• 한국해양공학회지
• /
• 제8권2호
• /
• pp.157-165
• /
• 1994

Effect of an accelerated iso-thermal aging (375 degree C x 66days, 375 degree C x 200days) on elastic-plastic fracture resistance curve were examined in SA533B low alloy steel. Fracture toughness test are conducted by unloading compliance method at room temperature. But the apparent negative crack growth phenomenon, usually arise in partial unloading compliance test. The phenomenon of negative crack growth may be eliminated by the offset technique. There is no effect of aging on J sub(IC) and dJ/da in iso-thermal aged (375 degree C x 66 days) specimen, but there is very little effect in iso-thermal aged (375 degree C x 200 days) specimen.

• 대한기계학회논문집A
• /
• 제29권8호
• /
• pp.1118-1122
• /
• 2005

The direct current potential drop (DCPD) method and the unloading compliance (UC) method with a crack opening displacement gauge were applied simultaneously to the Zr-2.5Nb curved compact tension (CCT) specimens to determine which of the two methods can precisely determine the crack initiation point and hence the crack length for evaluation of their fracture toughness. The DCPD method detected the crack initiation at a smaller load-line displacement compared to the UC method. As a verification, a direct observation of the fracture surfaces on the curved compact tension specimens was made on the CCT specimens experiencing either 0.8 to 1.0 mm load line displacement or various loads from $50\%\;to\;80\%$ of the maximum peak load, or $P_{max}$. The DCPD method is concluded to be more precise in determining the crack initiation and fracture toughness, J in Zr-2.5Nb CCT specimens than the UC method.

• 대한기계학회논문집A
• /
• 제26권1호
• /
• pp.113-120
• /
• 2002

Experimental procedure to measure fracture toughness (J$_{c}$) under mixed mode loading using CTS(Compact Tension-Shear) specimens is described. It\`s loading angle ranges from 0$^{\circ}$ to 45$^{\circ}$ with interval of 157. The general outline of experimental procedure is similar to that of ASTM E8l3-89 fur mode I fracture. Equations fur determining J-integral is quoted from the authors' previous works. The relation between unloading compliance and physical crack size was calibrated. As an example, fracture toughness of aluminum alloy 2024p-7361 was measured and some reasonable results of J$_{c}$ with various loading angles were obtained.

• 한국해양공학회지
• /
• 제12권1호
• /
• pp.65-75
• /
• 1998

The fracture resistance curve is one of most important and design techniques employed in nuclear pressure vessel structures. This study is to evaluate the J-R curve characteristics for the SA508C-3 by the unloading compliance method and load rato analysis. The effect of strain aging for the exponential correlation of the J-R curve in this metal are investigated at room temperature, 20$0^{\circ}C$ and 30$0^{\circ}C$. The load ratio analysis method can evaluate the J-R curve by using the simple tension load-displacement curve only without the repeat of the unloading and loading. Therefore, the analysis by the proposed load ratio method has a merit, in comparison with the unloading compliance method, which can measure the crack length without the precision measurement equipment.

• Journal of Welding and Joining
• /
• 제5권2호
• /
• pp.44-52
• /
• 1987

The fracture toughness, $J_{IC}$ of high frequency electric resistance welded steel pipe for smooth and side-grooved CT specimen was evaluated by unloading compliance method. The crack growth, .${\delta}a$ was obtained from the equation of Donald and Saxena & Hudak, and $J_{IC}$ was determined from the curve of J-${\delta}a$ relations. The crack growth on the experiment using unloading compliance method is underestimated as compared with ${\delta}a$ measured directly by the SEM, so the reliability of $J_{IC}$ from saxena & Hudak equation is large than that from Donald. The $J_{IC}$ value of side-grooved CT Specimen is estimated less than that of smooth, and this is the effect of the side-groove, the shear-lip of crack tip and the reduction of crack tunnelling phenomena.

