• Applied Chemistry for Engineering
• /
• v.5 no.4
• /
• pp.722-730
• /
• 1994

The effects of antioxidant and carbon black on weatherability of crosslinked polythylene(XLPE) for electrical insulation were investigated. 16 compositions were prepared in other to determine the weathering resistance. Samples were exposed in xenon-arc lamp Weather-Ometer for 500, 1000, 1500, 2000 hours respectively. Tensile strength, elongation at break, dielectric strength and tan ${\delta}$ were measured to evaluate the weatherability of XLPE. The results indicated that the effect of carbon black was more prominent than antioxidant and synergistic effect, was observed when two additives were mixed.

• Proceedings of the Korean Reliability Society Conference
• /
• 2002.06a
• /
• pp.147-155
• /
• 2002

본 연구에서는 옥외에서 사용하는 소재의 신뢰성 평가(내후성)에 관한 연구를 수행하였는데 국내와 일본의 옥외환경시험장에 시험편을 동시에 폭로하여 기상인자 및 주변환경에 따른 시험편의 특성 변화를 상호 비교ㆍ평가하였고 인공 촉진내후성 시험을 실시하여 옥외내후성과의 상관관계를 관찰하였으며 그 결과는 다음과 같다. 국내 지역의 옥외환경시험장 중에서는 인천 옥외환경시험장에 폭로한 시험편에서 가장 많은 변화를 나타내고 있으며, 일본 지역은 가혹한 기상환경을 나타내는 미야고지마 옥외환경시험장에 폭로한 시험편에서 많은 변화가 나타남을 관찰할 수 있었는데 국내 지역보다는 온도와 습도 등 기상제조건이 더 가혹한 일본 지역의 옥외환경시험장에 폭로한 시험편의 노화가 더 빠르게 진행됨을 관찰하였다.

• Journal of the Mineralogical Society of Korea
• /
• v.32 no.4
• /
• pp.259-271
• /
• 2019

We evaluated mineralogical, physical property and accelerated weather resistance of cinnabar, realgar and orpiment used as cultural heritages and traditional paintings. JB and JS are sample names of cinnabar and JH and UH are sample names of orpiment and Realgar, respectively. As a result of mineralogical property evaluation, Jinsa was identified cinnabar (HgS) and there was no difference in chemical composition according to the grade. UH and JH were confirmed realgar (AsS) and orpiment (As₂S₃), respectively. The polarization characteristics such as shape and color indicate that pigments using our test were natural mineral pigment observed by polarization microscope. Especially, in the case of cinnabar, it is not easy to distinguish between natural mineral pigment and synthetic pigment. But the results of polarization microscope said that cinnabar is natural occurring mineral which have authentic mineral particle and unevenly fracture. As a result of thermal analysis, JH has a higher glass transition temperature and heat stability than UH. After accelerated weather test, cinnabar, realgar and orpiment were striking result in color change because of light degradation. Red color of cinnabar turn into black and the color of realgar and orpiment became brighter than before. JB (meta-cinnabar) is more photosensitivity and faster becoming dark than JB (cinnabar). Finally light transforms realgar (red, As₄S₄) in arsenolite (As₂O₃).

• Journal of Korean Society of Steel Construction
• /
• v.28 no.5
• /
• pp.325-335
• /
• 2016

To predict service life of coating systems registered in Korean specifications for steel bridge coatings, field deterioration evaluation and accelerated weatherproof test were carried out, and deterioration models were drawn through regression analysis for evaluation results. For the coating systems that have not been used in field, regression analyses were carried out for the virtual evaluation results drawn by applying coordination factor to the field evaluation results for chlorinated rubber and urethane topcoat system. Service life prediction results showed that application of thermal sprayed coating (TSC) could extend service life of coatings to more than twice of general coatings.

• Proceedings of the Korean Reliability Society Conference
• /
• 2002.06a
• /
• pp.157-164
• /
• 2002

본 연구에서는 실생활에 응용되는 Chloroprene계 고무에 대하여 30개월 동안 옥외 폭로를 행하였으며 동시에 Xenon-arc Type의 촉진 내후성시험기를 이용하여 그에 따른 내후성의 변화를 평가하였다. 폭로기간에 따른 인장강도와 신장률의 변화를 측정하였고 폭로면의 표면층에 대하여 FT-IR과 SEM을 사용하여 화학적 특성 및 미세구조를 분석하였다. 태양복사와 습도에 노출된 고무의 표면은 매우 짧은 기간에 파괴되었고, 고무 내부에 존재하는 가교제들의 용출을 확인할 수 있었으며, 산소와의 결합으로 내부층보다 고무의 표면에서 더 많은 가수분해와 광분해가 이루어진다는 것을 확인할 수 있었다. 이와 같은 표면층의 변화와 파괴는 고무의 기계적 성질에도 의미 있는 영향을 주었다.

