• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1998년도 춘계학술대회 논문집
• /
• pp.211-214
• /
• 1998

The composite of polyvinylalcohol(PVA) and lithium salts(LiBF$_4$) is prepared for a solid-state electrolyte of electric double layer capacitor. The composite shows a good ionic conductivity. The solid-state electric double layer capacitor is made of PVA-LiBF$_4$ composite, activated carbon and etc.. As evaluation of characteristics of capacitor, capacitance change which measured by charge-discharge test with 2.2V~0V at 8$0^{\circ}C$ for 800 hours, was about 10%. The gravimetric and volumetric capacitance were 10.0 F/g~30.0 F/g and 16.0F/㎤~F/㎤, respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 추계학술대회 논문집
• /
• pp.61-64
• /
• 2001

This study relates to a method for manufacturing a solid electrolytic capacitor using a functional polymer composition. The method comprises immersing the rolled aluminum electrolytic capacitor device in polyaniline solution with high electric conductivity to impregnate the device with polyaniline, drying the impregnated device in a drying oven which is maintained at constant temperature to fully remove the solvent, inserting the dried device to a capacitor aluminum can and then sealing with epoxy resin, to manufacture a solid electrolytic capacitor using a conducting polymer. As such, the impregnation can be performed well at not only normal temperature and pressure, but also high temperature and reduced pressure. The solid electrolytic capacitor has the advantages of high capacity, low impedance and low ESR, and also, low manufacturing cost, simple processes and high reliability.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2008년도 추계학술대회 초록집
• /
• pp.93-93
• /
• 2008

니켈도금은 각종 소지 상에 직접적이고 밀착성이 양호하고, 변색이 적고 방청력이 크며, 경도, 내식성, 내마모성 및 유연성이 우수하다. 또한 최근 활발히 진행되고 있는 광촉매 연구에 $TiO_2$는 우수한 광화학적 안정성, 효과적인 전하분리, 높은 산화 환원력 및 상업적 적용성을 갖기 때문에 니켈도금용액에 $TiO_2$를 첨가하며 복합도금을 행함으로써 니켈이 가지고 있는 기존의 우수한 특성에 $TiO_2$의 광분해 효과를 부과시킴 으로써 그 특성이 한층 더 향상되는 것을 알수있다. 본 연구에서는 수용액전해질과 비수용액 전해질에서의 Ni-$TiO_2$ 복합도금의 특성을 비교 분석해보았다. 동전위(Potentiodynamic)실험 및 순환전위(Cyclic Voltammetry)실험을 하였으며, 도금층의 특성 및 두께는 OM,SEM을 이용하여 분석하였다. 또한 복합도금 촉매 전극에 의한 광분해 효과를 보기 위해서 UV램프를 이용하여 분석하였다.

• 전력전자학회:학술대회논문집
• /
• 전력전자학회 2014년도 전력전자학술대회 논문집
• /
• pp.453-454
• /
• 2014

태양광 발전용 AC-모듈에서 발생하는 전력 디커플링을 위해 사용되는 대용량 전해 커패시터는 시스템의 신뢰성을 감소시키므로 최근 보조회로를 이용한 디커플링 기법이 연구되고 있다. 하지만 디커플링 회로의 제어기 오차와 시스템의 효율이 고려될 경우, 태양광 패널에 전력 맥동이 존재하게 되고 이는 인버터 출력 전류를 왜곡시키는 원인이 된다. 본 논문에서는 제어기 오차와 시스템 효율을 고려하여 발생하는 전력 맥동에 대해 분석하고, 이를 저감시키기 위한 전류 왜곡 보상 기법을 제안하였다. 이를 PSIM 시뮬레이션을 통해 그 타당성을 검증하였다.

• 한국표면공학회지
• /
• 제22권3호
• /
• pp.118-127
• /
• 1989

The rate of electrodeposition Zinc-nickel alloy on to electrolytic ione in sulface solution both under an inter and air atmospherss has studied by use of a rotating disc geometry. The kinetics shows 1st order reaction, and the rate constants are proportional to the square root of rpm, however, they are less than the valuse suggested by Levich. The rate constants of zinc deposition approach the total mass transfer rate constants with increasing potential and deviate with increasing rotaing speed, but those of nickel deposition are constant. Below $40^{\circ}C$ the activation engrgies of zinc deposition and nikel deposition were 4.4Kcal/mol and 6.3Kcal/mol respectively. There results show that overall reaction rate of zinc-nickel plaeting is controlled by mixed reaction and zinc deposotion is more affected by mass transfer reaction than nickel. The current density for the zinc-nickel plating was less in an air atmosphere than in a nitrogen atmosphere. The cathode efficiency increased with decreasing cathode rotating speeds, potentials, and increasing temperatures. Zzinc-nickel platings are more improved in microhardnss than zinc platings.

• 한국지하수토양환경학회지:지하수토양환경
• /
• 제8권3호
• /
• pp.56-60
• /
• 2003

전기분해에 의한 부상현상을 이용하여 유류로 오염된 토양 세정 후 발생되는 유출수 중 유분 등을 분리하기 위한 적정 운전조건을 찾고자 하였다. 전기분해 반응조(200${\times}$10${\times}$15cm)를 이용하여 혼합계면활성제($POE_5$ : $POE_{14} $, 1:1) 1%용액에 디젤을 1,000 mg/L 농도로 용해시켜 실험하였다. 양극에는 티타늄 코팅전극, 음극으로는 스테인레스 스틸전극을 이용하였다. 반응시간은 62분(반응 :60분, 부상시간 :2분)이었으며 전압은 6V였다. 전해질 첨가에 의한 영향을 알아보기 위하여 실험한 결과, 전해질을 첨가하였을 경우 첨가하지 않았을 때보다 40% 정도의 효율이 증가하였다. 적정 전해질, 주입농도 및 반응시간을 알아보기 위하여 1N NaCl과 NaOH의 농도를 변화시켜 가면서 실험하였다. NaCl의 경우 더 좋은 효율을 나타내었다. 전해질의 농도는 0.2-1.0%의 농도범위에서 NaCl와 NaOH 모두 농도에 따라 순차적으로 효율이 증가하였다. 두 전해질 모두 0.4-1.0% 농도 범위에서 평형에 도달하는 시간은 20분으로 나타났다.

