• Journal of the Korean Recycled Construction Resources Institute
• /
• v.4 no.4
• /
• pp.99-104
• /
• 2009

For recycling of waste foundry sands, researchers recently try to recycle them rather than depend on reclamation, and are studying on how to combine waste foundry sands with cement and use them for various kinds of construction material as the effective recycling method of waste foundry sand. In this research, The ways to find the proper replacement rate of waste foundry sands and to make use of them were suggested through the experiments on the range to apply waste foundry sands with two levels of 1:3 mixture rate of W/C 43% and 50%. The research result showed that in terms of liquidity as the characteristic of unhardened mortar, as the replacement rate of waste foundry sands increased, its flow tended to decrease. The amount of air also displayed a similar tendency to that of liquidity in that the higher the replacement rate of waste foundry sands became, the lower it became. With regard to the solidity trait of hardened mortar, it increased when the waste foundry sands were replaced more, and the replacement of waste foundry sands caused increased initial solidity. As for the amount of water permeated and that of water absorbed as the water tight proofing properties, the amount of permeated water was proved to decrease because of the gap recharge effect by the fine powder of waste foundry sands, and the replacement of waste foundry sands in the structures requiring watertightness is concluded to be very effective.

• Korean Journal of Agricultural Science
• /
• v.8 no.2
• /
• pp.185-194
• /
• 1981

This study was carried out to determine the effect of accelerated curing on the strength of standard sand mortar and briquette ash mortar. The standard sand mortars and the briquette ash mortars made by mixture of the standard sand:cement and the briquette ash:cement at the ratio of 2 : 1, 3: 1 and 4 : 1, respectively, were cured at 4 different temperature of $20^{\circ}C$, $60^{\circ}C$, $80^{\circ}C$ and $100^{\circ}C$. The compression and tensil strength of mortars were measured at ${\sigma}_3$, ${\sigma}_7$, ${\sigma}_28$. The results obtained are summarized as follows; 1. At each age of curing and each curing temperature, the compression and tensile strength of the mortars made by the mixture of cement and standard sand was significantly higher than that of the mortars made by the mixture of cement and briquette ash. But the increasing rate of strength in compression and tension was significantly higher at the mortars of cement and briquette ash than those of cement and standard sand. 2. The strength of mortars which showed lower strength than Korean Standard at ordinary curing temperature was significantly increased and showed higher value than Korean Standard by the accelerated curing at high temperature. The increasing rate of strength by the accelerated curing was higher at the mortars containing less amount of cement than those containing more cement. The hardening of the mortars containing less amount of cement was significantly promoted by the accelerated curing in high temperature. 3. When the briquette ash was substituted for the materials of cement mortar, decline of the mortar strength is. unavoidable. But the enhancement of the mortar strength is still expected by the experimental results that the strength of cement-briquette ash mortar showed an increase of 137.6% by the accelerated curing at $60^{\circ}C$, 164.1% at $80^{\circ}C$ C and 183.8% at $100^{\circ}C$, respectively, compared with the strength of mortar cured at $20^{\circ}C$ for 28 days. 4. As the strength of cement briquette mortar is lower than that of cement standard sand mortar, the cement briquette ash mortar is expected to be increased in strength by the accelerated curing at high temperature. The cement briquette mortar is expected to be utilized to the production of secondary mortar goods or the constructions which need low strength of mortar.