• Journal of Conservation Science
• /
• v.29 no.1
• /
• pp.25-33
• /
• 2013

This study aims to investigate the film performance by physical properties of glue and gelatin in traditional paint(Dancheong). To do this, homemade, commercial glue and gelatin was selected and evaluated water reaction and weatherproof. The result, the highest gel strength, gelatin was better than acrylic acid ester resin, when compared with hygroscopic property and adhesive property. And that was better than in any others, when compared with water-proofing.

• Elastomers and Composites
• /
• v.48 no.2
• /
• pp.167-171
• /
• 2013

Weatherability was examined according to aluminum particle size and its orientation used in PCM(Paint Coated Metal). Substrate delamination was checked by different UV transmission rate with QUV$^{(R)}$ (Q-LAB) equipment that can make accelerated UV irradiation. Film was prepared using three different types of conflake aluminum pastes under a PCM coating process and clearcoat was sprayed. UV transmission test results showed low transmission rate when EKART #790 having the smallest particle size and horizontal orientation was used. From the gloss retention results, gloss retention was highest in EKART #790 and followed by #770, #750.

• Journal of the Korean Applied Science and Technology
• /
• v.32 no.3
• /
• pp.528-535
• /
• 2015

Humanity has tended pursuing beauty. Pearls has been loved by many people for thousands of years as a symbol of wealth and status. Today, Artificial pearl were made using organic pigment due to bright colors and easy coating process. But the new coating technique is required due to low durability, weather resistance and difficulty of luxurious luster expression. This study, nitrocellulose and urethane were used as binder and inorganic pigment were used to expression of colors. Experimental variable of artificial pearl with nitrocellulose and solvent ratio, urethane and curing agent ratio, the amount of pearl number of coating, drying temperature and time, and coating technology was developed. The coated artificial pearl was evaluated with color-difference meter, ultraviolet ray resistance, promotion weathering. Urethane was better than nitrocellulose when compared with weather resistance, acid-alkalinity resistance.

• Proceedings of the Korea Multimedia Society Conference
• /
• 2012.05a
• /
• pp.312-313
• /
• 2012

단청의 열화현상에 대한 연구는 주로 건축재로서의 내구성 향상에 초점을 두고 연구가 진행되고 있으나 본 연구는 가상유적지 재현을 위해 가상 건축물의 사실감을 높이기 위한 방안으로서 열화현상을 분석하고 가시화 하는데 초점을 두었다. 이를 위해 먼저, 전통건축에 나타나는 단청의 열화과정을 인간이 인지하는 색채감의 변화에 초점을 두고 연구를 진행한다. 우리나라 단청에서 사용된 안료를 살펴보고 문화재관리청에서 선정한 무기안료와 유기안료를 중심으로 내후성 시험을 통해 안료의 열화현상을 분석한다. 단청의 열화를 크게 색변과 박리 현상으로 나누어 촉진내후성시험기를 통해 얻어진 결과를 토대로 목조 전통건축의 열화현상을 분석한다.

• Journal of Conservation Science
• /
• v.17 s.17
• /
• pp.19-32
• /
• 2005

The exterior of Korean traditional wooden buildings have been painted with Danchung of painting method using glue and pigments. However because of losing traditional techniques and materials through the period of colonization and industrialization, many problems are occurring today. Especially after several years from painting, occurrence of scalings and flakings in painting layer is a serious problem. To improve weathering resistance of painting layer caused by stress from the difference of swelling and shrinkage between painting layer and wood plate, was examined by weathering tests. The stress is due to the hydrophilic property of wood, mechanical properties(tensile property and stress relaxation) of painting layer, and priming methods by various binders such as glue, acrylic emulsion(Primal AC-3444), acrylic resin(Paraloid B-72). Because stress relaxation of acrylic emulsion of which glasf transition temperature is below room temperature$(7^{\circ}C)$ is high, painting layers with acrylic emulsion generate no scalings and flakings and are in the most durable state in all weathering tests. Priming method which starts from low concentration to high concentration, is more effective to improve durability than other priming methods.