• Journal of the Mineralogical Society of Korea
• /
• v.15 no.4
• /
• pp.293-304
• /
• 2002

Wet purification process for the selective separation of montmorillonite from Gampo 13 and 35 bentonite ores was studied using physical processes such as ultrasonic scrubbing, decantation and centrifugation. Ultrasonic Scrubbing of Gampo 13 and 35 bentonite ores was revealed excellent result at 7 wt.% of slurry density and was almost finished within 30 minutes in the sample of Gampo 13 and 10 minutes in the sample of Gampo 35, respectively After decantation, approximately 52 wt.% from the bentonite of Gampo 13 and 64wt.% from the bentonite of Gampo 35 were recovered as purified products and the CEC was reached up to 119.4 meq/100 g and 124.5 meq/100 g, respectively. Particle separation by centrifugation showed that most of the impurity minerals such as quartz and feldspar were removed within the condition of 1,000 rpm.

• Resources Recycling
• /
• v.32 no.3
• /
• pp.18-25
• /
• 2023

Sericite was ground with or without additives (LiNO₃ or TiO₂) using a planetary mill. The resultant ground products included the average particle size of 2-3 ㎛ (sericite only or sericite+LiNO₃) and 0.5-0.6 ㎛ (sericite+TiO₂) were obtained within 10 minutes of grinding time. respectively. In the grinding of the sericite without any addictive, the particle size initially decreased, but, as grinding time elapsed thereafter, agglomerates were formed and D50 increased over 10 ㎛. In contrast, when the additive was added, the particle size decreased as the grinding time elapsed and any aggregation was relatively not noticeable, compared with the grinding of the sericite only. As a result of measuring the zeta potential for the raw or the ground samples, variation of the zeta potential values according to pH at the early stage of the grinding with the addictives was gentler than that at the final stage of grinding, which showed the relatively similar trend to the pH-zeta potential correlation in grinding of raw sericite. In addition, as a result of the disintegration experiment through ultrasonic excitation, D50 decreased rapidly only until the disintegration time of about 50 minutes.