. It was discovered the log-log plot of M-G relationships between the rupure time(tr) and he minimum creep rate(${\varepsilon}_m$) was conditional on test temperatures. The slop of m was 2.75 at $600^{\circ}C$ and m was 1.92 at $700^{\circ}C$. However; the log-log plot of modified M-G relationships between $t_r/\varepsilon_r$ and $\varepsilon_m$ was indpendent on stresses and temperatures. That is the slop of m' was almost 3.90 in all the data. Thus, change M-G relationships to creep life prediction could be vtilized more reasonably than that of M-G relationships for type Titan. It was divided that the constant slopes never theless of temperatures of practical stresses in the modified relationship were due to an intergranular break grown by wedge-type cauities.

• 마이크로전자및패키징학회지
• /
• 제10권3호
• /
• pp.29-35
• /
• 2003

SnAg, SnAgCu, SnCu 무연솔더합금을 주조 상태에서 냉간압연한 후 열적으로 안정화한 시편 (TS)과, 실제 솔더 범프와 유사한 미세구조의 수냉에 급속 냉각(WQ)된 시편 두가지를 $100^{\circ}C$에서 크리프 실험을 행하였다. 급속냉각한 시편의 냉각속도는 140-150 K/sec로 primary $\beta-Sn$ 크기가 TS 시편보다 5∼10배 정도 작았으며, 기지내 primary $\beta-Sn$이 차지하는 분율은 증가하였다. 반면에 공정상 내의 $Ag_3Sn$상의 크기는 더 작아졌다. 크리프 실험 결과 WQ 시편의 최소크리프 변형율 속도($\{beta}_{min}$)가 TS 보다 약 $10^2$배 정도 작았으며. 더 큰 파괴시간을 보였다. TS-SnAg의 크리프파괴는 $Ag_3Sn$ 또는 $Cu_6Sn_5$에서의 공공의 핵생성, power-law 크리프에 의한 공공의 성장, 그리고 크리프 공공의 상호 연결로 일어났으며, WQ-SnAgCu는 시편이 두께가 얇아 네킹에 의해 파괴가 일어났다.

• 대한기계학회논문집A
• /
• 제24권9호
• /
• pp.2326-2333
• /
• 2000

Creep tests for type 316L(N) stainless steel were carried out using constant-load creep machines at 55$0^{\circ}C$, 575$^{\circ}C$ and $600^{\circ}C$. Material constants necessary to predict creep rupture time were obtained from the experimental creep data. And the applicability of Monkman-Grant(M-G) and modified M-G relationships was discussed. The log-log plot of M-G relationship between the rupture time($t_r$,) and the minimum creep rate ($ $\varepsilon$ _m$) was dependent on test temperatures. The slope of m was 1,05 at 55$0^{\circ}C$ and m was 1.30 at $600^{\circ}C$. On the other hand, the log-log plot of modified M-G relationship between $t_r/$\varepsilon$_r$, and $ $\varepsilon$ _m$ was independent on stresses and temperatures. That is, the slope of m＇ was approximately 1.35 in all the data. Thus, modified M-G relationship for creep life prediction could be utilized more reasonably than that of M-G relationship for type 316L(N) stainless steel. It was analyzed that the constant slopes regardless of temperatures or applied stresses in the modified relationship were due to an intergranular fracture grown by wedge-type cavities.

• 터널과지하공간
• /
• 제20권2호
• /
• pp.97-104
• /
• 2010

가속 크리프 거동을 보이는 재료의 파괴를 설명하기 위하여 재료 파괴식($\ddot{\Omega}=A{(\dot{\Omega})}^\alpha$, $\Omega$는 변위와 같은 측정가능한 양을 나타낸다)이 사용된다. 상수 A와 $\alpha$는 주어진 측정 자료를 곡선적합하여 얻는다. 본 연구에서는 재료 파괴식을 이용하여 터널의 파괴시간을 예측하였고, 재료 파괴식을 적용하기 위하여 4가지 곡선적합기법이 사용되었다. 4가지 곡선적합기법 중 로그속도-로그가속도기법, 로그시간-로그속도기법, 역속도법은 선형최소자승법을 이용하고 비선형최소자승기법은 Levenberg-Marquardt 알고리즘을 이용한다. 로그속도-로그가속도기법은 재료 파괴식을 대수형태로 만들어 해석을 하기 때문에 터널의 파괴시간 예측에 재료 파괴식을 적용하는 것이 타당한지에 대한 근거를 제시한다. 로그속도-로그가속도기법에 따른 자료의 상관계수가 0.84로 비교적 높게 나타났기 때문에 재료 파괴식을 터널의 파괴시간 예측에 적용하는 것이 타당하다고 판단된다. 실제 파괴시간과 4가지 곡선적합기법으로부터 얻은 예측 파괴시간을 비교한 결과 로그시간-로그속도기법이 가장 우수한 결과를 보여주는 것으로 나타났다.