• Clean Technology
• /
• v.21 no.3
• /
• pp.200-206
• /
• 2015

In order to investigate the effect of cerium oxide addition, Cu-ZnO-CeO₂ catalysts were prepared using co-precipitation method for water gas shift (WGS) reaction. A series of Cu-ZnO-CeO₂ catalyst with fixed Cu Content (50 wt%, calculated as CuO) and a given ceria content (e.g., 0, 5, 10, 20, 30, 40 wt%, calculated as CeO₂) were tested for catalytic activity at a GHSV of 95,541 h^-1, and a temperature range of 200 to 400 ℃. Cu-ZnO-CeO₂ catalysts were characterized by using BET, SEM, XRD, H₂-TPR, and XPS analysis. Varying composition of Cu-ZnO-CeO₂ catlysts led the difference characteristics such as Cu dispersion, and binding energy. The optimum 10 wt% doping of cerium facilitated catalyst reduction at lower temperature and improved the catalyst performance greatly in terms of CO conversion. Cerium oxide added catalyst showed enhanced activities at higher temperature when it compared with the catalyst without cerium oxide. Consequently, ceria addition of optimal composition leads to enhanced catalytic activity which is attributed to enhanced Cu dispersion, lower binding energy, and hindered Cu metal agglomeration.

• Journal of Sericultural and Entomological Science
• /
• v.47 no.1
• /
• pp.36-40
• /
• 2005

This studies were carried out to develop the new silk degumming method by elelectrolyzed alkaline water on the silk degumming process. Using to this method, it could be collect pure sericin from the degumming water, because the degumming water by elelectrolyzed alkaline water was not contaminated by chemicals including soap. The range of elelectrolyzed alkaline water was pH 11.5 to 11.7 and maintained the first value for 8 days under the cool and closed conditions. The degumming ratio of silk was higher in elelectrolyzed alkaline water(pH 11.5~11.7)than that of soap and alkaline bath. When the pH value of elelectrolyzed alkaline water was adjusted at pH 11.0, the degumming ratio of silk was similar to that of soap and alkaline degumming. After degumming the pH value of degumming water decreased largely in the elelectrolyzed alkaline water compared to that of soap and alkaline bath. The tenacity and elongation of degummed silk by elelectrolyzed alkaline water was almost same those of soap and alkaline degumming for 90 min.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2001.11a
• /
• pp.28-28
• /
• 2001

$Bi_2Te_3$계 열전반도체 재료는 200 ~ 400K 정도의 저온에서 에너지 변환 효율이 가장 높은 재료로서 열전냉각 및 발전재료로 제조볍 및 특성에 관한 많은 연구가 진행되어 왔다. 전자냉각 모듈의 제조에는 P형 및 N형 $Bi_2Te_3$계 단결정이 주로 사용되고 있으나. $Bi_2Te_3$ 단결정은 C축에 수직한 벽개면을 따라 균열이 쉽게 전파하기 때문에 소자 가공사 수윤 저하가 가장 큰 문제점으로 지적되고 있다. 이에 따라 최근 열전재료의 가공방법에 따른 회수율 증가 및 열전특성 향상에 관한 열간압출, 단조와 같은 연구가 활발히 이루어지고 있다. 본 연구는 가스분사법(gas atomizer)을 이용하여 용질원자 편석의 감소, 고용도의 증가,균일고용체 형성, 결정립미세화 둥 급속응고의 장점을 이용하여 화학적으로 균질한$Bi_2Te_3$계 열전재료 분말을 제조하고, 제조된 분발을 압출가공하여 기계적성질, 소자의 가공성 및 열전 성능 지수율 향상시키는데 연구 목적이 있다. 본 설험에서는 99.9%이상의 고순도 Bi. Te. Se. Sb를 이용하여, 고주파 유도로에서 Ar 분위기로 용융하고, 가스분사법를 이용하여 균질한 $Bi_2Te_3$계 열전재료 분만을 제조하였다. 분말표면의 산화막을 제거하기 위하여 수소분위기에서 환원처리를 행하였고, 된 분말을 Al 캔 주입하여 냉간성형 한 후 진공중에서 압출온도를 변화시켜 열간압출 가공을 행하였다. 압출 온도변화에 따른 압출재의 미세조직 및 열전특성에 중요한 영향을 미치는 C면 배향에 대한 결정방위 해석, 압출재의 압축강도 등을 분석하였으며, 압출온도에 따삼 미세조직 변화와 결정방위의 변화에 따른 열전특성의 관계를 해석하였다성시켰고 이들이 산인 HNO3에서 녹았기 때문이다. 본 연구에서 개발된 새로운 에칭 용액인 90H2O2 - 10HNO3 (vol%)의 에칭 원리가 똑같이 적용 가능한 다른 종류의 초경 합금에서도 사용이 가능할 것으로 판단된다.로 판단된다.멸과정은 다음과 같다. 출발물질인 123 분말이 211과 액상으로 분해될 때 산소가스가 배출되며, 이로 인해 액상에서 구형의 기공이 생성된다. 이들 중 일부는 액상으로 채워져 소멸되나, 나머지는 그대로 남는다. 특히, 시편 중앙에 서는 수십-수백 마이크론 크기의 커다란 기공이 다수 관찰된는데, 이는 기공의 합체로 만들어진 것이다. 포정반응 열처리 시 기공 소멸로 만들어진 액상포켓들은 주변 211 입자와 반응하여 123 영역으로 변한다. 이곳은 다른 지역과 비교하여 211 밀도 가 낮기 때문에, 미반응 액상이 남거나 211 밀도가 낮은 123 영역이 된다. 액상으로 채워지지 못한 구형의 기공들 중 다수가 123 결정 내로 포획되며, 그 형상은 액상/ 기공/고상 계면에너지에 의해 결정된다.단의 경우, 파단면이 매끄럽고 파변상의 결정립도 매우 미세하였으며, 산확물 의 용집도 찾아보기 어려웠 나, 접합부 파단의 경우에는 파변의 굴곡이 비교척 심하고 연성 입계파괴의 형태를 보였￡며, 결정립도 모채부 파단의 경우에 비해 조대하였다. 조대하였다. 셋째, 주상기간 중 총 에너지 유입률 지수와 $Dst_{min}$ 사이에 높은 상관관계가 확인되었다. 특히 환전류를 구성하는 주요 입자의 에너지 영역(75~l13keV)에서 가장 높은(0.80) 상관계수를 기록했다. 넷째, 회복기 중에 일어나는 입자들의 유입은 자기폭풍의 지속시간을 연장시키는 경향을 보이며 큰 자기폭풍일수록 현저했다. 주상에서 관측된 이러한 특성은 서브스톰 확장기 활동이 자기폭풍의

