• Journal of the Korean Society for Nondestructive Testing
• /
• v.16 no.4
• /
• pp.241-250
• /
• 1997

The velocity dispersion of surface acoustical wave(SAW) of Si layer/mesh Au/Si substrate was measured by the frequency analysis technique of backward radiation at liquid/solid interface. The difference of backward radiation patterns depending on used transducers (2, 5, 10MHz) confirmed that the backward radiation phenomenon was caused by the energy radiation from SAW generated in surface region. An ultrasonic goniometer was constructed to measure continuously the angular dependence of backscattered intensity. The angular dependences of backward radiation(5MHz) were measured for Ni layer/Al substrate specimens that were bonded by epoxy involving different content of Cu powder. It was known that the width and pattern of backward radiation had informations such as the velocity dispersion, bonding quality and structure of surface region.

• Journal of the Korean Society for Precision Engineering
• /
• v.17 no.9
• /
• pp.81-86
• /
• 2000

This paper was carried out to investigate the characteristics of interlaminar fracture toughness of foam core sandwich structures under opening loading mode by using the double cantilever beam (DCB) specimens in Carbon/Epoxy and foam core composites. instead of using symmetric geometry of DCB specimen non-symmetric DCB specimen was used to calculate the interlaminar fracture toughness. Three approaches for calculating the energy release rate({{{{ {G }_{IC } }}}}) were compared. Fracture toughness of foam core sandwich structures by autoclave vacuum bagging and hotpress were compared and analyzed. Experiment nonlinear beam bending FEM method were performed. Suggested bonding surface compensation and equivalent area inertia moment was used to calculate the energy release rate in nonlinear analytical results. The conclusions among experimental nonlinear analytical and FEM results was observed. The vacuum bagging method was shown to be able to substitute method in stead of autoclave without serious loss of Mode I energy release rate({{{{ {G }_{IC }}}}}) to be able to substitute method in stead of autoclave without serious loss of Mode I energy release rate({{{{ {G }_{IC }}}}}).

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1992.04a
• /
• pp.115-119
• /
• 1992

산업의 발전과 더불어 새로운 재료의 개발에 대한 요구가 날로 증가하고 있으며 이와 같은 요구에 부응하기위하여 각종의 신소재가 개발되고있다. 이들 신소재 중에서 섬유강화 복합재료는 높은 비탄성과 비강도특성 때문에 구조물의 경량화가 요구되는 우주선, 항공기 등에 주로 이용 되어 왔으며 최근에는 복합재료의 가격이 저렴해 지면서 이 재료의 높은 비탄성과 감쇠특성을 이용하고자 스포츠용품 및 기계 부품에도 섬유강화 복합재료의 이용이 증가 되고 있다. 항공기나 고속회전체의 부품을 복합재료로 제작하였을 경우 복합재료를 다른 금속이나 다른 복합재료부품에 접합(joining)시켜야 하는데 이 때문에구조물의 효율은 Joint에서 주로 죄우된다. Joint를 제작하기 위해서는 복합재료의 표면을 가공한 수 Adhesive를 이용하거나 Bolt로 체결하기 위해 구멍 뚫기 작업이 필요하여 드릴링을 하였을때 이 재료가 매우 연마성이 강하여 심한 공구마멸을 일으키며, 드릴의 입구와 출구쪽에서 각 ply들의 박리 현상이 발생하고, 드릴가공된 벽면으로부터 섬유 또는 레진의 탈락현상등이 발생하는 결점을 가지고 있다. 따라서 본 연구에서는 이러한 결점을 최소화하여 고정밀도의 높은 생산성을 얻기위한 가공기술에 대한 자료를 만들고 최적 절삭조건 및 복합재료가공용 드릴의 설계를 위한 지침을 제시하고자 고속도강 표준드릴을 사용하여 유리섬유 에폭시 복합재료및 탄소섬유 에폭시 복합재료의 드릴링 실험에서 절삭조건이 가공면 생성, 공구마멸, 절삭력에 미치는 영향에 대하여 조사하였다.

