• Journal of the Microelectronics and Packaging Society
• /
• v.8 no.4
• /
• pp.25-33
• /
• 2001

Sn-3.5Ag-xBi alloys with five different levels of Bi (0, 2.5, 4.8, 7.5, 10 wt%) were prepared for evaluating creep properties. Cast alloys were roiled and heat treated to provide stable microstructures during the subsequent creep tests, which were conducted under constant load using dog-bone specimens. For the Bi containing alloys, creep strength showed the maximum around 2.5 wt%Bi and tended to decrease with increasing Bi content. The stress exponent of the alloy was around 4, suggesting typical dislocation creep, but the exponent was 2 for the 10 wt%Bi alloy, suggesting creep assisted by grain boundary Sliding. For the Bi containing alloys, the brittle fracture mode appeared showing small amount of reduction of area, while the ductile fracture mode was true for the Bi free alloy. Microstructural examination of ruptured specimens showed cavitations on grain boundaries normal to the load axis, and a significant of grain boundary sliding for the Bi containing alloys.

• Journal of the Korean Ceramic Society
• /
• v.28 no.8
• /
• pp.625-625
• /
• 1991

The specimens for the corrosion test were made by hot-pressing of SiC power with 2 wt% Nl2O3 and 10wt% Al2O3 additions at 2000℃ and 2050℃. The specimens were corroded in 37 mole% NaCl and 63 mole% Na2SO4 salt mixture at 1000℃ up to 60 min. SiO2 layer was formed on SiC and then this oxide layer was dissolved by Na2O ion in the salt mixture. The rate of corrosion of the specimen containing 10 wt% Al2O3 was slower than that of the specimen containing 2 wt% Al2O3. This is due to the presence of continuous grain boundary phase in the specimen containing 10 wt% Al2O3. The oxidation of SiC produced gas bubbles at the SiC-SiO2 interface. The rate of corrosion follows a linear rate law up to 50 min. and then was accelerated. This acceleration is due to the disruption oxide layer by the gas evolution at SiC-SiO2 interface. Pitting corrosion has found at open pores and grain boundaries.

• Journal of Welding and Joining
• /
• v.6 no.1
• /
• pp.35-45
• /
• 1988

오-스테나이트계 스테인레스강에 대한 용접은 용접재료의 개발과 더불어 각종 산업계에 널리 이용되고 있으며 최근 Type 303 오-스테나이트계 스테인레스강 등은 free machining재로써 널리 응용되고 있다. 그러나 이 303계는 피삭성, 절삭성, 칩형성개선을 위한 특수원소(Se, S 등)의 첨가 때문에 용접성에 문제점을 제기하고 있다. 본 연구에서는 Type 303을 중심으로 AISI 304-316NG 및 347NG계의 오-스테나이트계 스테인레스강의 고온연성거동과 고온균열감수성(용접성)에 관한 연구에 대한 검토중 고온연성거동에 관하여 조사하였다. 고온연성평가는 Gleeble Simulator에 의하여 재료와 방향성에 따라 검토하였으며, 그 결과 모든 재료는 압연방향을 종방으로 시험하였을 때는 거의 유사한 고온연성을 나타내었으나 횡방향으로 시험하였을 때는 종방향에 비하여 연성저하를 나타내었다. 이와 같은 고온연성은 후속연구에서 검토될 고온균열 감수성과 밀접한 관련성에 의하여 용접성을 평가할 수 있다.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1997.05b
• /
• pp.201-206
• /
• 1997

본 연구에서는 Ni-기 합금인 합금 600과 합금 690, Fe-기 합금인 합금 800 및 초내식성 오스테나이트계 스테인리스강인 SR-50A에 대하여 부식 환경의 변화에 따른 특성 평가를 행하였다. 전기화학적 부식 평가는 양극 분극 시험을 통하여 행하였으며 부식 환경은 NaCl, HCI, NaOH(+$Na_2$SO$_4$) 액이었다. 응력 부식 균열 시험으로는 CERT(Constant Extension Rate Test)를 행하였으며 부식환경은 40%NaOH, 40%OH+12%$Na_2$SO$_4$ 용액이었다. CERT시험 후 그 파면을 SEM관찰하여 파괴 양상을 관찰하였다. 각 합금의 양극 분극 특성을 부식 환경에 따라 평가한 결과, 부식 용액의 증류에 따라 서로 다른 분극 거동을 보이고 있는데 산성과 중성 용액에서는 SR-50A가 가장 큰 저항성을 보이는 반면, 강 알카리용액인 NaOH용액에서는 Ni-기 합금의 저항성이 Fe-기 합금의 저항성보다 우수하게 나타났다. 응력 부식 균열 저항성은 전반적으로 Fe-기 합금보다 Ni-기 합금이 우수하게 나타났다. 파단면을 SEM관찰한 결과 합금 800과 SR-50A(tube)는 용액에 관계없이 입내 파괴 모드를 나타내고 있으며, 합금 600과 SR-50A판재는 입계 파괴 양상을 보이고 있다. 또한 가성 용액 중에 $Na_2$SO$_4$를 첨가할 경우, 부식 속도를 가속화시키고 응력 부식 균열 저항성을 감소시키고 있다.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.22 no.3
• /
• pp.595-602
• /
• 1998

Specimens of 304 stainless steel were tested to failure at elevated temperatures under multiaxial stress states, uniaxial tension using smooth bar specimens, biaxial shearing using double shear bar specimens, and triaxial tension using notched bar specimens. Rupture times are compared for uniaxial, biaxial, and triaxial stress states with respect to the maximum principal stress, the von Mises effective stress, and the principal facet stress. The results indicate that the principal facet stress gives the best correlation for the material investigated, and this parameter can predict creep life data under multiaxial stress states with rupture data obtained with specimens under uniaxial stresses. The results also suggest that grain boundary cavitation, coupled with localized deformation processes such as grain boudary sliding, controls the lifetimes of the specimens.