• Journal of the Microelectronics and Packaging Society
• /
• v.21 no.2
• /
• pp.79-84
• /
• 2014

To investigate the plating properties of a diethylene glycol-based Ag immersion plating solution containing citric acid, silver immersion plating was performed in a range from room temperature to $50^{\circ}C$ using sputtered Cu specimens. The used Cu specimens possessed surface structure with large numbers of pinholes which were created with over-acid etching. The Ag immersion plating performed at $40^{\circ}C$ exhibited that the pinholes and copper surface were completely filled with Ag just after 5 min mainly due to galvanic displacement reaction, indicating the best plating properties. Subsequently, the surface morphology of Ag-coated Cu became rougher as the plating time increased to 30 min because of the deposition of silver nanoparticles created by chemical reduction in the solution. The specimen that its overall surface was covered with silver indicated the start of oxidation at temperature higher than around $50^{\circ}C$ in air as compared with pure Cu, indicating enhanced anti-oxidation properties.

• Korean Chemical Engineering Research
• /
• v.48 no.3
• /
• pp.304-310
• /
• 2010

The FTS(Fischer-Tropsch synthesis) was carried out over precipitated iron-based catalysts with or without $SiO_2$ in a fixed-bed reactor at $250^{\circ}C$ and 1.5 MPa. The catalysts with $SiO_2$ showed much higher catalytic activity for the FTS than those without $SiO_2$, displaying excellent stability during 144 h of reaction. The X-ray diffraction and $N_2$ physisorption revealed that the catalysts with $SiO_2$ showed enhanced dispersion of $Fe_2O_3$ compared with those without $SiO_2$. Also, the results of temperature-programmed reduction by $H_2$ showed that the addition of $SiO_2$ markedly promoted the reduction of $Fe_2O_3$ into $Fe_3O_4$ and FeO at low temperatures below $260^{\circ}C$. In contrast, surface basicity of the catalysts, which was analyzed by temperature-programmed desorption of $CO_2$, decreased as a result of $SiO_2$ addition. We attribute the high and stable performance of the catalysts with $SiO_2$ to the improved dispersion and reducibility by the $SiO_2$ addition.

• Journal of the Korean Electrochemical Society
• /
• v.6 no.1
• /
• pp.41-47
• /
• 2003

For the development of low temperature anode-supported planar solid oxide fuel cell, the planar anode supports with the thickness of 0.8 to 1 mm and the area of 25, 100 and $150\;cm^2$ were fabricated by the tape casting method. The strength, porosity, gas permeability and electrical conductivity of the planar anode support were measured. The porosity of anode supports sintered at $1400^{\circ}C$ and then reduced in$H_2$ atmosphere was increased from $45.8\%\;to\;53.9\%$. The electrical conductivity of the anode support was $900 S/cm\;at\; 850^{\circ}C$ and its gas permeability was 6l/min at 1 atm in air atmosphere. The electrolyte layer and cathode layer were fabricated by slurry dip coating method and then had examined the thickness of $10{\mu}m$ and the gas permeability of 2.5 ml/min at 3 atm in air atmosphere. As preliminary experiment, cathode multi-layered structure consists of LSM-YSZ/LSM/LSCF. At single cell test using the electrolyte layer with thickness of 20 to $30{\mu}m$, we achieved $300\;mA/cm^2$ and 0.6V at $750^{\circ}C$