• Journal of Welding and Joining
• /
• v.13 no.3
• /
• pp.55-64
• /
• 1995

Metallizing method on ceramic surface is one of the compositing technology of ceramics and metal. The purpose of this study is to make HIC (Hybrid Intergrated Circuit) with copper metallizing method of which copper layer is formed on ceramic substrate by firing in atmosphere in lieu of conventional hybrid microcircuit systems based on noble metal. Metallizing pastes were made from various copper compounds such as Cu$_{2}$O, CuO, Cu, CuS and kaolin. And the screen printing method was used. The characteristics of metallized copper layers were analyzed through the measurement of sheet resistance, SEM, and EDZX. The results obtainted are summarized as follows; 1. The copper metallizing layers on ceramic surface can be formed by firing in air. 2. The metallized layer using Cu$_{2}$O paste showed the smallest sheet resistance among a group of copper chemical compounds. And optimum metallizing conditions are 15 minutes of firing time, 1000.deg.C of firig temperature, and 3 minutes of deoxidation time. 3. The results of EDAX analysis showed mutual diffusion of Cu and Al. 4. The kaolin plays a important role of deepening the penetration of Cu to $Al_{2}$O$_{3}$ ceramics. But if the kaolin content is too much, sheet resistance increases and copper metallizing layer becomes brittle.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.25 no.10
• /
• pp.1541-1550
• /
• 2001

This paper describes experimental investigations in the direct extrusion of copper clad aluminum rods through conical dies. Composite materials consist of two or more different material layers. Copper clad aluminum composite materials are being used fur economic and structural purposes and the development of an efficient production method of copper clad aluminum composite material rods by extrusion is very important, It is necessary to know the conditions in which successful uniform extrusion ,and sound cladding may be carried out without any defects in the direct extrusion. There are several variables that have an influence on determining a sound clad extrusion. In order to investigate the influence of these parameters on the hot direct extrudability of the copper clad aluminum composite material rods, the experimental study have been performed with various extrusion temperatures, extrusion ratios and semi-cone angles of die. Subsequently, the microscopic inspection of interface bonding is carried out for extruded products. By measuring hardness, along extrusion way of products, a variation of hardness has been discussed. Proportional flow state has been considered by measuring radius ratio of Cu sleeve and Al core before and after extrusion.

• Journal of Welding and Joining
• /
• v.25 no.3
• /
• pp.51-56
• /
• 2007

A $CO_2$ laser overlay was conducted by using a Fe-based powder on the AC2B aluminum substrate. Cracks and intermetallic compounds (IMC) were observed inconsistently along the interface between the overlay and post-molten layer. A scanning electron microscopy (SEM) with energy dispersive spectroscopy (EDS) detected some Fe-rich IMC ($Fe_3Al$, FeAl) as well as the brittle Al-rich IMC ($Fe_2Al_5,\;FeAl_3$). Micro vickers hardness proved the formation of Al-rich IMC ($FeAl_3$) along the interface by showing HV0.1 $800{\sim}900$. Furthermore, nano indentation was successfully applied to investigate the behavior of IMC more precisely than the micro vickers hardness.

• Journal of Korean Association for Spatial Structures
• /
• v.12 no.4
• /
• pp.81-90
• /
• 2012

The concrete-filled tube (CFT) column has the excellent structural performance. But it is difficult to connect with column and beam because of closed section. Its Solution, 2 members of ㄷchennel in which Internal diaphragm is installed were welded beforehand and the method of making Rectangular Steel Tube was proposed. According to upside and downside junction shape, Internal diaphragm suggested as symmetric specimen and asymmetric specimen. The upper and lower diaphragm of the Symmetric specimen used the same horizontal and The upper diaphragm of the Asymmetric specimen used the horizontal plate and the lower diaphragm used the vertically plate. In this research, 4 T-shape column to beam steps connections were tested with cyclic loading experiment in order to evaluate the structural capability of the offered connection. Symmetric specimens be a failure in 0.03rad from beam flange. And Asymmetric specimens be a failure in 0.05rad from column interface. The comparison results of All specimens shown similar to energy absorption capacity in 0.02rad.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.173-174
• /
• 2007

