• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.36 no.10
• /
• pp.1235-1239
• /
• 2012

Primary water stress corrosion cracking (PWSCC) has been observed around the weld region of control rod drive mechanism (CRDM) nozzles in nuclear power plants overseas. The weld has a J-shaped groove and it connects the CRDM nozzle with the reactor vessel upper head (RVUH). It is a dissimilar metal weld (DMW), because the CRDM is made of alloy 600 and the RVUH is made of carbon steel. In this study, finite element analysis (FEA) was performed to estimate the stress condition around the weld region. Generally, it is known that a high tensile region is more susceptible to PWSCC. FEA was performed as for the condition of welding, hydrostatic test and normal operation successively to observe how the residual stress changes due to plant condition. The FEA results show that a high tensile stress region is formed around the weld starting point on the inner surface and around the weld stop point on the outer surface.

• Transactions of the Korean Society of Pressure Vessels and Piping
• /
• v.9 no.1
• /
• pp.56-61
• /
• 2013

This paper presents the results of integrity assessment for the cracks happened in reactor vessel upper head penetration nozzles. The crack morphology for a boat sample from crack area was analyzed through microscope. The stress condition including weld residual stress around crack was analyzed using finite element analysis. From the results of crack morphology and stress condition, the crack was concluded as primary water stress corrosion cracking. The integrity of the cracked nozzle was assessed by the methodology provided in ASME Section XI. According to the assessment results, the remaining life of the cracked nozzle was 1.43 yrs. and the plant decided to repair it.