• Tribology and Lubricants
• /
• v.10 no.3
• /
• pp.29-38
• /
• 1994

The friction and wear of mild steel at dry sliding surfaces under different vacuum conditions have been investigated to understand the wear mechanisms. For the test, a ball-ondisk typed wear-rig has been built and implemented, allowing control of sliding speed, load and vacuum. Results show that, at a high sliding velocity, friction of low carbon steel (SS41) under a high vacuum is much higher than that of ambient condition and wear is much severer. It is due to lack of effective oxidation film formation on which steel surfaces could protect themselves against the severe wear. It has been shown, however, that there is a critical regime with contact conditions (at a low sliding velocity, a low load, and under a medium vacuum) at which effective, protective films of low carbon steel have been built on the surfaces in a friction process with a self-regulating way, resulting in both very low coefficients of friction (about 0.3) and mild wear. In order to investigate the protective films on steel surfaces, the worn surfaces and the wear debris have been experimentally analyzed with SEM, AES/SAM and XRD. A theoretical analysis of frictional heating at sliding surfaces, and an experimental analysis of the influence of oxidation wear under various vacuum conditions are described. The important variables on which self-formations of protective films at dry sliding surfaces depend, and the wear mechanisms are also investigated.

• Journal of the Korean institute of surface engineering
• /
• v.43 no.4
• /
• pp.205-210
• /
• 2010

The A106 Gr B low carbon steel, which was used in the electric power plants and heavy chemical plants, was welded by multi-pass arc welding. The heat affected zone (HAZ) formed by welding was corroded in acid chloride solution, or in saturated $H_2S$ containing acid chloride solution, or in saturated $H_2S$ containing acid chloride solution under applied current. In this order of corrosion solution, the rate of corrosion increased, because $H_2S$ accelerated the iron dissolution, hydrogen evolution, and the formation of nonprotective FeS, whereas the applied current accelerated the electrochemical reaction. The scales formed in acid chloride solution consisted primarily of $Fe_3O_4$, while those formed in $H_2S$ containing acid chloride solution consisted primarily of $Fe_3O_4$ and FeS.

• Journal of the Korean Vacuum Society
• /
• v.10 no.2
• /
• pp.201-206
• /
• 2001

The evolution of textures in Fe-Ni alloy thin films fabricated by PVD using a sputtering method was investigated with parameters such as deposition time and chemical composition. The textures of the as-deposited films were characterized by fibre-type. In Invar alloy(Fe-36.5 wt%Ni) thin film, the <110>//ND fibre texture as a starting component changed to the <210>//ND fibre texture with increasing deposition time. In Permalloy(Fe-81 wt%Ni) thin film, a mixture of the <221>//ND and <311>//ND fibres developed at the early stage of deposition, and then transformed to the <210>//ND fibre with increasing deposition time. These texture changes were discussed in terms of relationship with the microstructural evolution of the films.

• Korean Journal of Materials Research
• /
• v.4 no.3
• /
• pp.364-375
• /
• 1994

The microstructure of medium-carbon non-heat treated steels by air-cooling shows ferritepearlite structure. Compared to the conventional Q/T steels, the strength of these steels containing V, Nb and Ti are similar to Q/T steels. However, their toughness are inferior. In this study, the mechanical properties and microstructures of low-carbon Mo bearing steels produced by direct-quenching process were investigated. Especially, the effect of Mo on the direct-quenched steels was examined. The direct-quenched steels containing Mo were found to have higher strength and toughness. Mo seemed to be effective in producing the fine structure and dense precipitates because of decreasing transformation temperature. The best results were 1211 MPa in UTS and 127.5 J in toughness in the oil quenched 0.15C+O.llV+ 0.035Nb+ 1.81Mo steel. Compared to 0.4% C microalloyed steels, this results showed that UTS increased by 45% and toughness by 2 times.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 1999.05a
• /
• pp.45-45
• /
• 1999