반도체 소자가 발달함에 따라서 박막은 더욱 다층화 되고 그 두께는 줄어들고 있다. 따라서 소자의 초고집적화를 위해서는 각 박막의 두께를 더욱 작게 하여야 한다. 또한 반도체 소자 제조 공정에서는 Si 기판과 금속 박막간의 확산이 커다란 문제로 부각되어 왔다. 특히 Cu는 높은 확산성에 의하여 Si 기판과 접합에서 많은 확산에 의한 문제가 발생하게 되며, 또한 선폭이 줄어듦에 따라 고열이 발생하여 실리콘으로 spiking이 발생하게 된다. 이러한 확산을 방지하기 위하여 금속 배선과 Si기판 사이에는 필연적으로 확산방지막을 삽입하게 되었다. 기존의 연구에서는 $1000\;{\AA}$의 W-B-C-N 확산방지막을 제작하여 연구하였다. 이 논문에서는 Cu의 확산을 방지하기 위한 W-B-C-N 확산방지막을 다양한 두께로 제작하여 그 특성을 확인하여 초고집적화를 위한 더욱 얇은 두께의 W-B-C-N 확산방지막에 대하여 연구하였다. W-B-C-N 확산방지막의 두께 변화에 대한 특성을 확인하기 위하여 $900^{\circ}C$까지 열처리 한 후 그 면저항을 측정하였다.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.23 no.1
• /
• pp.130-137
• /
• 2019

Precast concrete (PC) structure is one of the type of the structures which is made in a facility prior to installing it to a construction field. The contact surfaces between two PC structures should be treated for obtaining enough binding force by inducing prestressing force. However, in the many cases, the contact surface causes the crack and leakage of water. These cracks and water leakage can cause the corrosion of the rebar, and the corrosion of the rebar can severely reduce the long-term durability. In this study, the SMA wire connector is suggested to solve the problem with the contact surfaces between two PC structures. The pull-out resistance of the suggested SMA wire connector is evaluated by conducting the tests to find the effect of the number of wires, shape of connector part, and shape memory effect. As a result of this study, the empirical formula is suggested to estimate the pull-out resistance related with the effects of the shape of the connector, shape memory effect, and the adhesive force. The validity between the estimated pull-out resistance and the measured value is confirmed.

• The Sea:JOURNAL OF THE KOREAN SOCIETY OF OCEANOGRAPHY
• /
• v.12 no.3
• /
• pp.170-177
• /
• 2007

In this study, the long-term predictability of El Nino and La Nina events of Pusan National University Coupled General Circulation Model(PNU/CME CGCM) developed from a Research and Development Grant funded by Korea Meteorology Administration(KMA) was examined in terms of the correlation coefficients of the sea surface temperature between the model and observation and skill scores at the tropical Pacific. For the purpose, long-term global climate was hindcasted using PNU/CME CGCM for 12 months starting from April, July, October and January(APR RUN, JUL RUN, OCT RUN and JAN RUN, respectively) of each and every years between 1979 and 2004. Each 12-month hindcast consisted of 5 ensemble members. Relatively high correlation was maintained throughout the 12-month lead hindcasts at the equatorial Pacific for the four RUNs starting at different months. It is found that the predictability of our CGCM in forecasting equatorial SST anomalies is more pronounced within 6-month of lead time, in particular. For the assessment of model capability in predicting El Nino and La Nina, various skill scores such as Hit rates and False Alarm rate are calculated. According to the results, PNU/CME CGCM has a good predictability in forecasting warm and cold events, in spite of relatively poor capability in predicting normal state of equatorial Pacific. The predictability of our CGCM was also compared with those of other CGCMs participating DEMETER project. The comparative analysis also illustrated that our CGCM has reasonable long-term predictability comparable to the DEMETER participating CGCMs. As a conclusion, PNU/CME CGCM can predict El Nino and La Nina events at least 12 months ahead in terms of NIino 3.4 SST anomaly, showing much better predictability within 6-month of leading time.