• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.18 no.5
• /
• pp.278-284
• /
• 2017

In this study, the heat input conditions suitable for the AZ61 magnesium alloy were derived by controlling the welding speed at a constant rotational speed. In addition, from an economic point of view, industry demands higher welding speeds. Therefore,the effects of the welding speed were studied. The rotational speed applied was 800rpm, and the welding speed was varied from 100 to 500mm/min to evaluate the behavior of the welded regions. Tensile and hardness tests were conducted to examine the mechanical properties. Optical microscopy was used to observe the microstructure and soundness of the welded regions. Defects were observed at the welded region when the welding speed was more than400mm/min. As the welding speed increased, the grain size of the stir zone decreased and the hardness tended to increase proportionally. When the rotational speed was 800 rpm and the welding speed was 200mm/min and 300mm/min, there wereno defects in the welded region and excellent mechanical properties were recorded. In addition, the joint efficiencies were 100.5% and 101.2%, respectively, and the ultimate tensile strength was similar to that of the base metal. Fracture of the tensile specimen occurred between the advancing side and stir zone, and the fracture location coincided with the region where the hardness decreased temporarily.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.20 no.8
• /
• pp.133-138
• /
• 2019

This study evaluated the tensile properties of SAPH440, a hot-rolled steel for automotive structural applications, based on GMAW lap welding, the welding current, the welding voltage, and the feed rate. Tensile tests were performed according to the joint parameters of the GMAW process, for which specimens were fabricated according to KS B ISO 9018 by lap welding. The bead appearance was observed in each condition, and the weldability was evaluated by the tensile test. Higher the welding current resulted in a deeper weld, but the tensile strength was not significantly different from when the parameter was fixed due to the fracture of the base material. When the current was higher than the voltage, as in the case of a welding current of 200 A and welding voltage of 17 V, a large amount of spatter is generated, the welding is unstable, and the welded part breaks. Higher the voltage resulted in the bead not causing defects in general, and it also affected the weldability. If the current and voltage were too low, the welding was not performed normally, and the tensile strength could not be measured. However, as the current increased, the increase of the voltage and the feed rate did not affect the tensile strength.

• Composites Research
• /
• v.31 no.6
• /
• pp.332-339
• /
• 2018

Fiber metal hybrid laminate (FML) can be used as an economic material with superior mechanical properties and light weight than conventional metal by bonding of metal and FRP. However, there are disadvantages that it is difficult to predict fracture behavior because of the large difference in properties depending on the type of fiber and lamination conditions. In this paper, we study the failure behavior of hybrid materials with laminated glass fiber reinforced plastics (GFRP, GEP118, woven type) in Al6061-T6 alloy. The Al alloys were coated with GFRP 1, 3, and 5 layers, and fracture behavior was analyzed by using a static test and a low cycle fatigue test. In the low cycle fatigue test, strain - life analysis and the total strain energy density method were used to analyze and predict the fatigue life. The Al alloy did not have tensile properties strengthening effect due to the GFRP coating. The fatigue hysteresis geometry followed the behavior of the Al alloy, the base material, regardless of the GFRP coating and number of coatings. As a result of the low cycle fatigue test, the fatigue strength was increased by the coating of GFRP, but it did not increase proportionally with the number of GFRP layers.