일반 구조용 탄소강은 수용액 중에 노출될 때 부식에 의한 손상을 받기 쉽다. 부식의 양지를 위한 방법으로 사용 매체 중에 부식억제제를 첨가하여 탄소강의 부식속도를 낮추는 방법은 흔히 사용되는 방법이다. 부식억제제는 부식억제의 원리에 따라 양극부식억제제, 음극부식억제제 그리 고 이들의 혼합부삭억 세제 둥 여러 종류가 목적에 따라 사용되고 있다. 일반적으로 부식억제제의 성능 평가에는 무게감량볍, 표면분석법, 분극거동측정, 부석전위, 선 형분극법에 의한 부식속도 측정 등 다양한 방법이 시도되고 있다. 이 중에서 전기화학적 평가볍 은 부삭억제제의 작용 기구 규명 등을 위하여 많이 사용되고 있다. 한편 제품의 개발 단계에서 실질적인 평가법으로 갈리 사용하고 있는 방법은 무게 감량법인데 이 방법은 전면부식에 의한 금 속 손실량을 측정하여 부식억제능을 측정하는 방법이다. 그러냐 실제로 부삭억제제가 사용되고 있는 환경에서의 부식양상을 판찰하여보면 전면부식에 의한 손상보다는 국부부식에 의한 손상이 보다 치명적언 경우를 종종 목격할 수 있다. 이러한 관점에서 가존의 무게감량법은 한계가 있다. 따라서 본 연구에서는 이러한 국부부식을 보다 효과적으로 평가하기 위해 새로운 시험법을 도 입 상용 부식억제제의 종류별로 비교하였다. 부식억제제로는 수용액 중의 부식억제제로 널리 사용되고 있는 Nalco 39L과 본 연구실에서 SK해미칼과 공동 개발한 GH-110 등에 대하여 MCA(Multiple Crevice Assembly)를 이용 틈부식 저항성을 평가하였다. 또한 박막화된 전기저항형 부석속도 측정 센서를 틈부식 형태의 부식측정 에 적용하는 연구를 행하였다. 시험에 사용한 재갚는 천연가스의 감압 온도보상용으로 운전하는 가스히터의 주 구성 재료인 저탄소강을 사용하였으며 열화된 부식억제제 용액으로 사용기간이 서로 다른 수용액들에 대하여 평가 방법을 적용하여 비교하였다 다양한 부식억 제 제 수용액을 비교한 결과 MCA(Multiple Crevice Assembly)를 이용한 틈부식 억제능 시험은 실제 현장 사험 결과와 어느 정도 일치하는 결과를 보였다. 새로운 틈부식 저항성 측정법으로 시도한 철박막을 이용 틈부식 측정법은 육안 검사를 실시하지 않고도 틈부식의 전행 여부를 확인할 수 있는 가능성을 확인하였다.

• Journal of Conservation Science
• /
• v.30 no.4
• /
• pp.335-343
• /
• 2014

This study classified the result of non-metallic inclusion analysis and result of microstructure investigation on the ironware excavated in the Baekje region into Han River, Geum River, and Yeongsan River to estimate the iron making temperature and study the characteristics of regional and temporal characteristics of the heat treatment technology and steel making technology. Regardless of era, bloom iron and sponge iron are judged to be the major method for making as a directreduction process in all three regions. The result of the reinterpretation of the non-metallic inclusion by the oxide ternary constitutional diagram suggest that the temperature inside of the furnace is estimated to be between $1,100{\sim}1,300^{\circ}C$ while making the steel. The magnetic iron ores are the major raw material of steel ore and irons with high $TiO_2$ are estimated to use iron sands. Ironware with $CaO/SiO_2$ rate higher than 0.4% are considered to have artificially added the flux of calcareous materials. It was found that the iron making method is the solid caburizing-steel which caburizes low-carbon steels by the CO gas and $CO_2$ gas created when heating the forging furnace with charcoal. Also, the ironware manufacturers in the Baekje during 3rd century recognized the heat treatment technology as they performed carburizing process and quenching to intentionally increase the strength of necessary parts.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.14 no.6
• /
• pp.1552-1560
• /
• 1990

