• Journal of the Korean Society of Marine Environment & Safety
• /
• v.27 no.1
• /
• pp.187-192
• /
• 2021

In this study, Inconel 625 was used as a thermal spray material to prevent dew point corrosion damage to the economizer tube, and sealing treatment was performed after applying the arc thermal spray coating technology. Various electrochemical experiments were conducted in the 0.5 wt% sulfuric acid solution to analyze the corrosion resistance of the thermal spray coating (TSC) layer. After the anodic polarization experiment, the degree of corrosion damage was determined through a scanning electron microscope and EDS component analysis. When measuring the open circuit potential, the effect of the sealing treatment was confirmed through stable potential formation of the TSC+sealing treatment (TSC+Sealing). As a result of the anodic polarization experiment, the passivation region was confirmed in TSC and TSC+Sealing, and corrosion resistance was improved as no corrosion damage was observed. In addition, the corrosion resistance of TSC+Sealing was the best when analyzing the corrosion potential and corrosion current density calculated by Tafel analysis.

• Journal of the Korean Society of Marine Environment & Safety
• /
• v.27 no.4
• /
• pp.521-528
• /
• 2021

In this study, to repair damaged economizer fin tubes on ships, sealing treatment was performed after applying arc thermal spray coating technology using Inconel 625. A solid particle erosion (SPE) experiment was conducted according to ASTM G76-05 to evaluate the durability of the substrate, thermal spray coating (TSC), and thermal spray coating+sealing treatment (TSC+Sealing) specimens. The surface damage shape was observed using a scanning electron microscope and 3D laser microscope, and the durability was evaluated through the weight loss and surface roughness analysis. Consequently, the durability of the substrate was superior to that of TSC and TSC+Sealing, which was believed to be owing to numerous pore defects in the TSC layer. In addition, the mechanism of solid particle erosion damage was accompanied by plastic deformation and fatigue, which were the characteristics of ductile materials in the case of the substrate, and the tendency of brittle fracture in the case of TSC and TSC+Sealing was confirmed.

• Journal of Surface Science and Engineering
• /
• v.55 no.6
• /
• pp.433-440
• /
• 2022

Environmental pollution caused by power plant exhaust gas is highlighted and eco-friendly regulations are being strengthened. However, due to the abundant reserves and low prices of coal, still the most used for power generation in the world. Therefore, flexible operation of coal-fired power plants to reduce emissions has become an inevitable option. However, lowering the output increases the possibility of acid dew point corrosion as the exhaust gas temperature decreases. The dew point corrosion occurs when condensable gases such as SO₃, HCl, NO₂ and H₂O cools below the saturation temperature. SO₃ is already well known to cause severe low- temperature corrosion in coal-fired power plants. Therefore, this study aims to prevent damage that may occur during operation by analyzing the dew point and corrosion resistance with exhaust gas temperature and sulfuric acid concentration of the power plant economizer tube.

• Corrosion Science and Technology
• /
• v.20 no.6
• /
• pp.384-390
• /
• 2021

In this paper, durability evaluation and surface damage mechanism were investigated through solid particle erosion (SPE) test after applying hot-dip aluminizing (HDA) technology for the purpose of maintenance of marine economizer tube. Damaged surface shape was analyzed using SEM and 3D microscope. Compositional changes and microstructure of the HDA layer were analyzed through EDS and XRD. Durability was evaluated by analyzing weight loss and surface damage depth after SPE. HDA was confirmed to have a two-layer structure of Al and Al₅Fe₂. HDA+HT was made into a single alloy layer of Al₅Fe₂ by diffusion treatment. In the microstructure of HDA+HT, void and crack defect were induced during the crystal phase transformation process. The SPE damage mechanism depends on material properties. Plastic deformation occurred in the substrate and HDA due to ductility, whereas weight loss due to brittleness occurred significantly in HDA+HT. As a result, the substrate and HDA showed better SPE resistance than HDA+HT.

• Journal of Korean Society of Environmental Engineers
• /
• v.30 no.5
• /
• pp.552-559
• /
• 2008

Three dimensional numerical analysis were performed to investigate the combustion characteristics in a tangentially fired pulverized coal boiler. The predicted values at the outlet of economizer for the gas temperature, O$_2$, NO, CO were been compared with the measured data. By using the actual operating conditions of the power plant, the distribution of velocity, gas temperature, O$_2$, CO, CO$_2$ and NO as well as the particle tracking in the boiler were investigated. Throughout the present study, the non-uniform distribution of flue gas temperature in front of the final superheater might be resulted from the residual swirl flow in the upper furnace of the boiler. The present analysis on non-uniform distribution of the gas temperature could provide the useful information to prevent the frequent tube failure from happening in the final superheater of the tangentially coal-fired boiler.