• Proceedings of the KSME Conference
• /
• 2008.11a
• /
• pp.244-249
• /
• 2008

It happened a failure on special bolt which supported main landing gear actuator up-lock rod of 00 aircraft. Fracture was occurred at end of center drilled hole and thread machined on bolt. Metallographic, fractographic, and other characteristics of embrittlement analysis and experiments carried out on the failed bolt to find out the reason. Bolt surface was cadmium electroplated(EP) to give lubrication and provide excellent corrosion resistance. Resultly, Bolt was failed due to cadmium embrittlement occurred during baking treatment as well as center drilled hole. for the failure that are relevant to failure analysis and prevention. For their successful functional application, cadmium EP bolts require proper and adequate baking treatment after electroplating, and is complete with no center drilled hole

• Korean Journal of Materials Research
• /
• v.7 no.9
• /
• pp.717-722
• /
• 1997

노후화된 고온설비의 안정성 및 효율적인 운전조건을 확보하고, 고온부재의 취성파괴 방지를 위해서는 재질열화의 정량적 평가는 매우 중요하다. 그러나 현장실기에서 기계적 성질의 평가를 위한 대량의 시험편 채취는 거의 불가능하다. 따라서, 실기부재의 강도에 영향을 미치지 않는 범위에서 플랜트 구조물의 재질열화 평가를 비파괴적으로 검출 평가할 수 있는 새로운 시험방법들의 개발이 요구된다. 본 연구에서는 화력설비 부재의 다양한 탄소강을 대상으로 재질열화도 평가를 위한 전기화학적 양극분극시험법의 적용 가능성을 조사하였다. 또한 양극분극시험에 의한 재질열화평가 유효성을 조사하기 위해 전기화학적 시험결과를 입계부식시험결과와 비교.검토해 보았다.

• Journal of Korea Foundry Society
• /
• v.11 no.6
• /
• pp.491-497
• /
• 1991

Vanadium은 비중이 6.09로써 비교적 무거운 금속에 속하나 Al을 30wt% 이내로 첨가하여 $Ni_3Al$ 및 TiAl와 유사한 비강도가 크며 내열성을 지니는 V-Al합금을 얻을 가능성을 지니고 있다. 본 연구에서는 V-Al합금에 Si, Y, Ti, B등 제3원소를 첨가함에 따르는 미세 응고조직의 거동과 기계적 성질을 조사하였다. 알곤 분위기에서 제조된 V-30%Al합금은 상온에서 고용체와 취성이 큰 금속간 화합물인 $VAl_3$등 2상으로 존재하므로 용체화 처리 과정이 요구되며 24시간 이상 장시간 열처리에 의하여 단일 고용상을 이룰 수 있었다. 규소의 첨가는 금속간 화합물의 형성과 아울러 합금의 경도를 크게 증가시키는 경향을 나타내며 B을 0.3%정도가지 첨가할 때 경도가 낮아지는 현상이 관찰되었다. �c칭된 V-30%Al 합금은 입계면을 따라 decohesive rupture 현상을 나타내며 입자간 파괴 현상도 일부 관찰되었다.

• Korean Journal of Materials Research
• /
• v.6 no.6
• /
• pp.626-631
• /
• 1996

Reactive dc magnetron sputtering 법을 이용하여 증착한 molybdenum mitride 박막의 Cu 확산 방지막 특성을 조사하였다. Cu 확산 방지막으로서 molybdenum nitride 박막의 열적안정성을 관찰하기 위하여 molybdenum nitride 박막 위에 Cu를 evaporation 법으로 증착하고 진공 열처리하였다. Cu/r-Mo2N/si 구조는 $600^{\circ}C$, 30분간 열처리 시까지 안정하였다. 확산 방지막의 파괴는 $650^{\circ}C$, 30분간 열처리 시부터 격자 확산(lattice diffusion)이나 입계(grain boundary)과 결함(defect)을 통한 확산에 의해 나타나기 시작하였고, 이 때 molybdenum silicide과 copper silicide의 형성에 기인된 것으로 생각되었다. 열처리 이후 Cu/r-Mo2N/Si 사이의 상호반응이 증가하였다. 이는 Rutherford backscattering spectrometry, Auger electron spectroscopy 그리고 Nomarski microscopy 등의 분석을 통해 조사되었다.

• Journal of the Korea Institute of Military Science and Technology
• /
• v.13 no.5
• /
• pp.769-774
• /
• 2010

It happened fractures on special bolt which supported main landing gear actuator up-lock rod of aircraft. Cracks were initiated mainly from the center hole and the external thread of the special bolt. To find out failure root causes, metallographic, fractographic analyses as well as test work were carried out. From the fractographic study by SEM work, fracture occurred by a brittle intergranular type failure. The fracture could be occurred primarily by solid-metal-induced embrittlement due to cadmium embrittler penetrated into the flaw existed after machining work for center hole and thread on the bolt during baking treatment processing to eliminate hydrogen. For its successful application, cadmium EP bolts require proper and adequate baking treatment after electroplating, and make no more drilled center hole on the bolt to prevent same failure.