• 대한토목학회논문집
• /
• 제32권1B호
• /
• pp.79-84
• /
• 2012

질산성질소는 일반적인 지하수 오염물질로서, 본 연구에서는 영가철을 충진한 복극전해조를 이용하여 서로 다른 조건에서 질산성질소 제거실험을 수행하였다. 실험에 사용된 전해조에는 양쪽 끝에 위치한 주 전극 사이에 전도체로서 영가철이, 비전도체로서 규사가 혼합하여 충진되었다. 모의폐수(오염된 지하수를 모사하였으며 초기 질산성질소 농도 약 30 mg/L, 전기전도도 약 300 ${\mu}S/cm$)를 이용한 연속식 실험에서 인가전압 600 V, 유입유량 20 mL/min으로 최대 99% 이상의 질산성질소를 제거하였다. 최적 혼합비 및 최적 유입유량은 각각 1:1~2:1(규사:영가철), 30 mL/min으로 결정하였다. 질산성질소의 주입농도에 따라 유출수의 pH가 비례적으로 거동하였으며, 질산성질소 환원의 최종산물로서 약 60% 정도가 암모니아로 유출되었다. 실험이 끝난 후 영가철 표면에서의 산화철은 대부분 magnetite형태로 존재하였다.

• 대한화학회지
• /
• 제35권6호
• /
• pp.707-712
• /
• 1991

수은 pool 전해조를 사용하여 (5:3) EtOH/4N-HCl 용액계에서 선택적인 -N-N=O기의 전기화학적 환원에 의해 N'-phenyl-N-(2-chloroethyl)-N-nitrosourea로부터 N'-phenyl-N-(2-chloroethyl)-N-aminourea를 합성하였다. 전기화학적 환원에 앞서 반응의 최적조건을 검토하기 위하여 몇 가지 N'-aryl-N-(2-chloroethyl)-N-nitrosourea 유사체에 대하여 pH변화에 따른 환원전위를 순환전압전류법으로 조사한 결과 pH에 따라 $E_p$값이 "-"쪽으로 이동하였으며 aryl기의 치환기 효과는 -N-N=O기의 환원 전위에 크게 영향을 미치지 않는 것으로 나타났다. 용액계의 pH에 따른 반응성을 조사한 결과 강산성 용액(pH<1)에서 반응이 가장 잘 진행되며 -0.7 V vs. Ag/AgCl/4 N-HCl에서 N-N=O기의 선택적인 4전자 환원반응에 의해 N-N$H_2$가 생성됨을 확인하였다.

• 공업화학
• /
• 제5권2호
• /
• pp.255-262
• /
• 1994

아크용융방법으로 준비한 Ti-5Bi 합금을 산화시켜 제조한 산화티타늄의 에너지변환효율(${\eta}_e$)을 광학농도, 광에너지에 따라서 측정하였다. 그리고 광학농도 및 전해액의 pH변화에 따른 플랫-밴드전압변화를 측정하였다. 광학농도와 광에너지가 증가하면 에너지변환효율은 증가하였으며 광학농도 $0.2W/cm^2$, 조사되는 빛의 에너지가 4.0eV에서 최대 에너지변환효율은 각각 3.2%, 13%로 나타났다. 에너지변환효율은 인가전압 의존성을 보여주었으며 0.5V의 전압을 인가하였을 경우 최대값을 보여주었다. 한편 전체 광전류의 발생은 산화티타늄 공핍층 내의 전자-정공쌍의 생성반응에 의해 율속되었다. 광학농도가 증가하면 플랫-밴드전압은 -0.065V/decade의 기울기를 나타내었으며 전해액의 pH가 감소하면 플랫-밴드전압은 양의 방향으로 이동하였으며 그 기울기값은 0.059V/pH로 Nernst 식의 기울기값과 일치하였다.

• 청정기술
• /
• 제18권2호
• /
• pp.183-190
• /
• 2012

PCB에칭에 의해 발생한 염화철 폐식각액 중 염화철을 산화시키고 구리를 석출시키는 전기화학적 재생공정은 환경오염을 줄이면서도 부산물을 얻어내어 경제성이 크다. 그러나, 염화철 폐식각액은 철과 구리, 두 가지 금속이 함께 함유되어 있기 때문에 전해조에서 일어나는 반응이 복잡하다. 본 연구에서는 회분식 공정을 통하여 전기화학적인 염화철 산화 및 구리 석출반응의 특성을 조사하고 관련된 공정변수들의 최적 조건을 도출해내었다. 염화철의 산화는 항상 원하는 수준으로 되었으며, 탄소 음전극을 사용한 반응에서 $350mA/cm^2$의 전류밀도와 12 g/L의 구리 농도 조건에서, $Fe^{2+}$이온의 비율이 높을수록 구리 석출 효율이 높았다. 또한, 도출해낸 최적 조건을 바탕으로 Bench 장치 연속운전을 통해서 scale-up 가능성을 확인하였다.