Alginate obtained from marine brown algae, is a copolymer with repeating units of $\alpha$-($1{\rightarrow}4$)-L-guluronic acid(G) and $\beta$-($1{\rightarrow}4$)-D-mannuronic acid(M). It has good properties such as biocompatibility, non-toxicity. and hydrophilicity. However, alginate alone cannot be electrospun due to high viscosity and conductivity. To solve this problem. electro spinning of sodium alginate(SA) was performed by blending with poly(ethylene oxide)(PEO) and poly(vinyl alcohol)(PVA) in this study. Characteristics of SA/PEO nanofibers and SA/PVA nanofibers were estimated by SEM and XRD analyses. Optimal nanofiber webs are obtained from 2/2 wt% of SA/PEO and 2/7 wt% of SA/PVA. SA/PEO and SA/PVA nanofiber webs may have potentials for tissue engineering scaffold and wound dressing.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.08a
• /
• pp.383-383
• /
• 2012

최근 나노 소재의 활용 가능성이 확대되어감에 따라 다양한 소재의 나노구조체에 대한 연구가 진행되어 왔다. 그 중 은(Silver)은 열전도율과 전기전도율이 가장 우수한 금속으로 다양한 형태의 은 나노 입자를 형성할 수 있고. 이를 탄소, 비석, 고분자 등의 기판에 다양한 방법으로 성장시키는 연구가 진행되었다. 기판으로 사용되는 재료 중 탄소 복합소재는 내열성, 화학적 안정성, 열전도성, 저열팽창성에 따른 치수 안정성, 유연성 등의 우수한 특징을 지니고 있으며 최근까지 방열 소재로서 활용되고 있다. 본 연구에서는 탄소섬유의 표면에 다양한 결정 구조를 가지는 Ag seed 입자를 형성하고 폴리올 공정을 통하여 와이어 형태의 나노구조체를 성장시켜 그 형상제어 특성을 FE-SEM을 통하여 확인하였다.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.10 no.2
• /
• pp.176-183
• /
• 2022

High-purity waste CNTs were mixed into cement mortar to manufacture heat-generating concrete that can use low voltage power, and carbon fiber and waste cathode materials were also used improve the conductivity of the mortar. The waste CNTs were analyzed to have a high concentration of multi-walled CNTs, and substituted liquid type waste CNTs were used during mortar mixing in order to increase dispersibility. The temperature change of the mortar with CNT was evaluated when using electric power below DC 24 V in order to utilize a small self-generation facility such as small solar power module when the mortar heats up and to minimize electromagnetic waves. When liquid-type waste CNTs were applied and a voltage of DC 24 V was introduced, it rose to 60 ℃ in a 200 × 100 × 50 mm mortar block specimen. The field applicability of self heating mortar with waste CNT was sufficient and also the amount of change in heat energy in mortar with liquid type waste CNT, carbon fiber and waste cathode materials is more effective compared to it of other variables.

• Journal of Korean Tunnelling and Underground Space Association
• /
• v.17 no.2
• /
• pp.107-115
• /
• 2015

As TBM construction method is widely applied to construct underground transmission lines, increasing attention has been drawn to SFRC(steel fiber reinforced concrete) segment with respect to structural characteristics. Health hazards of electromagnetic wave which the underground transmission lines emit has emerged, and there is a concern that electromagnetic wave can be amplified because a segment characteristic such as electrical conductivity is changed by steel fibers. In order to analyze correlation between steel fiber dosage and electromagnetic wave, the specimens were fabricated on three conditions to perform experimental tests. From the measured data, it is proven that there is no correlation between the electromagnetic wave and steel fiber reinforced concrete.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.08a
• /
• pp.160-160
• /
• 2012

