• Journal of Ocean Engineering and Technology
• /
• v.12 no.1
• /
• pp.65-75
• /
• 1998

The fracture resistance curve is one of most important and design techniques employed in nuclear pressure vessel structures. This study is to evaluate the J-R curve characteristics for the SA508C-3 by the unloading compliance method and load rato analysis. The effect of strain aging for the exponential correlation of the J-R curve in this metal are investigated at room temperature, 20$0^{\circ}C$ and 30$0^{\circ}C$. The load ratio analysis method can evaluate the J-R curve by using the simple tension load-displacement curve only without the repeat of the unloading and loading. Therefore, the analysis by the proposed load ratio method has a merit, in comparison with the unloading compliance method, which can measure the crack length without the precision measurement equipment.

• Journal of Ocean Engineering and Technology
• /
• v.8 no.2
• /
• pp.157-165
• /
• 1994

Effect of an accelerated iso-thermal aging (375 degree C x 66days, 375 degree C x 200days) on elastic-plastic fracture resistance curve were examined in SA533B low alloy steel. Fracture toughness test are conducted by unloading compliance method at room temperature. But the apparent negative crack growth phenomenon, usually arise in partial unloading compliance test. The phenomenon of negative crack growth may be eliminated by the offset technique. There is no effect of aging on J sub(IC) and dJ/da in iso-thermal aged (375 degree C x 66 days) specimen, but there is very little effect in iso-thermal aged (375 degree C x 200 days) specimen.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.26 no.1
• /
• pp.113-120
• /
• 2002

Experimental procedure to measure fracture toughness (J$_{c}$) under mixed mode loading using CTS(Compact Tension-Shear) specimens is described. It\`s loading angle ranges from 0$^{\circ}$ to 45$^{\circ}$ with interval of 157. The general outline of experimental procedure is similar to that of ASTM E8l3-89 fur mode I fracture. Equations fur determining J-integral is quoted from the authors' previous works. The relation between unloading compliance and physical crack size was calibrated. As an example, fracture toughness of aluminum alloy 2024p-7361 was measured and some reasonable results of J$_{c}$ with various loading angles were obtained.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.29 no.8 s.239
• /
• pp.1118-1122
• /
• 2005

The direct current potential drop (DCPD) method and the unloading compliance (UC) method with a crack opening displacement gauge were applied simultaneously to the Zr-2.5Nb curved compact tension (CCT) specimens to determine which of the two methods can precisely determine the crack initiation point and hence the crack length for evaluation of their fracture toughness. The DCPD method detected the crack initiation at a smaller load-line displacement compared to the UC method. As a verification, a direct observation of the fracture surfaces on the curved compact tension specimens was made on the CCT specimens experiencing either 0.8 to 1.0 mm load line displacement or various loads from $50\%\;to\;80\%$ of the maximum peak load, or $P_{max}$. The DCPD method is concluded to be more precise in determining the crack initiation and fracture toughness, J in Zr-2.5Nb CCT specimens than the UC method.

• Journal of Welding and Joining
• /
• v.5 no.2
• /
• pp.44-52
• /
• 1987

The fracture toughness, $J_{IC}$ of high frequency electric resistance welded steel pipe for smooth and side-grooved CT specimen was evaluated by unloading compliance method. The crack growth, .${\delta}a$ was obtained from the equation of Donald and Saxena & Hudak, and $J_{IC}$ was determined from the curve of J-${\delta}a$ relations. The crack growth on the experiment using unloading compliance method is underestimated as compared with ${\delta}a$ measured directly by the SEM, so the reliability of $J_{IC}$ from saxena & Hudak equation is large than that from Donald. The $J_{IC}$ value of side-grooved CT Specimen is estimated less than that of smooth, and this is the effect of the side-groove, the shear-lip of crack tip and the reduction of crack tunnelling phenomena.

