• 대한기계학회논문집A
• /
• 제20권11호
• /
• pp.3415-3423
• /
• 1996

The compact tension specimen geometry has been widely used for measuring fatigue crack growth rates at elevated temperature when the fatigue load is under tension/tension condition. However, most of the elevated temperature components which have significant crack growth life experience fatigue load under tension/compression conditions. Thus test techniques are required since the compact tension specimen cannot be used for tension/compression loading. In this paper, a simplified test procedure for measureing fatigue crack growth rates is proposed, which employs a round bar specimen with a small surface crack. Fatigue crack growth rates under tension/ tension loading conditions at elevated temperature were measured according to the proposed procedure and compared with those previously measured by C/(T) specimens. Since both the measured crack growth rates were comparable, the fatigue crack growth rates under tension/ compression load can be reliably measured by the proposed procedure. For monitoring crack depth. DC electric potential method is employed and an optimal probe location and current input conditions were proposed.

• 대한기계학회논문집A
• /
• 제24권3호
• /
• pp.794-802
• /
• 2000

Since the examination of CTOD problem revealed that the discrepancy among CTOD's was a matte., of definition, the relationships among parameters based on different definitions have been studied Particularly, the relationship between $\sigma$BS R-curve based on BS 7448 and R-curve based on the recently introduced $\sigma$5 parameter was investigated in this research. For the comparison, compact tension specimens of used 1Cr-0.5Mo steel, heat treated 1Cr-0.5Mo steel to mimic the new one, A12024-T6, and A12024-T351 were prepared and tested. Consequently, the relationship between $\sigma$5 and $\sigma$BS R-curves for tested materials were established by shifting the rotational center which could determined by rotation factor and ligament size.

• 한국생산제조학회지
• /
• 제6권3호
• /
• pp.65-72
• /
• 1997

The horizontal corrosion fatigue tester has been developed for investigating environmental strength. Using this tester, we investigated about corrosion fatigue caracteristics for A106-Gr B steel weldments in 3.5% synthetic seawater and room temperature. Considered parameter is only frequency of 1, 3 and 5Hz.. and Corrosion fatigue crack length was measured by DC potential difference method. From the results, we could find that the horizontal corrosion fatigue tester could be well applied to estimation of fatigue strength. and, In case of 5Hz., corrosion fatigue crack growth pate of A106-Gr B steel weldment was transgranular, and of 1 and 3Hz. showed that transgranular and interfranular was mixed. Also, Material constants of corrosion fatigue crack growth estimated in each frequency were C=9.33$\times$$10^{-9}$ and m=2.93 in 1Hz., C=9.77$\times$$10^{-10}$ and m=3.47 in 3Hz., C=1.02$\times$$10^{-10}$ and m=4.05 in 5Hz

• 대한기계학회논문집A
• /
• 제25권2호
• /
• pp.220-227
• /
• 2001

The fatigue crack initiation life is studied on automotive tensile-shear spot weldment made from cold rolled carbon steel(SPC) sheet by using DCPDM and local strain approach. It can be found that the fatigue crack initiation behavior in spot weldment can be definitely detected by DCPDM system. To predict the fatigue life of spot weldment, the local stresses and strains at the potential critical region are estimated by approximate method based on Neubers rule and elastic-plastic FEM analysis. A satisfactory correlation between the predicted life obtained from Local strain approach based on Neubers rule and experimental life can be found in spot weldment within a factor of 2.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2001년도 춘계학술대회논문집A
• /
• pp.345-350
• /
• 2001

In order to perform elastic-plastic fracture mechanical analyses, fracture resistance curves for concerned materials are required. 1T-CT specimen was used to obtain fracture resistance curves. But the fracture resistance curve by the 1T-CT specimen was very conservative to evaluate the integrity of the structure. And fracture resistance curve was affected by the specimen geometry and crack plane orientation. The objective of this paper is to be certain the conservativeness of the fracture resistance curve by the 1T-CT specimen and to provide the additional safety margin. For these, the fracture tests using the real pipe specimen and standard 1T-CT specimen test were performed. 4-point bending jig was manufactured for pipe test and direct current potential drop method was used to measure the crack extension and length for pipe test. From the pipe and the 1T-CT specimen test results, it was observed that the J-integral of the 1T-CT specimen test at the crack initiation point was very small compare to that of the pipe specimen test.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2003년도 추계학술대회
• /
• pp.1062-1067
• /
• 2003

In this study, corrosion fatigue characteristics of CF8M and CF8A steel were investigated on the simulated PWR condition(Temp.:$316^{\circ}C$, Pres.: 15:MPa). To make the simulated PWR condition. the special test machine consisted of INSTRON, Autoclave, LOOP and Measurement system was developed. As ${\Delta}K$ is ranged from 11 to $20MPa{\sqrt{m}}$, Crack growth rate of PWR condition is faster than air condition. Above $20MPa{\sqrt{m}}$, the crack growth rate of PWR and air condition is similar. Corrosion fatigue characteristics regardless of the ferrite contents($10{\sim}25wt.%$) is not different. After the test, the fracture surface of specimens was examined. It was difficult to verify the fracture modes such as striation, intergranular crack and cleavage and so on. As the ferrite content of CF8M is increased, the more particles covered fracture surface were peeled.