산화아연, 산화니켈, 산화망간 등 금속산화물은 전기적, 광학적 및 화학적 특성이 우수하여 태양전지, 연료전지, 광촉매, 가스센싱 등 다양한 분야에 폭 넓게 활용되고 있다. 또한, 그 성장방법에 따라 다양한 형태와 크기를 제어할 수 있으며 각각의 응용되는 분야에서 요구되는 나노구조를 최적화할 수 있는 장점을 갖고 있다. 그 중, 전기화학증착법(electrochemical deposition method)은 기존의 제작방법에 비해서 간단한 공정과정과 저온성장이 가능하기 때문에 많이 사용하고 있으며, 씨드(seed)층의 형성을 통해서 원하고자하는 부분에 성장시킬 수 있다. 한편, 나노기술의 발전과 함께 IT기술이 일상생활에 밀접해지면서 구부리거나 휴대 또는 입을 수 있는 다양한 전자 및 광전자 소자의 기술 개발이 활발하게 이루어지고 있는데, 이와 더불어 다양한 금속산화물 여러 가지 플렉서블 기판에서의 나노구조의 성장 및 제어에 대한 연구가 시도되고 있다. 본 연구에서는, 전기화학증착법을 이용하여 전도성 섬유와 ITO/PET 기판을 포함한 다양한 플렉서블 기판에 산화아연, 산화니켈, 산화망간의 나노구조물을 제작하였다. 실험을 위해, 용액의 농도, 시간, 인가전압을 바꿔가면서 성장조건을 달리하여 다양한 형태와 크기의 금속산화물의 나노복합구조를 형성 및 제어를 할 수 있었다. 또한, 스퍼터링 또는 스핀코팅을 이용하여 다양한 유연기판에 씨드층을 형성함으로써 금속산화물 나노구조를 균일하고 조밀하게 성장시킬 수 있었다. 플렉서블 광전소자 응용을 위해 다양한 형태로 제작된 샘플의 결정구조와 형태, 광학적 특성, 표면특성과 같은 물리적 특성을 조사하였다.

• Journal of Sensor Science and Technology
• /
• v.23 no.6
• /
• pp.383-387
• /
• 2014

Electrically conductive polypyrrole-polyvinylpyrrolidone (PPy-PVP) nanofiber mats with a core-shell structure have been successfully fabricated by a two-step process: the formation of FeCl3-containing PVP nanofiber mat by electrospinning, and the vapor-phase polymerization (VPP) of pyrrole monomer on the mat in a sealed chamber at room temperature. Surface morphology and chemical composition of the PPy-PVP mat were characterized by SEM, EDX and FTIR analyses. The as-prepared nonwoven mat was composed of PPy-PVP nanofibers with an average diameter of 300 nm. The sheet conductivity of the nanofiber mat was measured to be approximately 0.01 S/cm by a four-point probe. We have also investigated gas-sensing properties of PPy-PVP nanofiber mat upon exposure to methanol vapor. The PPy-PVP nanofiber sensors were observed to have excellent methanol-sensing performance. The nanofiber-based core-shell nanostructure could give an opportunity to fabricate a highly sensitive and fast response sensor due to its high surfaceto-volume ratio.

• Journal of Ocean Engineering and Technology
• /
• v.23 no.3
• /
• pp.35-39
• /
• 2009

The main objective of this study was to investigate fiber reinforced composite materials (FRCM) with electromagnetic shielding characteristics using aluminum (Al) film and copper (Cu) meshes. This study investigated the electromagnetic interference (EMI) shielding effectiveness (SE) of fiber reinforced composites filled with Al film, Cu meshes, and nano carbon black as hybrid conductive fillers to provide the electromagnetic shielding property of the fiber reinforced composites. The coaxial transmission line method of ASTM D 4935-89 was used to measure the EMI shielding effectiveness of composites in the frequency range of 300 MHz to 1.5 GHz. The variations of SE of FRCM with Al film, fine Cu, and general Cu meshes are described. The results indicate that the FRCM having Al film exhibited up to 75 dB of SE at 1.5 GHz.

• Journal of the Korea Institute of Military Science and Technology
• /
• v.27 no.4
• /
• pp.528-534
• /
• 2024

In continuous research of detecting highly toxic chemical warfare agents to ensure preparedness for the future battlefield, flexible and wearable sensor platforms with high sensitivity are still demanding. Herein we demonstrate a facile fabrication of polypyrrole-based chemiresistors on cellulose paper for the detection of nerve gas simulants. In order to optimize electrical properties of sensor platform, conducting polymer made of polypyrrole were first synthesized on flexible cellulose paper and interdigitated electrodes were formed thereon. Following confirmation of polypyrrole and/or oxime moiety through FT-IR analyses, electrical characteristics were measured in the various ratio of monomers between simple pyrrole and oxime-modified one. Typically for the optimized chemiresistor(2:8 molar ratio of simple pyrrole and oxime-modified one), eleven species of chemical warfare agents were examined and enhanced conductivity(10⁴~10⁵ order) was observed for three simulants(diethyl cyanophosphonate, diisopropyl fluorophosphonate and diethyl chlorophosphonate), which was mainly attributed to intermolecular hydrogen bonding, while no significant responses was recorded against sixteen common volatile organic chemicals.