• Journal of Conservation Science
• /
• v.32 no.4
• /
• pp.579-588
• /
• 2016

This study analyzed nonmetallic inclusions in iron swords with a ring pommel excavated in the Ipbuk-dong, Suwon. Scanning electron microscopy with energy dispersive spectroscopy(SEM-EDS) was used to estimate the iron-making temperature, and we compared the oxide with $SiO_2$ to investigate the heat-treatment technology in the production of iron swords with a ring pommel by investigating the artificial insertion of a slag former and the metallurgical structure. From the wustite observed in most of the specimens, it is judged that these swords were produced by heating and forging iron smelted at a low temperature using the solid reduction method. In addition, judging from the partial presence of $P_2O_5$, it is assumed that they were smelted directly with natural ore, not calcined. From the ratios of $CaO/SiO_2$ and $TiO_2/SiO_2$, it is judged that the raw material for iron-making was iron ore and that a calcareous slag former was not artificially inserted. The structure of the blade part on the front end was pure iron. From the high carbon content of the blade part on the ring pommel and the formation of a martensitic structure and pearlite colony, it is judged that they were tempered after carburizing and that the back, handle part, and ring pommel were unintentionally carburized. Judging from the structure of these specimens, it was noted that they were produced by applying artificial partial heat-treatment technology. This study attempted to present a more scientific analysis by using the method of interpretation through component analysis of nonmetallic inclusions appearing in one relic by the ratio of the oxide divided by $SiO_2$. It is judged that reinterpreting the arguments by the results of the existing analysis and research in this way can obtain different interpretations.

• KOREAN JOURNAL OF CROP SCIENCE
• /
• v.36 no.5
• /
• pp.407-428
• /
• 1991

The eastern coastal area having variability of climate is located within Taebaek mountain range and the east coast of Korea. It is therefore ease to cause the wind damages in paddy field during rice growing season. The wind damages to rice plant in this area were mainly caused by the Fohn wind (dry and hot wind) blowing over the Taebaek mountain range and the cold humid wind from the coast. The dry wind cause such as the white head, broken leaves, cut-leaves, dried leaves, shattering of grain, glume discolouration and lodging, On the other hand the cold humid wind derived from Ootsuku air mass in summer cause such symptom as the poor rice growth, degeneration of rachis brenches and poor ripening. To minimize the wind damages and utilize as a preparatory data for wind injury of rice in future, several experiments such as the selection of wind resistant variety to wind damage, determination of optimum transplanting date, improvement of fertilizer application methods, improvement of soils and effect of wind break net were carried out for 8 years from 1982 to 1989 in the eastern coastal area. The results obtained are summarized as follows. 1. According to available statisical data from Korean meteorological services (1954-1989) it is apperent that cold humid winds frequently cause damage to rice fields from August 10th to September 10th, it is therefore advisable to plan rice cultivation in such a way that the heading date should not be later than August 10th. 2. During the rice production season, two winds cause severe damage to the rice fields in eastern coastal area of Korea. One is the Fohn winds blowing over the Taebaek mountain range and the other is the cold humid wind form the coast. The frequency of occurrence of each wind was 25%. 3. To avoid damage caused by typhoon winds three different varieties of rice were planted at various areas. 4. In the eastern coastal area of Korea, the optimum ripening temperature for rice was about 22.2$^{\circ}C$ and the optimum heading date wad August 10th. The optimum transplanting time for the earily maturity variety was June 10th., medium maturity variety was May 20th and that of late maturity was May 10th by means of growing days degree (GDD) from transplanting date to heading date. 5.38% of this coastal area is sandy loamy soil while 28% is high humus soil. These soil types are very poor for rice cultivation. In this coastal area, the water table is high, the drainage is poor and the water temperature is low. The low water temperature makes it difficult for urea to dissolve, as a result rice growth was delayed, and the rice plant became sterile. But over application of urea resulted in blast disease in rice plants. It is therefore advise that Ammonium sulphate is used in this area instead of urea. 6. The low temperature of the soil inhibits activities of microorganism for phosphorus utilization so the rice plant could not easily absorb the phosphorus in the soil. Therefore phosphorus should be applied in splits from transplanting to panicle initiation rather than based application. 7. Wind damage was severe in the sandy loamy soil as compared to clay soils. With the application of silicate. compost and soil from mointain area. the sand loamy soil was improved for rice grain colour and ripening. 8. The use of wind break nets created a mocro-climate such as increased air. soil and water temperature as well as the reduction of wind velocity by 30%. This hastened rice growth, reduced white head and glume discolouration. improved rice quality and increased yield. 9. Two meter high wind break net was used around the rice experimental fields and the top of it. The material was polyethylene sheets. The optimum spacing was 0.5Cm x 0.5Cm. and that of setting up the wind break net was before panicle initiation. With this set up, the field was avoided off th cold humid wind and the Fohn. The yield in the treatment was 20% higher than the control. 10. After typhoon, paddy field was irrigated deeply and water was sprayed to reduce white head, glume discolouration, so rice yield was increased because of increasing ripening ratio and 1, 000 grain weight.