• Proceedings of the Korean Magnestics Society Conference
• /
• 2005.12a
• /
• pp.168-169
• /
• 2005

• Journal of the Korean Magnetics Society
• /
• v.17 no.4
• /
• pp.156-161
• /
• 2007

To develop array magnetic sensors, specular-type giant magnetoresistive- spin valve (GMR-SV) film of Glass/Ta(5)MiFe(7)/IrMn(10)NiFe(5)/$O_2$/CoFe(5)/Cu(2.6)/CoFe(5)/$O_2$/NiFe(7)/Ta(5)(nm) was deposited by using a high-vacuum sputtering system. One of 15 way sensors in the area of $8{\times}8mm^2$ was Patterned a size of $20{\times}80{\mu}m^2$ in multilayer sample by Photo-lithography. All of 15 sensors with Cu electrodes were measured a uniform magnetic properties by 2-probe method. The highest magnetic sensitivity of MR and output voltage measured nearby an external magnetic field of 5 Oe were MS = 0.5%/Oe and ${\triangle}$V= 3.0 mV, respectively. An easy-axis of top-free layers of $CoFe/O_2/NiFe$ with shape anisotropy was perpendicular to one of bottom-pinned layers $IrMn/NiFe/O_2/CoFe$. When the sensing current increased from 1 mA to 10 mA, the output working voltage uniformly increased and the magnetic sensitivity was almost stable to use the nano-magnetic devices with good sensitive properties.

• Journal of the Korean Magnetics Society
• /
• v.16 no.3
• /
• pp.157-162
• /
• 2006

In this study, a high sensitive giant magnetoresistance-spin valve (GMR-SV) bio-sensing device with high linearity and very low hysteresis was fabricated by photolithography and ion beam deposition sputtering system. Detection of the Fe-hemoglobin inside in a red blood and magnetic nanoparticles using the GMR-SV bio-sensing device was investigated. Here a human's red blood includes hemoglobin, and the nanoparticles are the Co-ferrite magnetic particles coated with a shell of amorphous silica which the average size of the water-soluble bare cobalt nanoparticles was about 9 nm with total size of about 50 nm. When 1 mA sensing current was applied to the current electrode in the patterned active GMR-SV devices with areas of $5x10{\mu}m^2 $ and $2x6{\mu}m^2 $, the output signals of the GMRSV sensor were about 100 mV and 14 mV, respectively. In addition, the maximum sensitivity of the fabricated GMR-SV sensor was about $0.1{\sim}0.8%/Oe$. The magnitude of output voltage signals was obtained from four-probe magnetoresistive measured system, and the picture of real-time motion images was monitored by an optical microscope. Even one drop of human blood and nanopartices in distilled water were found to be enough for detecting and analyzing their signals clearly.

• Journal of the Korean Vacuum Society
• /
• v.5 no.3
• /
• pp.258-262
• /
• 1996

We have investigated the changes in magnetoresistive characteristics, interfacial roughness, and preferred orientation with the Fe buffer layer thickness, annealing temperature, and the stacking number of layers variation in Fe/[NiFe/Cu] multilayers by using the 3-gun d.c. magnetron sputtering method. Intensity of the (200) orientation was increased with the increment of the Fe-buffer layer thickness. We found a maximum magnetoresistance ration of 4.7%, when the buffer layer thickness was 70$\AA$, and the field sensitivity also showed a maximum value at the same thickness. We varied the stacking number of multilayers with fixing the Fe buffer layer thickness of 70$\AA$. When the stacking number was 40 layers, maximum MR ratio(5.3%) was observed. With the variation of annealing temperature no change in the MR ratio was found beyond $300^{\circ}C$. But decrement of MR ratio was observed above $300^{\circ}C$. This decrement of the MR ratio was responsible for the increment of paramagnetic mixed layer caused by the diffusion of Cu layer and the change of antiferromagnetic coupling.

• Journal of the Korean Magnetics Society
• /
• v.18 no.5
• /
• pp.174-179
• /
• 2008

The measurement dissolution sensor system using GMR-SV device with magnetic sensitivity of 0.8 %/Oe and Mg-film thick of 200 nm and Mg-foil thick of 50 mm was fabricated and characterized. During the water dissolving process of Mg-film and Mg-foil, the subtle variation of magnetic field by the decrease of current in solenoid was detected by the GMR-SV sensor. The variations of Mg bubble number and ORP as a function of time for three different kinds of edible, tap, and distilled water, are measured and compared. A After 45 min, the speed of fast dissolving Mg was shown the order of edible > tap > DI water. The variation of output magnetoresistance as a function of dissolved time of Mg-film and Mg-foil for edible water, which is composed of mineral content of $0.8{\sim}5.4\;mg/l$ was investigated. The response times for the dissolution in edible water were 5 min and 20 min, respectively. From the measurement of dissolving time and speed for Mg-film and Mg-foil using GMR-SV device, the mineral Mg sensor system in edible water can be possible to develop.