• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.11 no.5
• /
• pp.88-92
• /
• 2002

This research is about slurry wear of SM45C and SUS304, which using standard sand and KUM river sand. The results are as follows ; 1. Mass loss rates of both standard sand and KUM river sand were linearly increased as increasement of time and velocity. 2. The average diameter of sand from relatively, less wear rate and portion of larger particles. 3. Wear resistance was linear with time and velocity of liquid jet regardless of type of sand. Also, it was able to evaluate with the formula, $HV^2$/E calibrated with n, the velocity index. 4. The wear surface in liquid jet experiment was smooth. The maximum wear depth was observed at the location 2~4mm apart from the center in the condition of $90^{\circ}$ of collision angle 6mm of nozzle diameter, and 20mm of collision distance. The sectional shape in radial appeared as 'W'shape.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2001.04a
• /
• pp.798-801
• /
• 2001

This research is about slurry wear of SM45C and SUS304, which using standard sand and KUM river sand. The results are as follows ; 1. Mass loss rates of both standard sand and KUM river sand were linearly increased as increasement of time and velocity. 2. The average diameter of sand from relatively, less wear rate and portion of larger particles. 3. Wear resistance was linear with time and velocity of liquid jet regardless of type of sand. Also it was able to evaluate with the formula, HV2/E calibrated with n, the velocity index. 4. The wear surface in liquid jet experiment was smooth. The maximum wear depth was observed at the location, 2~4mm apart from the center in the condition of 90$^{\circ}$of collision angle 6mm of nozzle diameter, and 20mm of collision distance. The sectional shape in radial appeared as 'W' shape.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.29 no.2
• /
• pp.217-225
• /
• 2002

When we use the flowable resin on the primary molars for quick handling, one of the most important property is the wear resistance. This study was performed to compare the wear resistance characteristics of four flowable composite resins [Arabesk flow (group 1), Tetric flow (group 2), Aeliteflow (group 3), Filtek flow (group 4)] to that of one control composite resin [Z100 (group 5)]. Specimen discs(n=10), 10mm wide and 2mm thick, were stored in distilled water at $37^{\circ}C$ for 7 days prior to testing. The specimens were subjected to 50,000 strokes at 2 Hz on the MTS system. During the test, the following parameters were maintained: the lateral excursion at 0.4mm, occlusal force at 2-100N with a force profile in the form of a half sine wave. The measurements of volume loss, depth of wear, and Vicker's hardness number of composite resins, and SEM observations of the polished and abraded surfaces were established. One-way ANOVA and Scheffe's multiple comparison test were employed to detect statistically significant differences among the flowable composite resin groups and the control composite group at P<.05. The following results were obtained: 1. Group 3 showed the least volume loss, while group 4 showed the greatest. The mean volume loss increased in the following order: group 3

• Journal of the korean academy of Pediatric Dentistry
• /
• v.31 no.4
• /
• pp.685-695
• /
• 2004

The aim of this study was to evaluate the resistance to degradation and to compare the wear resistance characteristics of four composite resins in an alkaline solution. The resistance to degradation was evaluated on the basis of mass loss(%), degradation depth(${\mu}m$), Si loss(ppm) and wear depth. The brands studied were Heliomolar flow, Filtek supreme, Point4, Tetric flow. The results were as follows: 1. The sequence of the mass loss was in descending order by Heliomolar flow, Filtek supreme, Point4, Tetric flow. There was significant differences among the materials except Heliomolar flow and Filtek supreme. 2. The sequence of the degree of degradation layer depth was in descending order by Filtek supreme, Heliomolar flow, Tetric flow, Point4. There were significant differences among the materials except Heliomolar flow and Tetric flow. 3. The sequence of Si loss was in descending order by Filtek supreme, Heliomolar flow, Point4, Tetric flow. There were significant differences among the materials except Point 4 and Tetric flow. 4. The sequence of maximum wear depth was in descending order by Heliomolar flow, Point4, Fillet supreme, Tetric flow and there was increasing wear depth on soaking in 0.1N NaOH solution. 5. When observed with SEM, destruction of bonding between matrix and filler was observed and when observed with CLSM, the depth of degradation layer of specimen surface was observed. There results indicate that wear and hydrolytic degradation could be considered to be evaluation factors of composite resins.