• Transactions of the Korean Society of Mechanical Engineers
• /
• v.18 no.8
• /
• pp.1930-1938
• /
• 1994

In this paper, the effects of temperature change on the impact of CFRP laminates was experimentally studied. Composite laminates used for this experiment are CFRP orthotropic laminated plates, which have two-interfaces$[0_6^{\circ}/90_7^{\circ}]_s$ and four-interfaces$[0_3^{\circ}/90_6^{\circ}/0_3^{\circ}]_s$. The interrelations between the impact energy vs. delamination area, the impact energy vs. residual bending strength, and the interlayer delamination area vs. the decrease of the residual flexural strength of carbon fiber epoxy composite laminates subjected to FOD(Foreign Object Damage) under high temperatures were experimentally observed.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.20 no.6
• /
• pp.1836-1842
• /
• 1996

In this paper, static and fatigue bending strengths of CFRP(carbon fiber reinforced plastic laminates having impact damage(FOD) are evaluated. Composite laminates used for this experiment are CF/EPOXY and CF/PEEK orthotropy laminated plates, which have two-interfaces[${0^0}_4{90^0}_4}$]$_sym$. A steel ball launched by the air gun colides against CFRP laminates to generate impact damages. The damage growth during bending fatigue test is observed by the scanning acoustic microscope(SAM). When the impacted side is compressed, the residual fatigue bending strength of CF/PEEK specimen P is greater that that of CF/EPOXY SPECIMEN B. On the other hand, when the impacted side is in tension, the residual fatigue bending strength of CF/PEEK speicemen P is smaller than that of CF/EPOXY specimen B. In the case of impacted-side compression, fracture is proposed from the transverse crack generated near impact point. On the other hand, fracture is developed toward the impact point from the edge of interface-b delamination in the case of impacted-side tension.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.8 no.6
• /
• pp.247-258
• /
• 2000

It is thought that impact damages and hygrothermals can affect to CFRP (Carbon-fiber reinforced plastic) composite laminated due to the sensitivity on the composite laminated Therefore, this paper focuses on the fracture mechanisms experimentally based on a scanning acoustic microscope (SAM) when subjected to impact damages, i.e., foreign object damages(FOD), and also the influence of impact damages and hygrothermals on residual fatigue bending strength of CFRP laminates. Composite laminates used in the experiment are CF/EPOXY orthotropy laminated plates, which constist of two-interfaces [04/904]s. A steel ball launched by an air gun collides against CFRP laminates to generate impact damages. Bending fatigue tests are periodically interrupted for a nondestructive evaluation (NDE) measurement of the progrossive damages to built the fracture mechanism by impact damages, and three-point fatigue bending tests are carried out to investigate the influence of hygrothermals on the effect on the residual bending fatigue strength of CFRP laminates.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.17 no.11
• /
• pp.2752-2761
• /
• 1993

The purpose of this study is to confirm the decreasing problems of residual bending strength, and the fracture machanism experimentally when CFRP composite laminates are subjected to Foreign Object Damage. Composite laminates used for this experiment are CFRP orthotropy laminated plates, which have two-interfaces [O/sub 6//sup o//90/sub 6//sup o/]sub sym/ and four-interfaces [O/sub 3//sup o//90/sub 6//sup o//O/sub 3//sup o]/sub sym/. When the specimen is subjected to transverse impact by a steel ball, the delamination area generated by impact damage is observed by using SAM(Scanning Acoustic Microscope). also, Thefracture surfaces obtained by three-point bending test were observed by using SEM (Scanning Electron Microscope). Then, fracture mechanism was investigated based on the observed delamination area and fracture surface. The results were summarized as follows; (1) It is found that for the specimen with more interface, the critical delamination energy is increased while delamination-development energy is decreased. (2) Residual bending strength of specimen A is greater than that of Specimen B within the impact range of impact energy 1. 65J (impacted-side compression) and 1. 45J (impacted-side tension). On the other hand, when the impact energy is beyond the above ranges, residual bending strength of specimen A is smaller than that of specimen B. (3) In specimen A and B, residual strength of CFRP plates subjected to impact damage is lower in the impacted-side compression than in the impacted-side tension. (4) In the case of impacted-side compression, fracture is propagated from the transverse crack generat-ed near impact point. On the other hand, fracture is developed toward the impact point from the edge of interface-B delamination in the case of impacted-side tension.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.26 no.5
• /
• pp.835-842
• /
• 2002

In this paper, static and fatigue bending strengths and failure mechanisms of CFRP (carbon fiber reinforced plastics) laminates having impact damages have been evaluated. Composite laminates used for this experiment are CF/EPOXY orthotropy laminated plates, which have two-interfaces $[0^0_ 4/90^0_4]_{ sym}$. A steel ball launched by the air gun collides against CFRP laminates to generate impact damages. The damage growth during bending fatigue test is observed by the scanning acoustic microscope (SAM) and also, the fracture surfaces were observed by using the SEM (scanning electron microscope). In the case of impacted-side compression, fracture is propagated from the transverse crack generated near impact point. On the other hand, fracture is developed toward the impact point from the edge of interface-B delamination in the case of impacted-side tension. Eventually, failure mechanisms have been confirmed based on the observed delamination areas and fracture surfaces.