• Journal of Korean Society of Environmental Engineers
• /
• v.34 no.11
• /
• pp.757-764
• /
• 2012

The surface of graphite fiber fabric anode was modified with a hydrogel and a mixture of hydrogel and multiwall carbon nanotube, and their effectiveness were compared to the unmodified anodes in a batch microbial fuel cell (microbial fuel cells). The maximum power density of the MFC was determined by both performance of the anode and cathode. The maximum power density for the MFC with the anode modified with the mixture of hydrogel and multiwall carbon nanotube was $1,162mW/m^2$ which was 27.7% higher than that with the unmodified graphite fiber fabric anode. "The mixture of hydrogel and multiwall carbon nanotube is a good surface modifier for anode with high biological affinity and low activation losses."

• Proceedings of the Korean Society of Dyers and Finishers Conference
• /
• 2011.03a
• /
• pp.58-58
• /
• 2011

CNT 나노기술을 응용한 IT산업용 적층간지용 ESD(정전방전, Electrostatic Dissipation)PU 발포필름의 제조 가공기술 및 상품화 개발은 전자제품 패키지에 요구되는 쿠션성과 정전방전 기능을 갖는 폴리우레탄 발포 필름의 제조기술을 확립함으로써 가능 할 수 있다. 특히 IT산업용 필름제품이 개발되면 ESD 성능을 발휘하게 됨으로서 정전기 쇼크에 의한 각종 전자제품의 오작동이나 파손 방지가 가능하게 되어 포장재, 자동차, 전자제품의 하우징 등으로 사용될 수 있게 된다. 현재까지 ESD 기능을 부여하기 위해서 사용되는 충전재로는 금속섬유, 금속플레이크, 탄소섬유, 카본블랙 등이 있으며, 최근 탄소나노튜브를 응용한 연구가 많이 진행되고 있는데 탄소나노튜브는 직경이 수십nm, 종횡비 1000이상의 나노섬유형태로 서 전기전도성이 구리수준으로 알려져 있고 소량을 충전할 시 기계적 특성도 오히려 증대하는 장점을 가지고 있으며 전기적 특성으로는 상대적으로 낮은 나노튜브 함량에서는 ESD를 들 수 있고 높은 함량에서는 전자파 차폐성까지 기대되고 있다. 본 연구에서는 우수한 인장강도, 기계적 강도, 열적 안정성, 내약품성을 가지면서 습식 또는 용융공정을 통해 용이하게 시트, 필름, 코팅제를 제조할 수 있는 방수, 투습방수성을 가지는 유연재료인 폴리우레탄(PU) 1액형 PU에 MWNT 함량이 3wt%인 IPA/MWNT 분산용액을 PU 함량 대비 20, 30, 40파트로 함유시켜 $120^{\circ}C$에서 2분 건조시켜 제조한 그라운드 필름에 2액형 PU와 IPA/MWNT 분산용액에 발포제를 첨가하여 발포온도 140, 150, $160^{\circ}C$에서 5분간 건조시켜 시료 필름을 제조하였다. 제조된 필름의 전기전도성 측정은 부피저항과, 표면저항을 각각 측정하여 확인하였으며, 필름의 마찰 대전압은 E.S.T-7 마찰 대전압 시험기를 이용하여 표면 마찰 대전압과 반감기를 측정하여 확인하고, 필름의 물리적 특성은 인장시험기를 이용하여 breaking stress, breaking strain을 구하였다. 필름의 표면 특성은 영상 현미경 시스템을 사용하여 ${\times}1000$ 배율로 측정하여 분산특성과의 연관성을 확인하였다.