• Journal of the Korea Institute of Building Construction
• /
• v.13 no.3
• /
• pp.235-241
• /
• 2013

In this study, a mortar was produced using re-dispersible polymer powders that addresses the defects of aqueous polymer and improves the durability of cement mortar. Also, an attempt was made to examine the properties of polymer modified mortars using re-dispersible polymer powders by strength and durability tests between ordinary Portland cement mortars and polymer modified mortars mixed with aqueous dispersion. The test showed that strength and durability are improved considerably compared with ordinary Portland cement mortar, and the performance of aqueous polymer cement mortar was considerably improved. Accordingly, it is expected that high-quality prepackaged polymer modified mortars can be produced using re-dispersible polymer powders.

• Proceedings of the Korean Society of Agricultural Engineers Conference
• /
• 2005.10a
• /
• pp.128-134
• /
• 2005

This study was performed to evaluate the strength and durability properties of recycled concrete containing water - redispersible copolymer powder(WRP) and blast furnace slag powder(BSP) [RCWS]. Material used were cemente, recycled coarse aggregare, natural fine aggregate, water-redispersible copolymer powder, blast-furnace slag powder. Especially, Water-redispersible powder was used for blending with Inorganic binders such as cemente, gypsum and hydrated lime etc. First of all, Mixed ratio method of RCWS made Two Type. One was called type-1 which used to BSP content 5% and WRP(Water-redispersible powder) content 0%, 1%, 2%, 3%, 4%, 5%, 6%. respectively. Another was called Type-2 which used to BSP(blast furnace slag powder)content 10% and WRP(Water-redispersible powder) content 0%, 1%, 2%, 3%, 4%, 5%, 6%. respectively. According to the experimental results of (RCWS), Incase Type-2 at curing age 28days, Compressive strength, pulse velocity and dynamic modulous of elasticity were shown higher than Type-1 and The more WRP content increasing($0%{\sim}6%$) was the lower Compressive strength, Pulse velocity and Dynamic modulous of elasticity. Water absorption ratio was in the range of $3.85%\;{\sim}\;3.23%$, it was almost equal to Type-1, 2 but Increasing the WRP content($0%{\sim}6%$), The water absorption ratio is decreased.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.17 no.5
• /
• pp.94-104
• /
• 2013

Experiments were divided into two parts; one part is to understand the basic properties of high flowable VA/VeoVa-modified cement mortar with different polymer cement ratio (P/C) and the weight ratio of fine aggregate to cement (C:F) and the other part is to investigate the effect of surface water spread on the concrete substrate on adhesion in tension. To understand the basic performance, the specimens were prepared with proportionally mixing VA/VeoVa redispersible powder, ordinary portland cement, silica sand, superplasticizer and viscosity enhancing agent. Here, P/C were 10, 20, 30, 50 and 75% and C:F were 1:1 and 1:3. As the change of P/C and C:F unit weight, flow test, crack resistance and adhesion in tension were measured. Three specimens with good adhesion properties were selected among specimens with different P/C and C:F. The effect of surface water evenly sprayed on concrete substrate on adhesive strength is investigated. The results show that surface water on concrete substrate increases the adhesion in tension of high flowable VA/VeoVa-modified cement mortar and additionally improves the flowability compared to the non-sprayed case.