• 대한기계학회논문집A
• /
• 제25권5호
• /
• pp.772-778
• /
• 2001

In this study, corrosion fatigue characteristics of 12Cr alloy steel were investigated in 3.5wt.% NaCl solution of 150$^{\circ}C$ and 4.5bar. Behavior of corrosion fatigue cracks was measured by the indirect compliance method and compared with the results in distilled water and in air. 1) 12Cr alloy steel was susceptible to temperature. Its susceptibility was increased as the temperature was increased. 2) The crack growth characteristics of 12Cr alloy steel in distilled water were similar to 3.5wt.% NaCl solution. 3) The temperature of solution affects to the crack growth characteristics of 12Cr alloy steel. In corrosion solutions of 4.5bar, 150$^{\circ}C$, fracture surfaces of corrosion fatigue crack growth at a/W=0.3 was showed the trans-granular fracture suface. As the crack grew up, it was changed to inter-granular type. In condition of high temperature, The crack growth behaviors of 12Cr alloy steel were remarkable.

• 대한기계학회논문집A
• /
• 제28권5호
• /
• pp.640-647
• /
• 2004

In order to perform elastic-plastic fracture mechanical analyses, fracture resistance curves for concerned materials are required. The unloading compliance method and the DCPD(Direct Current Potential Drop) method have been widely used for measuring the crack length and the extension for a standard specimen fracture resistance curve test. However it is difficult to apply the unloading compliance method to a real pipe fracture resistance curve test. The objective of this paper is to propose the calibration equation between the normalized crack length and the normalized electric potential, and to apply to pipe fracture experiments. For these, finite element analyses were performed with various current input locations and crack front configurations. Also the 4-point bending jig was manufactured for a pipe test and the DCPD method was used to measure crack extensions and crack lengths for a pipe test. The calculated crack length by the DCPD method agreed with the measured crack length within 5% error.

• 비파괴검사학회지
• /
• 제18권1호
• /
• pp.10-16
• /
• 1998

사용중인 터빈 로터에서 균열이 발견된다면 그 안전성을 평가하기 위해서는 제조 당시의 재료물성 데이터가 아닌 열화된 재료의 물성 및 인성을 사용해야 한다. 본 연구에서는 시험재료로 터빈 로터재로 널리 사용되고 있는 1Cr-1Mo-0.25V강을 사용하였다. 로터강의 경우 발전소에서 실제 사용된 열화재를 종류별로 입수하는 것은 매우 어렵기 때문에 실제로 열화된 재료의 미세조직과 유사한 미세조직을 갖는 시료를 얻기 위해서 실제 사용온도보다 높은 $630^{\circ}C$에서 등온 열화처리하여 열화도가 다른 7종류의 시료를 만들었다. 열화도와 재료의 인성을 비파괴적으로 평가하기 위하여 직류 전위차법을 이용하였으며, 상온에서 전기비저항을 측정하였다. 열화도의 증가에 따라 전기비저항과 재료인성은 일정시간까지는 감소하는 것으로 나타났으며, 전기비저항과 인성과의 상관관계를 만들었다. 따라서 이를 이용하여 비파괴적으로 재료인성을 평가할 수 있는 기초를 마련하였다.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2011년도 추계학술발표대회
• /
• pp.39.1-39.1
• /
• 2011

가압경수로의 압력경계기기는 약 $300^{\circ}C$, 150기압의 고온고압수환경에서 가동되고 있다. 특히 가압기 밀림관은 고온수와, 저온수가 교차하는 부분으로 열성층 형성으로 열적, 기계적 피로 및 수화학환경이 더해진 부식피로 등에 의하여 손상을 받는다. PWR 원전에서 수화학환경은 대표적으로 용존산소(DO) 5ppb, pH 6~8, 용존수소(DH) <30 cc/kg, 온도 $316^{\circ}C$의 환경을 유지하게 된다. 가압기 밀림관에는 오스테나이트계 스테인리스강이 사용되는데, 오스테나이트계 스테인리스강은 고온 수화학환경에 민감한 것으로 알려져 있다. 따라서 오스테나이트계 스테인리강을 공기중에서의 기계적특성 및 피로특성을 향상시키기 위하여 질소를 첨가한 스테인리스강을 제조하여 PWR 원전환경에서의 피로균열성장특성을 평가하였다. 실험에 사용된 재료는 PWR 원전 가압기 밀림관 소재인 Type 347 스테인리스강에 0.0005 wt%가 첨가된 상용재와 0.11 wt% 질소가 첨가된 재료이다. 사용된 시편형상은 두께 5 mm, 폭 25.4 mm의 CT 시편이다. 수화학환경은 150기압, 온도 $316^{\circ}C$, 용존산소(DO) 5ppb, 용존수소(DH) 30 cc/Kg, pH는 약 7로 유지 하였으며, 응력비 0.1, 하중 반복속도 10Hz의 기계적 조건에서 하중제어로 시험을 진행하였다. 균열길이는 직류전위차법(Direct Current Potential Drop: DCPD)을 이용하여 측정하였다. 질소함량이 증가할수록 동일 사이클에서 균열길이가 늦게 성장하였고, 피로균열성장속도도 약간 늦어지는 것으로 나타났다. 각 스테인리스강의 피로파면 관찰결과 상용재는 약 1 ${\mu}m$의 산화물들이 생성되는 반면 질소첨가 스테인리스강은 약 0.1 ${\mu}m$정도 산화물이 생성되었다. 산화막의 두께도 질소가 첨가됨으로써 상용재에 비해 얇게 생성되었다. 따라서 질소가 첨가됨으로써 부식환경에서 내산화성이 향상되었으며, 이는 피로균열성장특성에 영향을 미치는 것으로 판단된다.