A general form of the mathematical function in the fatigue crack growth rate law for CT specimens was determined by means of the dimensional analysis at elevated temperatures. The experimental results can be rigorously described by the combination of rate theory and fracture mechanics. The rate theory approach extends the scope of fracture mechanics through the consideration of the temperature. The fatigue crack growth rates are represented by the Arrhenius type equation. This equation explains fairly well the experimental data for Cr-Mo-V rotor steel and A517-F steel in the comparatively wide temperature regions as affected with the temperature and the stress intensity factor range interaction.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.22 no.4
• /
• pp.665-672
• /
• 2013

With the development of advanced processing technology, laser processing systems, which require high-quality precision processing, have attracted considerable attention. Although laser equipment is expensive, it enables quick processing and less deformation of materials. This technology is often applied to secondary batteries, which has thus farinvolved the use of argon tungsten inert gas (TIG) welding. However, the welding characteristics of argon TIG welding are not yet good, and a laser is used for welding to address this problem. In this study, lap-joint welding was conducted, and the desired welding characteristics were obtained when the laser power was 1800W and the laser beam travel speed was 1.8 m/min. Lap-joint welding was conducted on Ni-coated SS41. Two cases were compared. No pores were observed in the Ni-coated SS41 lap-joint welding part, and cracks appeared from the lap-joints. Moreover, the pole rod and tap were welded together in a T-joint form to improve the output of the secondary battery. T-joint laser welding showed better welding characteristics than TIG welding.

• Journal of the Korean Society for Heat Treatment
• /
• v.18 no.1
• /
• pp.29-40
• /
• 2005

Formation of nanocrystalline ferrite was investigated using milled powders obtained by planetary ball milling of chips, which were made by high speed mechanical cutting of a low carbon steel(0.15%C-1.1%Mn-0.01%Ti). After 4 hour milling the chips were changed to powders of $50{\mu}m$ in average size, and with increasing milling time the powders were refined to about $3{\mu}m$ for 128 hour and showed more equiaxed shapes. Nanocrystalline(nc) region appeared in the surfaces of powders milled for 1 hour, and the 4 hour milled powders were almost filled with nc region. Hardness of nc region was much higher than that of work-hardened(WH) region. With increasing milling time, ferrite and cementite in pearlite were severely deformed and lamellar spacing was decreased, and then cementites began to disappear after 4 hour milling due to dissolution into ferrite. Deformation bands formed in lightly work-hardened region showed large width and similar crystallographic orientations. Spacing of deformation bands was decreased with deformation and the layered microstructure consisting of narrow deformation bands subdivided into variously oriented small grains was formed by more deformation, and eventually this structure seemed to be evolved to the nc structure by further deformation. It is also conjectured the growth of nc ferrite grains occurred through the coalescence of nanocrystalline ferrites rather than the nucleation and growth of recrystallized grains.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2004.08a
• /
• pp.307-316
• /
• 2004

This study examined the cause of the wrinkle defect which is frequently encountered in wire rod rolling of low carbon steel$(C0.08\~0.13wt.\%)$. Even a small defect on the surface of rolled bars can easily develop into fatal cracks during cold heading process of low carbon steel, and it is therefore necessary to minimize inherent defects on the surface of hot rolled bars. Hot rolling process of low carbon steel was analyzed to identify the cause of the wrinkle defect in conjunction with FE analysis. The integrated analysis revealed that the wrinkle defect initiated in the first stage of rolling, and it was at the billet edge where severe deformation and drastic temperature drop were present. To elucidate the micro-mechanical mechanism of the wrinkle defect, hot compression tests were carried out at various temperatures and strain rates using Gleeble-3800. The surface profile of the each other compressed specimens was compared, and rough surface lines were observed at relatively low temperatures. Those surface defects can develop into wrinkles during multi-pass rolling. To control the wrinkle defect in rolling, it is necessary to design an adequate caliber which can minimize the loss of ductility, and thereby prevent flow localization. To use the result of this study fur other steels, the quantitative measure of the wrinkle defect and flow localization parameter should be proposed.