• 대한기계학회논문집A
• /
• 제22권1호
• /
• pp.64-72
• /
• 1998

This paper was undertaken to develop the fracture toughness testing method using small and single specimen compared to the conventional method in evaluating elastic-plastic fracture toughness of the superconducting magnet structural material at cryogenic temperature. The elastic-plastic fracture toughness test was conducted by using the unloading compliance method recommended by ASTM E813-89 to accomplish the above purpose. And, the 20% side-grooved 0.5TCT and 1TCT specimens were used to evaluate the fracture toughness by using as possible as miniaturized CT specimen. The unloading compliance method was a very useful method in evaluating elastic-plastic fracture toughness at cryogenic temperature. It could be taken valid fracture toughness values by using 20% side-grooved 0.5TCT specimen recommended by ASTM E813-89.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2003년도 춘계학술대회
• /
• pp.397-402
• /
• 2003

Fracture resistance curves for concerned materials are required in order to perform elastic-plastic fracture mechanical analyses. Fracture resistance curve is built with J-integral values and crack extension values. The objective of this paper is to apply the load ratio method to the measurement of the crack length for the real scale pipe specimen. For these, the fracture test using the real scale pipe specimen and finite element analyses were performed. A 4-point bending jig was manufactured for the pipe test and the direct current potential drop method and the load ratio method was used to measure the crack extension and the length for the real scale pipe test. Finite element analyses about the compliance of the pipe specimen were executed for applying the load ratio method according to the crack length.

• 대한기계학회논문집A
• /
• 제22권2호
• /
• pp.343-351
• /
• 1998

This paper was investigated degradation of the fracture toughness caused by sensitizing heat-treatment of the cryogenic structural material JN1 base metal using unloading compliance method reported as useful a method in evaluating the elastic-plastic fracture toughness at cryogenic temperature. The specimens used in this paper were 20% side-grooved 0.5T-CT specimens which were machined in the JN1 base metal. Also, to investigate cryogenic fracture toughness of the fusion line region in the JN1 GTA weldments, it was also used 20% side-grooved 0.5T-CT specimens that was machined fusion line to located in the middle of the specimen. The cryogenic fracture toughness values of the JN1 base metal were significantly decreased with increasing the time and temperature of the heat treatment. The fracture toughness value obtained from the fusion line specimen was invalid, but it was lower value than that of the JN1 base metal. Especially, this value was approximately equal with that obtained from the JN1 650.deg. C-5h heat-treated material.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2004년도 추계학술대회
• /
• pp.262-267
• /
• 2004

The unloading compliance method is the most commonly used method to evaluate the fracture resistance characteristics of a material. In dynamic loading condition, the direct current potential drop(DCPD) method has been used because the unloading compliance method can not be applied due to the discontinuity of loading. However, even in the dynamic test using DCPD method, there is a problem that the voltage drops sharply on the initiation of crack. For the reason metioned above, the normalization method was suggested on ASTM E 1820 which is revised recently, as a new method to evaluate the dynamic fracture resistance characteristic. The nomalization method can be used to obtain a fracture resistance curve directly from a load-load line displacement. In this study, we obtained two fracture resistance curves from static test of welding part of nuclear piping both by unloading compliance and nomalization method. The two curves were almost same each other, so the adaptability of the nomalization method has been proved. We conducted a dynamic fracture resistance test for the same material. The fracture resistance curve from the dynamic test was obtained by normalization method and compared to that of the static test result.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2001년도 춘계학술대회논문집A
• /
• pp.447-452
• /
• 2001

An automated system is developed to perform fatigue crack growth tests under constant effective stress intensity factor range ${\Delta}K_{eff}$. In the system, crack length and crack opening load are measured in real-time by using the unloading elastic compliance method. The system consists of two personal computers, an analogue electrical subtraction circuit, a stepping motor, a stepping motor driver, a PIO board, and the application software used to integrate the whole system. The performance of the developed system was tested and discussed performing constant ${\Delta}K_{eff}$ crack growth tests on a CT specimen of 7075-T6 aluminum alloy. The performance of the system is found to be strongly dependent on the accuracy of measurements of crack opening load. Besides constant ${\Delta}K_{eff}$ testing, the system is expected to be successfully applied for automation of various fatigue tests.