• Journal of Welding and Joining
• /
• v.15 no.4
• /
• pp.178-186
• /
• 1997

The purpose of this study is to evaluate the J-R curve characteristics for the 5083 aluminum alloy weldment by the load ratio analysis. The results of the load ratio analysis are compared with those of the J-R curve which are obtained by the ASTM unloading compliance method. The crack length calculated by the load ratio analysis is agrees well with the measured final crack length. The slope of the exponential J-R curve estimated by the load ratio analysis is slightly smaller than that by the ASTM unloading compliance method. The exponential correlation of the J-R curve for the 5083 aluminum alloy base metal by the load ratio analysis is J = 93.88 ${\Delta}{\alpha}^{0.375}$. That for the weld metal and HAZ is J = 69.87 ${\Delta}{\alpha}^{0.389}$ and J = 70.59 ${\Delta}{\alpha}^{0.359}$ respectively. The J-R curve obtained by the ASTM unloading compliance method is overpredicted and should be offsetted due to the initial negative crack. On the other hand, the load ratio analysis method can evaluate the J-R curve by only load displacement curve without particular crack measurement equipment.

• Journal of Power System Engineering
• /
• v.1 no.1
• /
• pp.80-90
• /
• 1997

The purpose of this study is to evaluate the validity examination of the J-R curve characteristics for the nuclear reactor pressure vessel steels and Al alloys by the load ratio analysis. The results of the load ratio analysis are compared with those of the J-R curve which are obtained by the ASTM unloading compliance method. The crack length calculated by the load ratio analysis is agree well with the measured final crack length. The slope of the exponential J-R curve estimated by the load ratio analysis is slightly smaller than that by the ASTM unloading compliance method. The J-R curve obtained by the ASTM unloading compliance method is over-predicted and should be offsetted due to the initial negative crack. On the other hand, the load ratio analysis method can evaluate the J-R curve by only load-displacement curve without particular crack measurement equipment.

• Proceedings of the KWS Conference
• /
• 2001.05a
• /
• pp.228-231
• /
• 2001

Elastic-plastic fracture toughness $J_{1c}$ can be used as an effective design criterion in elastic plastic fracture mechanics. Most of these systems are operated at high temperature and $J_{1c}$ values are affected by temperature. therefore, the $J_{1c}$ valuse at high temperature must be determined for use of integrity evaluation and designing of such systems. Elastic-plastic fracture toughness $J_{1c}$ tests were performed on SA516 carbon steel plate and test results were analyzed according to ASTM E 813-8, ASTM 1813-89. Safety and integrity are required for reactor pressure vessels vecause pthey are operated in high temperature. there are single specimen method, which used as evaluation of safety and integrity for reactor pressure vessels. In this study, elastic-plastic fracture toughness$(J_{1c})$ and $J-\Delta{a}$ of SA 516/70 steel used as reactor pressure vessel steel are measured and evaluated at room Temperature, $150^{\circ}C$, $250^{\circ}C$ and $370^{\circ}C$ according to unloading compliance method.

• Journal of Ocean Engineering and Technology
• /
• v.15 no.2
• /
• pp.99-104
• /
• 2001

Elastic-plastic fracture toughness $J_{lc}$ can be used as an effective design criterion in elastic plastic fracture mechanics. Most of these systems are$J_{lc}$ $J_{lc}$ value at high temperature must be determined for use of integrity evaluation and designing of such systems. Elastic-plastic fracture toughness $J_{lc}$ tests were performed on SA516/70 carbon steel plate and test results were analyzed according to ASTM E 813-87, ASTM E 813-89 and ASTM E 1152-87.safety and integrity are required for reactor pressure vessels because, they are operated in high temperature. There are single specimen method, which used as evaluation of safety and integrity for reactor pressure vessels. In this study, elastic-plastic fracture toughness($J_{lc}$) and J-$\Delta$a of SA 516/70 steel used as reactor pressure vessel steel are measured and evaluated at room temperature, 150$^{\circ}C $, 250$^{\circ}C $ and 370$^{\circ}C $ according to unloading compliance method.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.22 no.1
• /
• pp.64-72
• /
• 1998

This paper was undertaken to develop the fracture toughness testing method using small and single specimen compared to the conventional method in evaluating elastic-plastic fracture toughness of the superconducting magnet structural material at cryogenic temperature. The elastic-plastic fracture toughness test was conducted by using the unloading compliance method recommended by ASTM E813-89 to accomplish the above purpose. And, the 20% side-grooved 0.5TCT and 1TCT specimens were used to evaluate the fracture toughness by using as possible as miniaturized CT specimen. The unloading compliance method was a very useful method in evaluating elastic-plastic fracture toughness at cryogenic temperature. It could be taken valid fracture toughness values by using 20% side-grooved 0.5TCT specimen recommended by ASTM E813-89.