• Proceedings of the Korea Concrete Institute Conference
• /
• 2002.05a
• /
• pp.355-360
• /
• 2002

The purpose of this study was to remove the excessive air foaming which was produced in mixing the RSLMC(latex-modified concrete with rapid- setting cement) by choosing the best antifoam agent type and the optimized quantity for performance improved RSLMC. A series of RSLMM(latex-modified mortar with rapid-setting cement) experiments were carried out as the basic for RSLMC with the main experimental variables such as antifiamer types(A, B, C, D), antifoamer contents(0, 1, 2, 3%). Air content test and compressive, flexural tests were carried out to measure the improved properties of RSLMM and RSLMC. Chloride ion permeability test was carried out to estimate water permeability resistance. The results of RSLMM showed that the decrease of 50% air content was obtained by admixturing a antifoam agent by 1%. The compressive strength and flexural strength at 3 hours after RSLMC placement were 235kgf/cm$^2$ and 49kgf/cm$^2$, respectively, which exceeded the flexural strength criterion of 45kgf/cm$^2$ in order to open the RSLMC placed to traffic. The chloride permeability using A and C antifoamer at 28 days were below 100 coulombs, which was the permeability rating of negligible according to ASTM.

• Journal of Industrial Technology
• /
• v.25 no.B
• /
• pp.73-80
• /
• 2005

Durability of concrete structures is seriously compromised by cracking at early-age concretes, particularly in high-strength or high-performance concrete structures. Since early-age cracking is influenced by various factors that affect the hydration process, early-age shrinkage and stress/strain development, the behavior at early-age is highly complex and no rational methodologies for its control have yet been established. Concrete structures often present volumetrical changes particularly due to thermal and moisture related shrinkages. Volumetric instability is detrimental to the performance and durability of concrete structures because structural elements are usually restrained. These restrained shrinkages develope tensile stresses which often results in cracking in combination with the low fracture resistance of concrete. Early-age defects in high-performance concrete due to thermal and autogenous deformation shorten the life cycle of concrete structures. Thus, it is necessary to examine the behavior of early-age concrete at the stages of design and construction. The purpose of this study was to propose a shrinkage models of VES-LMC (very-early strength latex-modified concrete) at early-age considering thermal deformation and autogenous shrinkage.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.11a
• /
• pp.269-272
• /
• 2004

After concrete casts, temperature decent and shrinkage bring volume changes of concrete pavement. Microcracking and cracking in concrete pavement are caused by these volume changes. As a result, durability of concrete pavement is deteriorated. Recently, Very-Early Strength Latex Modified concrete(below:VESLMC) from the beginning of High-Way is used as urgent repair material for bridge deck. The advantage of VESLMC is that compressive and flexural strength at 3 hours age are 4.5MPa and 21MPa respectively. It allows the traffic to open in 3 hours. But, this material has the problem which is early-age shrinkage cracking caused by water self-dissipation with rapid hydration reaction and water evaporation with body dry. Unfortunately, until now, the research about early-age shrinkage of VESLMC leaves something to be desired. Therefore, the purpose of this study is to present the early-age shrinkage of VESLMC respect to latex contents and shrinkage ratio to maximum length change that can help field engineers' skill. Latex contents of 0, 5, 10, 15, $20\%$ in standard of same workability in VESLMC are selected by experimental variables. After initial set, shrinkage value was measured with 10mm LVDT for 3 days. The results of maximum shrinkage ratio were 0.019, 0.017, 0.023, $0.027\%$ respectively.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.11 no.3
• /
• pp.1040-1046
• /
• 2010

The main disadvantage of rapid setting concrete is the occurrence of cracking because of fast hydration reaction due to high thermal expansion and shrinkage. However, if the fly ash is used in concrete, it is possible to prevent cracking since the hydration heat can be decreased. Although Very-Early Strength-Latex Modified Concrete(VES-LMC) is an excellent material, occurrence of cracking has been reported because of high hydration heat. In the present study, new method which can apply the fly ash to the VES-LMC was developed. Research for the new method to improve the safety for the cracking was conducted. Safety was confirmed by reducing the shrinkage and hydration heat in the condition of overcoming the low early-age strength. Detailed conclusions are follows. Early-age compressive strength was decreased a little with increase of UFFA content. However, 28-d compressive strength was statistically insignificant regardless of UFFA contents. If the UFFA is replaced 15% to 20% of unit cement weight in concrete, maximum shrinkage can be reduced up to 43% to 47%. Usage of UFFA in VES-LMC guarantees the safety for cracking since it is very effective to control of early-age shrinkage.