• Journal of the Korea institute for structural maintenance and inspection
• /
• v.26 no.1
• /
• pp.67-72
• /
• 2022

Concrete prevents corrosion of reinforcing bars due to its strong alkalinity. However, in the sea, strong alkali components with a pH of 12 to 13 are eluted, which adversely affects the ecological environment and growth of marine organisms. In this study, the mechanical properties and durability of the low alkali mortar were evaluated for the development of a low alkali mortar for the 3D printed artificial reefs. As a result of evaluation of strength characteristics, the α-35 mixture, which were produced with fly ash, silica fume and α-hemihydrate gypsum, satisfied the strength requirement 27 MPa in terms of compressive strength. As a result of pH measurement, it was found that mixing with alpha-type hemihydrate gypsum resulted in minimizing pH due to the the formation of calcium sulfate instead of calcium hydroxide production. As a result of the chloride ion penetration resistance test, the α-35 mixture exhibited the best performance, 3844C. As a result of measuring the length change over time, the α-35 mixture showed the shrinkage 33.5% less compared to the Plain mix.

• Journal of Environmental Science International
• /
• v.28 no.6
• /
• pp.561-570
• /
• 2019

A zeolitic material (Z-Y2) was synthesized from Coal Fly Ash (CFA) using a fusion/hydrothermal method under low-alkali condition (NaOH/CFA = 0.6). The adsorption performance of the prepared zeolite was evaluated by monitoring its removal efficiencies for Sr and Cs ions, which are well-known as significant radionuclides in liquid radioactive waste. The XRD (X-ray diffraction) patterns of the synthesized Z-Y2 indicated that a Na-A type zeolite was formed from raw coal fly ash. The SEM (scanning electron microscope) images also showed that a cubic crystal structure of size $1{\sim}3{\mu}m$ was formed on its surface. In the adsorption kinetic analysis, the adsorption of Sr and Cs ions on Z-Y2 fitted the pseudo-second-order kinetic model well, instead of the pseudo-first-order kinetic model. The second-order kinetic rate constant ($k_2$) was determined to be $0.0614g/mmol{\cdot}min$ for Sr and $1.8172g/mmol{\cdot}min$ for Cs. The adsorption equilibria of Sr and Cs ions on Z-Y2 were fitted successfully by Langmuir model. The maximum adsorption capacity ($q_m$) of Sr and Cs was calculated as 1.6846 mmol/g and 1.2055 mmol/g, respectively. The maximum desorption capacity ($q_{dm}$) of the Na ions estimated via the Langmuir desorption model was 2.4196 mmol/g for Sr and 2.1870 mmol/g for Cs. The molar ratio of the desorption/adsorption capacity ($q_{dm}/q_m$) was determined to be 1.44 for Na/Sr and 1.81 for Na/Cs, indicating that the amounts of desorbed Na ions and adsorbed Sr and Cs ions did not yield an equimolar ratio when using Z-Y2.

• Journal of Environmental Science International
• /
• v.31 no.2
• /
• pp.171-180
• /
• 2022

Zeolitic material, Z-Y3, was synthesized from coal fly ash (CFA) under low-alkaline conditions (NaOH/CFA ratio = 0.3 and NaOH solution concentrations of 0.0, 0.5, and 1.0 M) using a fusion/hydrothermal method. The adsorption capacities of the fabricated Z-Y3 samples for Cs and Sr ions and the desorption capacity of Na ions were evaluated. The XRD patterns of the Z-Y3 sample fabricated using a 1.0 M NaOH solution (Z-Y3 (1.0 M)) indicated the successful synthesis of a zeolitic material, because the diffraction peaks of Z-Y3 coincided with those of the Na-A zeolite in the 2θ range of 7.18-34.18. Moreover, the SEM images revealed that morphology of the Z-Y3 (1.0 M) sample, which presented zeolitic materials characteristics, consisted of sharp-edged cubes. The adsorption isotherms of Cs and Sr ions on all the fabricated Z-Y3 samples were described using the Langmuir model, and the maximum adsorption capacities of Cs and Sr were calculated to be 0.14-0.94 mmol/g and 0.19-0.78 mmol/g, respectively. The desorption of Na ions from the Cs and Sr ions adsorbed Z-Y3 samples followed the Langmuir desorption model. The maximum desorption capacities of Na ions from the Cs and Sr ions adsorbed Z-Y3 (1.0 M) samples were 1.28 and 1.49 mmol/g, respectively.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.26 no.6
• /
• pp.139-147
• /
• 2022

In this study, we designed a high-strength, low-alkali type cement composite for artificial reef by mixing various binders and evaluated whether it is possible to manufacture it with an ME method 3D printer. As a result of the tests, it is found that it is important to control the water-binder ratio, the silica sand-binder ratio, and the type of silica sand in order to control the fluidity of the cement composites to enable 3D printing. The surface quality of 3D printer output can be achieved by adjusting the amount of viscosity agent added while obtaining printable fluidity. In the cement composites mixing proportion using the alpha-type hemihydrate gypsum, a setting control agent needs to be used to control the quick setting effect. It is also necessary to derive the time to maintain the fluidity, and to apply it when printing. To obtain the required strength, the mix proportion needs to be modified while satisfying the fluidity level of 3D-printable cement composites. In the present study, 3D-printable mix proportions were designed by the use of multi-component binders including alpha-type hemihydrate gypsum a for low-alkali type artificial reefs, and the printability was confirmed. A further study needs to be performed to quantitatively evaluate the alkali reduction effect.